Chemical Admixtures for Hydraulic Cements

ABSTRACT

This invention relates to a new class of chemical admixtures for hydraulic cement compositions such as pastes, mortars, grouts and concretes. The cement compositions are comprised of ordinary Portland cement, blended cements, or non-Portland cements made with Supplementary Cementitious Materials. The admixtures contain complexes of metals with derivatives of hydroxycarboxylic acids, and improve properties of cement compositions, including setting, hardness, compressive strength, shrinkage, and freeze-thaw resistance. The invention discloses a method for improving the properties of hydraulic cements by adding the disclosed chemical admixtures to cement compositions, and also discloses methods of preparing said admixtures.

This application claims the benefit of priority to U.S. Provisional Patent Application No. 61/538,396, filed Sep. 23, 2011.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention generally relates to a new class of chemical admixtures for hydraulic cement compositions such as pastes, mortars, grouts and concretes. The cement compositions are comprised of Ordinary Portland Cement, or blended cements or non-Portland cements made with Supplementary Cementitious Materials (SCMs). The admixtures improve the properties of cement compositions, including setting, hardness, compressive strength, shrinkage, and freeze-thaw resistance.

2. Description of the Related Art

Ordinary Portland Cement (OPC, also known as Portland Cement) underpins modern construction technology and constitutes the second most manufactured product in the world. According to Struble, et al., Introduction to Portland Cement, in Portland Cement: Composition, Production and Properties, pp. 1-47 (2011 ICE Publishing, 3rd ed.); Herfort, et al., The Chemistry of Portland Cement Clinker, 2010 Adv. Cem. Res. 22: 187-194; and Jackson, Portland Cement Classification and Manufacture, in Lea's Chemistry of Cement and Concrete, pp. 25-94 (2003 Elsevier, 4th ed.), U.S. and world production of OPC currently stands at 72 million metric tons (t) and 2.8 billion t respectively.

Alas, OPC manufacturing has a large ecological footprint as it requires large amounts of mineral, fuel and water resources, and is accompanied by the release of various pollutants. See Huntzinger, et al., A life-cycle assessment of Portland cement manufacturing, 2009 J. Cleaner Prod. 17: 668-675; Flower et al., Green house gas emissions due to concrete manufacture, 2007

Int. J. LCA 12: 282-288; Marceau, et al., Life Cycle Inventory of Portland Cement Manufacture, pp. 1-68 (2006 Portland Cement Association); Rehan et al., Carbon dioxide emissions and climate change: policy implications for the cement industry, 2005 Environ. Sci. Policy 8: 105-114; Worrell, Cement and Energy, in Encyclopedia of Energy, pp. 307-316 (2004 Elsevier, Volume 1); van Oss, and Padovani, Cement manufacture and the environment, Part 2: Environmental challenges and opportunities, 2003 J. Ind. Ecol. 7: 93-126; van Oss and Padovani, Cement manufacture and the environment, Part 1: Chemistry and technology. 2002 J. Ind. Ecol. 6: 89-105; and Worrell. et al., Carbon dioxide emissions from the global cement industry, 2001 Ann. Rev. Energy Env. 26: 303-3029.

Indeed, every 1.0 t of OPC uses 1.50-1.75 t of minerals, 0.89-1.21 t of fuel, and 0.52-1.03 t of water for its production, and results in the emission of 0.70-0.92 t of carbon dioxide as well as various other toxic substances, including carbon monoxide, nitrogen oxides, sulfur oxides, hydrogen chloride, dioxins, lead, mercury and selenium. Since 72 million t of OPC are produced in the U.S. every year, this equates to the use of 108-126 million t of minerals, 64-87 million t of fuel, and 37-74 million t of water, and the emission of 50-66 million t of carbon dioxide.

In view of the poor environmental metrics of OPC, efforts have been made to produce “Green” and sustainable cements by partially or completely replacing OPC with alternative binders with lower ecological footprints, as described in the publications, Schneider, et al., Sustainable cement production—present and future, 2011 Cement Concrete Res. 41: 642-650; Sharp, et al., Novel cement systems, 2010 Adv. Cem. Res. 22: 195-202; Damtoft, et al., Sustainable development and climate change initiatives, 2008 Cement Concrete Res. 38: 115-127; Phair, Green chemistry for sustainable cement production and use, 2006 Green Chem. 8: 763-780; and Placet, et al., Toward a Sustainable Cement Industry, pp 1-92 (2002 Battelle, Substudy 7).

With suitable formulation and additives, OPC can be partially or completely replaced by a variety of minerals and industrial byproducts, collectively referred to as Supplementary Cementitious Materials (SCMs, also known as Mineral Admixtures), the resultant products being referred to as blended cements and non-Portland cements respectively. Blended cements are described in the publications, Massazza, Pozzolana and pozzolanic cements, in Lea's Chemistry of Cement and Concrete, pp. 471-631 (2003 Elsevier, 4th ed.); and Mineral Admixtures in Cement and Concrete, pp. 1-248 (2011 CRC Press); and Kosmatks, et al., Portland, Blended, and Other Hydraulic Cements, in Design and Control of Concrete Mixtures, pp. 21-56 (2006 Portland Cement Association, 14th ed.).

SCMs are characterized as cementitious, pozzolanic (having cementitious activity in the presence of lime), or both cementitious and pozzolanic. ASTM C-989, C-618 and C-1240 describe three major classes of SCMS: (i) Iron blast furnace slags (cementitious); (ii) Fly ash Class C (cementitious and pozzolanic), fly ash Class F (pozzolanic), and natural (raw or calcined) pozzolans such as diatomaceous earths, opaline cherts and shales, tuffs, volcanic ashes, and calcined clays and shales; and (iii) Silica fume (pozzolanic). The major SCMs are low-value industrial byproducts, most notably fly ash and blast furnace slag, which are waste products of coal-fired power plants and iron ore smelters respectively. SCMs are described in Mineral Admixtures in Cement and Concrete, pp. 1-248 (2011 CRC Press); Supplementary Cementing Materials, pp. 1-283 (2011 Springer); Lohtia, et al., Mineral Admixtures, in Concrete Admixtures Handbook, pp. 657-739 (2006 Noyes, 2nd ed.); Waste Materials and Byproducts in Concrete, pp. 1-407 (2008 Springer), Kosmatks, et al., Fly Ash, Slag, Silica Fume, and Natural Pozzolans, in Design and Control of Concrete Mixtures, pp. 57-72 (2006 Portland Cement Association, 14th ed.); Massazza, Pozzolana and pozzolanic cements, in Lea's Chemistry of Cement and Concrete, pp. 471-631 (2003 Elsevier, 4th ed.); and Waste Materials Used in Concrete Manufacturing, pp. 1-637 (1997 Noyes).

Since SCMs are industrial byproducts or lightly processed minerals, they have lower ecological footprints than OPC, as described by Schneider, et al., Sustainable cement production—present and future, 2011 Cement Concrete Res. 41: 642-650; Sharp, et al., Novel cement systems, 2010 Adv. Cem. res. 22: 195-202; Damtoft, et al., Sustainable development and climate change initiatives, 2008 Cement Concrete Res. 38: 115-127; Phair, Green chemistry for sustainable cement production and use, 2006 Green Chem. 8: 763-780; and Placet, et al., Toward a Sustainable Cement Industry, pp 1-92 (2002 Battelle, Substudy 7). For example, the CO₂ footprints of fly ash, blast furnace slag, steel slag, limestone fines and calcined natural pozzolans are 0.02-0.04, 0.13-0.16, 0.10-0.14, 0.16-0.19 and 0.18-0.22 t-CO₂ per t-SCM respectively, compared to OPC's CO₂ footprint of 0.70-0.92 t-CO₂ per t-cement. Substituting SCMs for OPC proportionally improves environmental metrics, with blended cements and non-Portland cements showing CO₂ footprints of only 0.28-0.67 and 0.26-0.50 t-CO₂ per t-cement respectively.

Blended cements, especially those employing fly ash and/or blast furnace slag as SCMs, are used worldwide in place of OPC for certain applications. In the U.S., blended cements are specified under ASTM C-595-06 as Portland-Pozzolan cement, Type IP(X), which allows 0-40% w/w replacement of OPC with a pozzolan (typically fly ash), and as Portland-blast furnace slag cement, Type IS(X), which allows 0-95% w/w replacement of OPC with blast furnace slag.

Blast furnace slag is a cementitious material that can replace up to 95% w/w of OPC in blended cements, and is typically used at 50% replacement level. But, its availability is limited, with U.S. and world production standing at 9 million and 250 million t respectively, or only 13 and 9% of OPC consumption respectively. Fly ash is available in much larger quantities, with U.S. and world production standing at 70 million and 700 million t, or on par with U.S. OPC consumption and some 25% of world OPC usage respectively. Its use in blended cements at low to moderate levels (0-50% replacement of OPC) can improve durability metrics such as ultimate compressive strength, permeability, salt resistance, rebar corrosion resistance and freeze-thaw resistance. Fly ash is available at a low cost—in the range of $5-60 per t in the U.S., and in quantities large enough to satisfy the total demand for cement in the U.S. and some 25% of world cement demand.

Despite its availability and use potential, fly ash is highly underutilized with less than 15% of U.S. ash output going into blended cements, and with some 65% of ash sent for storage or disposal. This has resulted in the accumulation of over 500 million t of ash, a situation that seems certain to worsen as U.S. ash output is projected to increase to 100 million t by 2030. Unused ash carries significant public health and environmental burdens due to the presence of potentially toxic elements, and approaches for its safe and beneficial utilization in added value products such as cement are essential for the sustainable management of ash. Fly ash is reviewed in the publications, Ahmaruzzaman, A review on the utilization of fly ash, 2010 Prog. Energy Combust. Sci. 36: 327-363); Kelly, et al., Coal Combustion Products Statistics, pp. 1-2 (2010 U.S. Geological Survey); Coal Combustion Product Production & Use Survey Results, pp. 1-2 (2009 American Coal Ash Association); Beneficial Use of Secondary Materials—Coal Combustion Products, pp. 1-95 (2008 U.S. Environmental Protection Agency); Nugteren, Fly ash: From waste to industrial product, 2007 Part. Part. Sys. Charact. 24: 49-55; Hall, et al., Fly ash quality, past, present and future, and the effect of ash on the development of novel products, 2002 J. Chem. Technol. Biotechnol. 77: 234-239; and Rayzman, et al., Technology for chemical-metallurgical coal ash utilization, 1997 Energy Fuels 11: 761-773.

While fly ash is an attractive SCM, performance considerations limit the fly ash content in blended cements to less than 50% replacement of OPC, with U.S. states allowing a maximum substitution level in the range of just 15-25%. Despite the use of performance-enhancing chemical additives, the replacement of more than 25% of OPC with fly ash retards setting and the rate of hardness and compressive strength development, increases the demand for air-entraining agents, can adversely affect durability metrics such as salt resistance, and may require the use of increased cement content in cement compositions. For example, blended cements with 25% and 50% w/w replacement of OPC with fly ash typically show only 50-75% and 30-50% of the hardness and compressive strength development of OPC-based compositions, and can require 1-3 months to reach performance parity, as described in the publications, Mineral Admixtures in Cement and Concrete, pp. 1-248 (2011 CRC Press); Supplementary Cementing Materials, pp. 1-283 (2011 Springer); Lohtia, et al., Mineral Admixtures, in Concrete Admixtures Handbook, pp. 657-739 (2006 Noyes, 2nd ed.); Waste Materials and Byproducts in Concrete, pp. 1-407 (2008 Springer), Kosmatks, et al., Fly Ash, Slag, Silica Fume, and Natural Pozzolans, in Design and Control of Concrete Mixtures, pp. 57-72 (2006 Portland Cement Association, 14th ed.); Massazza, Pozzolana and pozzolanic cements, in Lea's Chemistry of Cement and Concrete, pp. 471-631 (2003 Elsevier, 4th ed.); and Waste Materials Used in Concrete Manufacturing, pp. 1-637 (1997 Noyes).

Attempts to develop blended cements containing other SCMs such as limestone, steel slag and non-ferrous slags, have been hampered by similar albeit worse problems to OPC-fly ash cements. Thus, ASTM C-150 allows the addition of only 5% of limestone to OPC, due to concerns about setting retardation, poor strength development and excessive shrinkage at higher limestone contents. Blended cements made with steel slag and non-ferrous slags face a variety of problems including poor setting, slow hardness and strength development, delayed expansion, cracking, and poor freeze-thaw resistance.

Performance issues and the lack of industry-standard specifications for high-SCM content blended cements necessitate extensive pretesting to ensure durable cement compositions that meet building codes, and invariably lead to higher costs. As such, the availability and use of blended cements in the U.S. has been highly restricted, with the average replacement level of SCMs for OPC being less than 15%, and less than 3% of cement in the U.S. being blended cement. See e.g. Loreti, Greenhouse Gas Emission Reductions from Blended Cement Production, pp. 1-35 (2008 The Loreti Group); and Characteristics of Portland and Blended Cements: Results of a Survey of Manufacturers, pp. 83-101 (2006 IEEE Conference Proceedings).

Non-Portland cements, such as those based upon fly ash and/or blast furnace slag suffer from similar albeit worse problems to blended cements. For example, cements made from fly ash, or blends of fly ash with other SCMs, can display flash or delayed setting, poor hardness and compressive strength development, excessive shrinkage, aggregate-induced expansion, and poor long-term durability. Indeed, there is no industry-standard specification for non-Portland cements in the U.S., and no significant commercial production of such cements.

Various approaches have been used to elevate the performance of blended cements and non-Portland cements to that of OPC, the most successful being the use of chemical admixtures to improve such properties as setting, and the rate of hardness and compressive strength development. As generally described in the publications, Chemical Admixtures for Concrete, pp. 1-1 to 6-10 (1999 Taylor and Francis, 3rd ed.) and Concrete Admixtures Handbook, pp. 137-1024 (1996 Noyes, 2nd ed.), chemical admixtures are inorganic or organic compounds that are used to modify the physicochemical properties of cement compositions. These properties include viscosity, slump, water requirement, setting, hardness, compressive strength, shrinkage, porosity, air content, water resistance, freeze-thaw resistance, salt resistance and rebar corrosion resistance. Chemical admixtures such as sodium hydroxide, sodium silicate, sodium aluminate, sodium citrate, calcium chloride, calcium sulfate, calcium nitrate, calcium nitrite, calcium formate, citric acid, carboxylic acid-containing polymers and copolymers, and alkanolamines have long been used to regulate setting and hardness and compressive strength development in OPC, and have found similar albeit less utility in blended cements and non-Portland cements.

The prior art describes the application of calcium salts, citric acid, and citrate salts as accelerators for high-SCM content blended cements and SCM-based non-OPC cements. However, these approaches are often not placement/use equivalent to OPC, and give variable results in terms of setting, hardness and strength development, shrinkage, cracking, aggregate reactivity and/or long-term durability. Because of these issues, none of these approaches have found significant commercial applications, other than very specialized uses such as rapid-setting cements. The use of citric acid and citrate salts as accelerator(s) for blended cements and fly ash-based non-Portland cements is described U.S. Pat. No. 4,842,649, U.S. 4997484, U.S. Pat. No. 5,374,308, U.S. Pat. No. 5,536,310, U.S. Pat. No. 4,640,715, U.S. Pat. No. 4,642,137, U.S. Pat. No. 7,854,803, U.S. Pat. No. 7,288,148, U.S. Patent Application 2008178770 A1 and U.S. Pat. No. 6,827,776. The use of calcium sulfate as accelerator for fly ash-based non-Portland cements is described in the publications, U.S. Pat. No. 5,439,518, U.S. Pat. No. 5,578,122, U.S. Pat. No. 4,240,952, U.S. Pat. No. 4,470,850 and U.S. Pat. No. 4,256,504. The use of calcium nitrate as an accelerator for blended cements is described in the publication, U.S. Patent Application 20110048285 A1.

The prior art also describes the use of highly alkaline chemical admixtures (also known as alkali activators) such as sodium hydroxide, potassium hydroxide, sodium silicate and sodium aluminate for forming so-called “geopolymers” with blended cements and SCM-based non-Portland cements. While the properties of geopolymer cements can match or exceed those of OPC or conventional blended cements, they have severe drawbacks—most notably that the admixtures are highly corrosive and required in large amounts (typically 5-25% of the cement content), that the cements are not use/placement equivalent to OPC and require special formulation, handling and curing, and that they lack long-term stability and durability. Indeed, there is currently no geopolymeric cement of commercial significance in the U.S. Alkali activators and geopolymer cements are described in the publications, Alkali Activated Cements and Concretes, pp. 1-334 (2006 Taylor and Francis); Duxson, et al., The role of inorganic polymer technology in the development of ‘green concrete’, 2007 Cement Concrete Res. 37: 1590-1597; Pachecho-Torgal, et al., Alkali-activated binders: A review Part 1. Historical background, terminology, reaction mechanisms and hydration products, 2008 Constr. Build. Mater. 22: 1305-1314; Pachecho-Torgal, et al., Alkali-activated binders: A review. Part 2. About materials and binders manufacture, 2008 Constr. Build. Mater. 22: 1315-1322; and Duxson, et al., Geopolymer technology: the current state of the art, 2007 J. Mater. Sci. 42: 2917-2933.

While currently available chemical admixtures are useful for improving the properties of blended cements containing low to moderate levels of SCMs (up to 25% of fly ash, up to 50% of blast furnace slag, and up to 15% of limestone), their performance is not as satisfactory with higher levels of SCMs, and even less so with SCM-based non-Portland cements. To date there is no commercial general-use high-SCM content blended cement or non-Portland cement available in the U.S., despite the demand for such Green and sustainable cements as alternatives to OPC.

SUMMARY OF THE INVENTION

Thus, there is a need in the art for chemical admixtures that can improve the properties of blended cements containing high levels of SCMs and SCM-based non-Portland cements, and that can make them use/performance equivalent to OPC. In particular, there is a need for admixtures capable of improving setting, the rate of hardness and compressive strength development, shrinkage, permeability, and long-term durability indicators such as salt resistance and freeze-thaw resistance. Such admixtures would improve economics by enabling the partial or complete substitution of OPC, which costs $80-100 per t, with SCMs, which cost just $5-60 per t. Also, environmental and public health metrics would be greatly improved by reducing the natural resource use and pollution footprint deriving from OPC, and by increasing the beneficial use of SCMs and diverting them from storage and disposal.

It is an object of an embodiment this invention to provide a new class of chemical admixtures that improves the properties of cement compositions, particularly with regard to blended cements and non-Portland cements made with SCMs.

Accordingly, an embodiment of the present invention is directed to a new class of chemical admixtures for hydraulic cement compositions such as pastes, mortars, grouts and concretes. The cement compositions are comprised of Portland cement, or blended cements or non-portland cements made with Supplementary Cementitious Materials (SCMs). The admixtures improve the properties of cement compositions, including setting, hardness, compressive strength, shrinkage and freeze-thaw resistance, thereby substantially obviating one or more of the problems due to limitations and disadvantages of the related art.

An object of the present invention is to provide an economical admixture that can be used to prepare hydraulic cement compositions that are cheaper, more environmentally friendly, and have a lower carbon footprint than traditional cement composition. Another object of the present invention is to enable Portland cement to be partially or completely replaced by SCMs in hydraulic cement compositions, while maintaining substantial use and performance equivalence.

In another aspect, an embodiment of the present invention provides the processes and methods for preparing the admixtures, and further provides methods in which they can be used in the manufacture of hydraulic cement compositions such as pastes, mortars, grouts and concretes. Additional features and advantages of the invention will be set forth in the descriptions that follow and in part will be apparent from the description, or may be learned by practice of the invention. The objectives and other advantages of the invention will be realized and attained by the structures and compositions particularly pointed out in the written description and claims thereof.

To achieve these and other advantages and in accordance with the purpose of the present invention, as embodied and broadly described, an embodiment of the present invention provides admixtures for hydraulic cement compositions, which contain complexes of metals and/or semi-metals with hydroxycarboxylic acid-derived ligands, and may be described by the following general empirical chemical formula:

A¹ _(a) . . . A^(n) _(x)B¹ _(a′) . . . B^(n) _(x′)[M¹ _(a″) . . . M^(n) _(x″)C¹ _(a′″) . . . C^(n) _(x′″)L¹ _(a″″) . . . L^(n) _(x″″)]

where, A¹ . . . A^(n) are cations, B¹ _(a′) . . . B^(n) _(x′) are anions, M¹ . . . M^(n) are chelated metal and/or semi-metal cations, C¹ . . . C^(n) are coordinating ligands, and L¹ . . . L^(n) are chelating hydroxycarboxylic acid-derived ligands. The subscripts a and x, a′ and x′, a″ and x″, a′″ and x′″, and a″″ and x″″ refer to the cation, anion, chelated metal, coordinating ligand, and chelating hydroxcarboxylic acid-derived ligand stoichiometries respectively. The admixtures described by the above general formula contain at least one chelated metal or semi-metal cation (M^(n) _(x″)), and at least one chelating hydroxycarboxylic acid-derived ligand (L^(n) _(x″)). Furthermore, the admixtures may contain one or more cations (A^(n) _(x)), and/or one or more anions (B^(n) _(x′)) and/or one or more coordinating ligands (C^(n) _(x′″)).

It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory, and are intended to provide further explanation of the invention as claimed.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENTS

Described are admixtures for hydraulic cement compositions. The term “cement composition” as used herein refers to pastes, mortars and concretes. The cement compositions are comprised of Portland cement, or blended or non-Portland cements made with Supplementary Cementitious Materials (SCMs).

The admixtures contain complexes of metals and/or semi-metals with hydroxycarboxylic acid-derived ligands, and may be described by the following general empirical chemical formula:

A¹ _(a) . . . A^(n) _(x)B¹ _(a′) . . . B^(n) _(x′)[M¹ _(a″) . . . M^(n) _(x″)C¹ _(a′″) . . . C^(n) _(x′″)L¹ _(a″″) . . . L^(n) _(x″″)]  Formula 1.

In the above general formula, A¹ . . . A^(n) are cations, B¹ _(a′) . . . B^(n) _(x′) are anions, M¹ . . . M^(n) are chelated metal and/or semi-metal cations, C¹ . . . C^(n) are coordinating ligands, and L¹ . . . L^(n) are chelating hydroxycarboxylic acid-derived ligands. The subscripts a and x, a′ and x′, a″ and x″, a′″ and x′″, and a″″ and x″″ refer to the cation, anion, chelated metal, coordinating ligand, and chelating hydroxcarboxylic acid-derived ligand stoichiometries respectively. The admixtures, described by the above general formula, contain at least one chelated metal or semi-metal cation (M^(n) _(x″)), and at least one chelating hydroxycarboxylic acid-derived ligand (L^(n) _(x″″)). Furthermore, the admixtures may contain one or more cations (A^(n) _(x)), and/or one or more anions (B^(n) _(x′)) and/or one or more coordinating ligands (C^(n) _(x′″)).

The cations (A¹ _(a) . . . A^(n) _(x)) in Formula 1 are in particular selected from, but not limited to the examples detailed below and depicted in Table 1:

-   -   (i) The ammonium ion (NH₄ ⁺), and alkyl-, cycloalkyl-, aryl-,         arylalkyl and/or heteroaryl-substituted ammonium ions (1-4), as         exemplified by but not limited to the tetramethylammonium,         ethyltrimethylammonium, butyltrimethylammonium,         cyclohexylammonium, dicyclohexylammonium, and         benzyltrimethylammoniun ions.     -   (ii) Cations of alkyl-, cycloalkyl-, aryl-, and/or arylalkyl-         and/or heteroaryl-substituted aminoalcohols, as exemplified but         not limited to the 2-hydroxyethylammonium,         bis(2-hydroxyethyl)ammonium, and tris(2-hydroxyethyl)ammonium         ions (5-7).     -   (iii) The proton (H⁺), and metal cations, as exemplified by but         not limited to ions of the lithium family (Group IA, 8), and         beryllium family (Group IIA, 9).

TABLE 1 Examples of Cations (A^(n) _(x))

1

2

3

4 R^(1,3,5,7) = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,4,6,8) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

5

6

7 R^(1,3,5) = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,4,6) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃). H⁺ Li⁺ Na⁺ K⁺ Rb⁺ Cs⁺ 8 Be²⁺ Mg²⁺ Ca²⁺ Sr²⁺ Ba²⁺ 9

The anions (B¹ _(a) . . . B^(n) _(x)) in Formula 1 are in particular selected from, but not limited to the examples detailed below and depicted in Table 2:

-   -   (i) Metal, non-metal and semi-metal anions, as exemplified by         but not limited to ions of the boron family (Group IIIA, 10),         carbon family (Group IVA, 11), nitrogen family (Group VA, 12),         oxygen family (Group VIA, 13) and fluorine family (Group VIIA,         14), and derivatives thereof (15).     -   (ii) The anions of aliphatic, cycloaliphatic, aromatic         arylaliphatic and heteroaromatic sulfonic acids (16), as         exemplified by, but not limited to methanesulfonic acid,         ethanesulfonic acid, propane-1-sulfonic acid, butane-1-sulfonic         acid, cyclohexanesulfonic acid, benzenesulfonic acid,         4-methylbenzenesulfonic acid (tosic acid), and         pyridine-3-sulfonic acid.     -   (iii) The anions of aliphatic, cycloaliphatic, aromatic         arylaliphatic and heteroaromatic sulfate monoesters (17), as         exemplified by, but not limited to prop-1-yl sulfate, but-1-yl         sulfate, hex-1-yl sulfate, dec-1-yl sulfate, dodec-1-yl sulfate         (lauryl sulfate), tetradec-1-yl sulfate (myristyl sulfate),         hexadec-1-yl sulfate (palmityl sulfate), octadec-1-yl sulfate         (stearyl sulfate), and phenylmethyl sulfate (benzyl sulfate).     -   (iv) The anions of aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         monocarboxylic acids (18), as exemplified by, but not limited to         ethanoic acid (acetic acid), propanoic acid (propionic acid),         butanoic acid (butyric acid), pentanoic acid (valeric acid),         hexanoic acid (caproic acid), heptanoic acid (ananthic acid),         heptanoic acid (caprylic acid), octanoic acid (pelargonic acid),         decanoic acid (capric acid), dodecanoic acid (lauric acid),         tetradecanoic acid (myristic acid), hexadecanoic acid (palmitic         acid), octadecanoic acid (stearic acid), 2-methylpropanoic acid         (isobutyric acid), 2-ethylhaxanoic acid (octoic acid),         2-methyloctadecanoic acid (2-methylstearic acid), ethoxyethanoic         acid (ethoxyacetic acid), (2′-ethoxyethoxy)ethanoic acid,         cyclopentane carboxylic acid, cyclohexane carboxylic acid,         benzoic acid, 4-methylbenzenecarboxylic acid (p-toluic acid),         napthalenel-carboxylic acid (1-napthoic acid), phenylacetic         acid, 3-phenylpronanoic acid, and pyridine-2-carboxylic acid         (2-picolinic acid).

TABLE 2 Examples of Anions (Bnx) BO₂ ⁻ BO₃ ³⁻ B₂O₅ ⁴⁻ B₃O₇ ⁵⁻ 10 B₄O₇ ²⁻ B₄O₉ ⁶⁻ CO₃ ²⁻ HCO₃ ⁻ SiO₃ ²⁻ 11 SiO₂(OH)₂ ²⁻ SiO₄ ⁴⁻ NO₂ ⁻ NO₃ ⁻ HPO₃ ²⁻ PO₃ ³⁻ 12 HPO₄ ²⁻ PO₄ ³⁻ P₆O₁₈ ⁶⁻ OH⁻ S²⁻ SO₃ ²⁻ SO₄ ²⁻ 13 S₂O₃ ²⁻ S₄O₆ ²⁻ F⁻ Cl⁻ Br⁻ I⁻ ClO₃ ⁻ 14 TiF₆ ²⁻ BF₄ ⁻ AlF₆ ³⁻ SiF₆ ²⁻ 15 PFO₃ ²⁻ PF₂O₂ ⁻ PF₆ ⁻ SFO₃ ⁻

16

17

18 R¹ = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,3) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

The chelated metal/semi-metal cations (M¹ _(a″) . . . M^(n) _(x″)) in Formula 1 are in particular selected from, but not limited to the examples detailed below and depicted in Table 3:

-   -   (i) Metal and/or semi-metal cations, as exemplified by but not         limited to ions of the beryllium family (Group IIA, 19),         scandium family (Group IIIB, 20), titanium family (Group IVB,         21), vanadium family (Group VB, 22), chromium family (Group VIB,         23), manganese, iron, cobalt, nickel, copper and zinc families         (Groups IB, IIB, VIIB and VIIIB, 24), boron family (Group IIIA,         25), carbon family (Group IVA, 26), and nitrogen family (Group         VA, 27).     -   (ii) Oxocations, as exemplified by but not limited to oxocations         and peroxocations of the titanium family (Group IVB, 28),         vanadium family (Group VB, 29), chromium family (Group VIB, 30),         and nitrogen family (Group VA, 31).

TABLE 3 Examples of Metal Cations (M^(n) _(x″)) Chelating Hydroxycarboxylic Acid-Derived Ligands Be²⁺Mg²⁺Ca²⁺Sr²⁺Ba²⁺ Sc³⁺Y³⁺La³⁺Ce³⁺Ce⁴⁺Eu³⁺ Ti⁴⁺Zr⁴⁺Hf⁴⁺ 19 20 21 V³⁺V⁴⁺V⁵⁺Nb³⁺Nb⁴⁺Nb⁵⁺ Cr³⁺Mo⁴⁺Mo⁶⁺W⁶⁺ Mn²⁺Fe²⁺Fe³⁺Co²⁺Ni²⁺Cu²⁺ Ta³⁺Ta⁴⁺Ta⁵⁺ Zn²⁺ 22 23 24 B³⁺Al³⁺Ga³⁺In³⁺ Ge⁴⁺Sn²⁺Sn⁴⁺ Sb³⁺Sb⁵⁺Bi³⁺ TiO²⁺ [Ti₂(O₂)₂]⁴⁺ [Ti₄(O₂)₄]⁸⁺ ZrO²⁺ HfO²⁺ 25 26 27 28 VO³⁺VO₂ ⁺NbO³⁺TaO³⁺ MoO⁴⁺MoO³⁺MoO₂ ⁺ SbO⁺BiO⁺ TaO₂ ⁺ WO⁴⁺WO₂ ²⁺WO³⁺WO₂ ⁺ 29 30 31

The coordinating ligands (C¹ _(a′″) . . . C^(n) _(x′″)) in Formula 1 are in particular selected from, but not limited to the examples detailed below and depicted in Table 4:

-   -   (i) Water (H₂O).     -   (ii) The anions of aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         monocarboxylic acids (32), as exemplified by, but not limited to         ethanoic acid (acetic acid), propanoic acid (propionic acid),         butanoic acid (butyric acid), pentanoic acid (valeric acid),         hexanoic acid (caproic acid), heptanoic acid (ananthic acid),         heptanoic acid (caprylic acid), octanoic acid (pelargonic acid),         decanoic acid (capric acid), dodecanoic acid (lauric acid),         tetradecanoic acid (myristic acid), hexadecanoic acid (palmitic         acid), octadecanoic acid (stearic acid), 2-methylpropanoic acid         (isobutyric acid), 2-ethylhaxanoic acid (octoic acid),         2-methyloctadecanoic acid (2-methylstearic acid), ethoxyethanoic         acid (ethoxyacetic acid), (2′-ethoxyethoxy)ethanoic acid,         cyclopentane carboxylic acid, cyclohexane carboxylic acid,         furan-2-carboxylic acid (2-furoic acid), benzoic acid,         4-methylbenzenecarboxylic acid (p-toluic acid), napthalene         1-carboxylic acid (1-napthoic acid), phenylacetic acid,         3-phenylpronanoic acid, and pyridine-2-carboxylic acid         (2-picolinic acid).     -   (iii) The anions of aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         dicarboxylic acids (33), as exemplified by but not limited to         ethanedioic acid (oxalic acid), propane-1,3-dioic acid (malonic         acid), butane-1,4-dioic acid (succinic acid), pentane-1,5-dioic         acid (glutaric acid), hexane-1,6-dioic acid (adipic acid),         heptane-1,7-dioic acid (pimelic acid), octane-1,8-dioic acid         (suberic acid), nonane-1,9-dioic acid (azealic acid),         decane-1,10-dioic acid (sebacic acid), dodecane-1,12-dioic acid,         tetradecane-1,14-dioic acid, hexadecane-1,16-dioic acid,         octadecane-1,18-dioic acid, cyclohexane-1,2-dicarboxylic acid,         furan-2,5-dicarboxylic acid, benzene-1,2-dicarboxylic acid         (phthalic acid), benzene-1,3-dicarboxylic acid (isophthalic         acid), and benzene-1,4-dicarboxylic acid (terephthalic acid).     -   (iv) The anions of aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         tricarboxylic acids (34), as exemplified by but not limited to         3-carboxypentane-1,5-dioic acid (carballylic acid),         benzene-1,2,4-tricarboxylic acid (trimellitic acid), and         benzene-1,3,5-tricarboxylic acid (trimesic acid).     -   (v) The anions of alkyl, heteroalkyl, cycloalkyl,         cycloheteroalkyl, aryl, arylalkyl and heteroaryl-substituted         unsaturated aliphatic monocarboxylic acids (35), as exemplified         by but not limited to (E)-but-2-enoic acid (crotonic acid),         (E)-2-methylbut-2-enoic acid (tiglic acid), and         (E)-3-phenylprop-2-enoic acid (cinnamic acid).     -   (vi) The anions of alkyl, heteroalkyl, cycloalkyl,         cycloheteroalkyl, aryl, arylalkyl and heteroaryl-substituted         unsaturated aliphatic dicarboxylic acids (36), as exemplified by         but not limited to (Z)-but-2-ene-1,4-dioic acid (maleic acid),         and (E)-but-2-ene-1,4-dioic acid (fumaric acid).     -   (vii) The anions of aliphatic, aromatic or mixed         aliphatic-aromatic polycarboxylic acids, polycarboxylic acid         copolymers and their derivatives, as exemplified by but not         limited to poly(acrylic acid), poly(methacrylic acid),         poly(itaconic acid), poly(maleic acid), poly(acrylic         acid-co-maleic acid), poly(ethylene-co-acrylic acid),         poly(ethylene-co-methacrylic acid), poly(ethylene-co-maleic         acid), poly(styrene-co-maleic acid), poly(methyl vinyl         ether-alt-maleic acid), poly(acrylic acid)-poly(ethylene glycol)         methyl ether esters, and poly(methacrylic acid)-poly(propylene         glycol) methyl ether esters.     -   (viii) Aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         diols (37), triols, and polyols, as exemplified by but not         limited to ethane-1,2-diol (ethylene glycol), propane-1,2-diol,         propane-1,3-diol, butane-1,2-diol, butane-1,3-diol,         butane-2,3-diol, butane-1,4-diol, benzene-1,2-diol (catechol),         benzene-1,3-diol (resorcinol), 4-methylbenzene-1,2-diol         (4-methylcatechol), propane-1,2,3-triol (glycerol),         butane-1,2,4-triol, hexane-1,2,6-triol, benzene-1,2,3-triol         (pyrogallol), benzene-1,2,4-triol (hydroxyhydroquinone),         benzene-1,3,5-triol (phloroglucinol), hexane-1,2,3,4,5,6-hexaol         (sorbitol), 2-(2′-hydroxyethoxy)ethanol (diethylene glycol), and         2-[2′-(2″-hydroxyethoxy)ethoxy]ethanol (triethylene glycol).     -   (ix) Aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         hydroxynitriles (38), as exemplified by but not limited to         3-hydroxypropanenitrile, 3-hydroxybutanenitrile,         4-hydroxybutanenitrile, and 5-hydroxypentanenitrile.     -   (x) Aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         diamines (39), as exemplified by but not limited to         ethane-1,2-diamine (ethylene diamine), propane-1,2-diamine,         propane-1,3-diamine, butane-1,4-diamine, xexane-1,6-diamine, and         cyclohexane-1,2-diamine.     -   (xi) Aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         aminonitriles (40), as exemplified but not limited to         3-aminopropanenitrile, 3-aminopentanenitrile,         5-aminopentanenitrile, and 6-aminohexanenitrile.     -   (xii) Aliphatic, heteroaliphatic, cycloaliphatic,         cycloheteroaliphatic, aromatic, arylaliphatic and heteroaromatic         aminoalcohols (41-43), as exemplified by but not limited to         2-aminoethanol (ethanolamine), 2-aminopropan-1-ol,         2-aminobutan-1-ol, 4-aminobutan-1-ol,         bis(2-hydroxyethyl)amine(diethanolamine),         tris(2-hydroxyethyl)amine(triethanolamine),         2-(2′-aminoethoxy)ethanol (diethylene glycol amine),         2-aminophenol, and 3-aminophenol.

TABLE 4 Examples of Coordinating Ligands (C^(n) _(x′′′))

32

33

34 R^(1,6) = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,3,4,5) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

35

36

37 R^(1,6) = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,3,4,5) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

38

39

40 R¹ = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,3) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

41

42

43 R^(1,3,5) = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,4,6) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

The chelating hydroxycarboxylic acid-derived ligands L¹ _(a″″)L² _(b″″) . . . L^(n) _(x″″) are selected from, but not limited to the examples detailed below and depicted in Tables 5-7:

-   -   (i) Anions of aliphatic hydroxycarboxylic acids with a single         hydroxyl group and a single carboxyl group, as exemplified by         but not restricted to hydroxyacetic acid (glycolic acid, 45),         3-hydroxypropanoic acid (46), 2-hydroxypropanoic acid (lactic         acid, 47), 4-hydroxybutanoic acid (4-hydroxybutyric acid, 48),         3-hydroxybutanoic acid (3-hydroxybutyric acid, 49),         2-hydroxybutanoic acid (2-hydroxybutyric acid, 50),         3-hydroxy-2-methylpropanoic acid (3-hydroxyisobutyric acid, 51),         2-hydroxypentanoic acid (52), 3-hydroxypentanoic acid (53), and         3-hydroxy-3-methylbutanoic acid (54).     -   (ii) Anions of aliphatic hydroxycarboxylic acids with two or         more hydroxyl and/or carboxyl groups, as exemplified by but not         restricted to 2-hydroxypropane-1,3-dioic acid (tartronic acid,         55), 2-hydroxybutane-1,4-dioic acid (malic acid, 56),         2-hydroxypentane-1,5-dioic acid (57),         2-hydroxy-2-methylbutane-1,4-dioic acid (citramalic acid, 58),         3-carboxy-3-hydroxypentane-1,5-dioic acid (citric acid, 59),         3-carboxy-3-hydroxyhexane-1,6-dioic acid (homocitric acid, 60),         2,3-dihydroxypropanoic acid (glyceric acid, 61),         3,5-dihydroxy-3-methylpentanoic acid (mevalonic acid, 62),         2,3-dihydroxybutane-1,4-dioic acid (tartaric acid, 63),         2,3,4-trihydroxybutanoic acid (threonic acid, 64),         2,3,4,5,6-pentahydroxyhexanoic acid (gluconic acid, 65), and         2,3,4,5-tetrahydroxyhexane-1,6-dioic acid (mucic acid, 66).     -   (iii) Anions of cycloaliphatic hydroxycarboxylic acids, as         exemplified by but not restricted to         1,3,4,5-tetrahydroxycyclohex-1-carboxylic acid (quinic acid,         67), and 3,4,5-trihydroxycyclohex-1-ene-1-carboxylic acid         (shikimic acid, 68).     -   (iv) Anions of functionalized aliphatic or cycloaliphatic         hydroxycarboxylic acids, as exemplified by but not restricted to         2-(2′-hydroxyethoxy)butane-1,4-dioic acid (hydroxyethylsuccinic         acid, 69), 3-hydroxy-2-oxo-propanoic acid (hydroxypyruvic acid,         70), N,N-bis(2′-hydroxyethyl)-aminoethanoic acid (Bicine, 71),         2-amino-3-hydroxypropanoic acid (serine, 72),         2-amino-3-hydroxybutanoic acid (threonine, 73),         3-amino-4-hydroxybutanoic acid (homoserine, 74),         2-amino-4-hydroxybutanoic acid (β-homoserine, 75),         4-hydroxypyrrolidine-2-carboxylic acid (4-hydroxyproline, 76),         and 3-hydroxypyrrolidine-2-carboxylic acid (3-hydroxyproline,         77).

TABLE 5 Examples of Chelating Hydroxycarboxylic Acid Ligands

44 X = H or OH; Y = H or CO₂H; R^(1,2,3,4,5,6,7,8,9) = alkylene/ heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(10,11) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

45

46

47

48

49

50

51

52

53

54

55

56

57

58

59

60

61

62

63

64

65

66

67

68

69

70

71

72

73

74

75

76

77

-   -   (v) Anions of aryalkylhydroxycarboxylic acids, as exemplified by         but not restricted to 3-hydroxy-2-phenylpropanoic acid (tropic         acid, 78), 2-hydroxy-2-phenylethanoic acid (mandelic acid, 79),         and 2-hydroxy-2-(3′,4′-dihydroxyphenyl)ethanoic acid         (3,4-dihydroxymandelic acid, 80).     -   (vi) Anions of aromatic hydroxycarboxylic acids, exemplified by         but not restricted to 2-hydroxybenzoic acid (salicylic acid,         81), 2,3-dihydroxybenzoic acid (3-hydroxysalicylic acid, 82),         2,4-dihydroxybenzoic acid (4-hydroxysalicylic acid, 83),         2,5-dihydroxybenzoic acid (5-hydroxysalicylic acid, 84),         2,6-dihydroxybenzoic acid (6-hydroxysalicylic acid, 85),         3,4,5-trihydroxybenzoic acid (gallic acid, 86),         4-hydroxy-3-methoxybenzoic acid (vanillic acid, 87),         3-hydroxybenzene-1,2-dicarboxylic acid (3-hydroxyphthalic acid,         88), and 4-hydroxybenzene-1,2-dicarboxylic acid         (4-hydroxyphthalic acid, 89).     -   (vii) Anions of aryalkenylhydroxycarboxylic acids, as         exemplified by but not restricted to         3-(2′-hydroxyphenyl)prop-2-enoic acid (o-coumaric acid, 90),         3-(3′-hydroxyphenyl)prop-2-enoic acid m-coumaric acid, 91),         3-(4′-hydroxyphenyl)prop-2-enoic acid (p-coumaric acid, 92),         3-(3′,4′-dihydroxyphenyl)prop-2-enoic acid (caffeic acid, 93),         and 3-(3′-methoxy-4′-hydroxyphenyl)prop-2-enoic acid (ferulic         acid, 94).     -   (viii) Anions of functional arylhydroxycarboxylic acids, as         exemplified by but not restricted to         2-amino-2-(4′-hydroxyphenyl)ethanoic acid (hydroxyphenylglycine,         95), and 2-amino-3-(3′,4′-dihydroxyphenyl)propanoic acid         (dihydroxyphenylalanine, DOPA, 96).     -   (ix) Anions of heterocyclic hydroxycarboxylic acids, as         exemplified by but not restricted to         3-hydroxypyridine-2-carboxylic acid (3-hydroxypicolinic acid,         97), 4-hydroxypyridine-2-carboxylic acid (4-hydroxypicolinic         acid, 98), 6-hydroxypyridine-2-carboxylic acid         (6-hydroxypicolinic acid, 99), 2-hydroxypyridine-5-carboxylic         acid (6-hydroxynicotinic acid, 100),         2-hydroxypyridine-3-carboxylic acid (2-hydroxynicotinic acid,         101), 3-hydroxypyridine-4-carboxylic acid (3-hydroxyisonicotinic         acid, 102), and 2-hydroxyquinoline-4-carboxylic acid (103).     -   (x) Anions of conjugates of aliphatic and aromatic         hydroxycarboxylic acids, as exemplified by but not restricted to         chlorogenic acid (104).

TABLE 6 Further Examples of Chelating Hydroxycarboxylic Acid Ligands

78

79

80

81

82

83

84

85

86

87

88

89

90

91

92

93

94

95

96

97

98

99

100

101

102

103

104

-   -   (xi) Anions of derivatives of the hydroxycarboxylic acids         detailed above, including but not limited to esters, thioesters,         amides, N-substituted amides, imides, acylhydrazines, and         hydroxamic acids, as exemplified by but not limited to         2-O-esters (105 and 106) of 2,3-dihydroxybutane-1,4-dioc (63)         acid with monocarboxylic acids and dicarboxylic acids, and         monoesters, diesters, monoamides and diamides (107-110) of         3-carboxy-3-hydroxypentane-1,5-dioic acid (citric acid, 59).

TABLE 7 Examples of Chelating Hydroxycarboxylic Acid Derivative Ligands (C^(n) _(x′′′))

105

106

107 X = N or O; R¹ =alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,3) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

108

109

110 X = N or O; R^(1,4) = alkylene/heteroalkylene (C₀₋₁₈N₀₋₆O₀₋₆), cycloalkylene/ cycloheteroalkylene (C₃₋₈N₀₋₃O₀₋₃), arylene/heteroarylene (C₃₋₁₄N₀₋₃); R^(2,3,5,6) = H, alkyl/heteroalkyl (C₀₋₁₈N₁₋₆O₀₋₆), cycloalkyl/cycloheteroalkyl (C₃₋₈N₁₋₃O₀₋₃), aryl/heteroaryl (C₃₋₁₄N₁₋₃).

As previously stated, the admixtures of this invention, as depicted by Formula 1, contain chelate complexes of metals with hydroxycarboxylic acid-derived ligands, as exemplified by but not limited to metal-hydroxycarboxylate complexes. While the scientific literature describes the characterization and uses of metal-hydroxycarboxylate complexes in biological systems and environmental settings, there is no prior art on the use of metal-hydroxycarboxylate as admixtures for cements. See Lajunen, et al., Stability constants for alpha-hydroxycarboxylic acid complexes with protons and metal ions and the accompanying enthalpy changes—Part I: Aromatic ortho-hydroxycarboxylic acids, 1997 Pure Appl. Chem, 69: 329-381; Portanova, et al., Critical evaluation of stability constants for alpha-hydroxycarboxylic acid complexes with protons and metal ions and the accompanying enthalpy changes—Part II: Aliphatic 2-hydroxycarboxylic acids, 2003 Pure Appl. Chem. 75: 495-540; O. Happel, et al., Separation and characterization of aluminium malate species by ion chromatography, 2008: Anal. Bioanal. Chem. 392: 1373-1381; Dakanali, et al., A novel dinuclear species in the aqueous distribution of aluminum in the presence of citrate, 2003 Inorg. Chem. 42: 252-254; Matzapetakis, et al., Synthesis, structural characterization, and solution behavior of the first mononuclear, aqueous aluminum citrate complex, 1999 Inorg. Chem. 38: 618-619; Sheikh-Osman, et al., Aluminum carboxylates in aqueous solutions, 1993 J. Chem. Soc. Dalton Trans. 3229-3223; Feng, et al., Aluminum citrate: Isolation and structural characterization of a stable trinuclear complex, 1990: Inorg. Chem. 29: 408-411; Motekaitis, et al., Complexes of aluminum(III) with hydroxy carboxylic acids, 1984 Inorg. Chem. 23: 18-23; G. Bandoli, et al., Mononuclear six-coordinated Ga(III) complexes, 2009 Coord. Chem. Rev. 253: 56-77; N. Yang, H. Sun, Biocoordination chemistry of bismuth: Recent advances, 2007 Coord. Chem. Rev. 251: 2354-2366); Sadler, et al., Coordination chemistry of metals in medicine: Target sites for bismuth, 1999 Coord. Chem. Rev. 185-186: 689-709; Asato, et al., Synthesis, structure, and spectroscopic properties of bismuth citrate compounds and the bismuth-containing ulcer-healing agent colloidal bismuth subcitrate (CBS), 1995 Inorg. Chem. 34: 2447-2454); Szczepaniak, et al., Use of bismuth ion-selective electrode for investigation of bismuth complexes of citric and malic acids, 1986 Talanta, 33: 371-373; Tomita, et al., A water-soluble titanium complex for the selective synthesis of nanocrystalline brookite, rutile, and anatase by a hydrothermal method, 2006 Angew. Chem. Int. Ed. 45: 2378-2381; Deng, et al., pH-Dependent isolations and spectroscopic, structural, and thermal studies of titanium citrate complexes, 2004: Inorg. Chem. 43: 6266-6273; Todorovskya, et al., On the chemical nature of lanthanum-titanium citric complexes, precursors of La₂Ti₂O₇, 2004 Mater. Lett. 58: 3559-3563; Ruzdic, et al., Coordination properties of α-hydroxy carboxylic acids. Part I. Binuclear niobium(V) complex acids and some salts, 1984 Inorg. Chim. Acta, 88: 99-103; Brnicevic, et al., Coordination complexes of niobium and tantalum. XI. Crystalline malato complexes of niobium(V), 1971 J. Less Common Metal. 23: 61-66; J. J. Lingane, Polarographic investigation of oxalate, citrate and tartrate complexes of ferric and ferrous iron, J. Am. Chem. Soc. 68: 2448-2454; Zhang, et al., Syntheses, spectroscopies and structures of zinc complexes with malate, 2009 Inorg. Chim. Acta 362: 2643-2649; L. Meites, Polarographic studies of metal complexes. V. The cadmium(II), zinc(II) and iron(III) citrates, 1951 J. Am. Chem. Soc. 73: 3727-3732; Biagioli, et al., Molecular structure, characterization and reactivity of dioxo complexes formed by vanadium(V) with α-hydroxycarboxylate ligands, 2000 Inorg. Chim. Acta 310: 1-9); Zhou, et al., Syntheses, crystal structures and biological relevance of glycolato and S-lactato molybdates, 2004 J. Inorg. Biochem. 98: 1037-1044); —H. Zhou, et al., Synthesis and characterization of homochiral polymeric S-malatomolybdate(VI), 2002 J. Inorg. Biochem. 90: 137-143; Zhang, et al., pH-and mol-ratio dependent tungsten(VI)-citrate speciation from aqueous solutions: syntheses, spectroscopic properties and crystal structures, 2003 Inorg. Chim. Acta 351: 311-318; and Zhou, et al. Tungsten-malate interaction. Synthesis, spectroscopic and structural studies of homochiral S-malato tungstate(VI), Λ-Na ₃ [WO ₂H(S-mal)₂], 2001 Inorg. Chim. Acta 314: 184-188;

Similarly, while the patent literature describes the use of metal-hydroxycarboxylate complexes as pharmaceutical agents, cosmetics agents, and as modifiers for textiles, polymers and minerals, there is no prior art relating to the use of metal-hydroxycarboxylate complexes as admixtures for cements. The use of hydroxycarboxylate complexes of aluminum, bismuth, chromium, iron, magnesium and zinc as medicinal agents is described in U.S. Pat. No. 3,200,136, U.S. Pat. No. 6,903,235, U.S. Pat. No. 2,644,828, U.S. Pat. No. 7,005,531, U.S. Pat. No. 5,008,256, U.S. Pat. No. 5,206,265, U.S. Pat. No. 7,767,851, U.S. Pat. No. 3,591,616, U.S. Pat. No. 6,903,235, U.S. Pat. No. 5,165,914, U.S. Pat. No. 1,964,696, U.S. Pat. No. 3,506,761, G.B. Patent 843865 and G.B. Patent 949405. The use of hydroxycarboxylate complexes of aluminum, magnesium, titanium and zirconium as astringent and antiperspirant agents is described in U.S. Pat. No. 3,090,728, U.S. Pat. No. 2,498,514, U.S. Pat. No. 4,021,536, U.S. Pat. No. 391176, U.S. Pat. No. 3,712,948, U.S. Pat. No. 3,734,940, U.S. Pat. No. 6,632,421 and G.B. Patent 843865. The use of hydroxycarboxylate compexes of iron as solvents for cellulose is described in U.S. Pat. No. 4,265,675 and U.S. Pat. No. 4,705,876. The use of hydroxycarboxylate complexes of aluminum as crosslinking agents for polymers is described in U.S. Pat. No. 4,601,340 and U.S. Pat. No. 5,559,263. The use of hydroxycarboxylate complexes of aluminum, chromium, iron and zirconium as drilling aids for petroleum recovery is described in U.S. Pat. No. 5,532,211, U.S. Pat. No. 4,129,183 and U.S. Pat. No. 3,843,524.

Examples of known metal-hydroxycarboxylate complexes of metals from the scandium family (111), titanium family (112), vanadium family (113), chromium family (114), manganese, iron, cobalt, nickel, copper and zinc families (115), boron family (116), carbon family (117), and nitrogen family (118) are provided in Table 8.

TABLE 8 Examples of Metal-Hydroxycarboxylate Complexes [La^(III)(CitH⁻³)] NH₄[La^(III)(CitH⁻⁴)] 111 (NH₄)₂[Ti(GlyH⁻²)₃] (NH₄)₂[Ti(LacH⁻²)₃] Na₂[Ti(CitH⁻²)₃] Na₃[Ti(CitH⁻³)(CitH⁻²)₂] Na₄[Ti(CitH⁻³)₂(CitH⁻²)] Na₆[Ti(CitH⁻⁴)(CitH⁻³)₂] K₅[Ti(CitH⁻³)₃] Na₈[Ti(CitH⁻⁴)₃] (NH₄)₆[Ti₄(O₂)₄(μ-O)₂(GlyH⁻²)₄(GlyH⁻¹)₂] (NH₄)₄[Ti₂(O₂)₂(CitH⁻⁴)₂] Ba₂(NH₄)₂[Ti₄(O₂)₄(CitH⁻⁴)₂(CitH⁻³)₂] (NH₄)₈[Ti₄(O₂)₄(CitH⁻⁴)₄] Na₄[Zr₂(LacH⁻²)₆] Na₄[Zr₂(LacH⁻²)₆] 112 Rb₂[{V^(V)O₂(GlyH⁻²)}₂] Cs₂[{V^(V)O₂(LacH⁻²)}₂] Cs₂[{V^(V)O₂(MalH⁻²)}₂] NH₄[Nb^(V) ₂O₄(GlyH⁻¹)(GlyH⁻²)] NH₄[Nb^(V) ₂O₄(LacH⁻¹)(LacH⁻²)] NH₄[Nb^(V) ₂O₃(MalH⁻²)(MalH⁻³)] K[Nb^(V) ₂O₂(OH)(MalH⁻³)₂] Li[Nb^(V) ₂O(MalH⁻³)₃] Ca[Nb₂O₂[TarH⁻⁴]₂] 113 Py₂[Cr^(III)(CitH⁻³)(CitH⁻²)] K₂[Mo^(VI)O₂(GlyH⁻²)₂] K₂[Mo^(VI)O₂(LacH⁻²)₂] Na₃[Mo^(VI)O₂(MalH⁻²)(MalH⁻³)] (NH₄)₂[Mo^(VI)O₂(MalH⁻²)₂] (NH₄)₄[Mo^(VI)O₂(MalH⁻³)₂] (NH₄)₄[Mo^(VI) ₄O₁₁(MalH⁻³)₂] K₄[(Mo^(VI)O₂)₂O(CitH⁻³)₂] K₂Na₄[(Mo^(VI)O₂)₂O(CitH⁻⁴)₂] Na₂[W^(VI)O₂(CitH⁻²)₂] Na₃[W^(VI)O₂(MalH⁻²)(MalH⁻³)] NaK₃[W^(VI) ₂O₅(CitH⁻³)₂] K₄[W^(VI)O₃(CitH⁻⁴)] 114 [Fe^(III) ₂(MalH⁻³)₂)] Ca[Fe^(III) ₂(MalH⁻⁴)₂] K₃[Fe^(III) ₃(MalH⁻³)₄] K[Fe^(III) ₂(MalH⁻⁴)•(MalH⁻³)] [Fe^(III)(MalH⁻²)•(Mal⁻¹)] [Fe^(II)(CitH⁻²)] [Fe^(III)(CitH⁻²)]NO₃ [Fe^(III)(CitH⁻³)] [Fe^(III) ₂(CitH⁻²)₃] Na[Fe^(III)(CitH⁻⁴)] K₃[Fe^(III)(CitH⁻³)₂] [Fe^(III)(OH)(H₂PO₄)(CitH⁻¹)] Na₂[Fe^(III)(OH)(H₂PO₄)₂(CitH⁻²)] Na₃[Fe^(III)(H₂PO₄)₂(CitH⁻²)₂] [Zn(MalH⁻¹)₂(H₂O)₂] [Zn₂(MalH⁻²)₂(H₂O)₄] (NH₄)[Zn(MalH⁻¹)₃] (NH₄)₂[Zn(MalH⁻²)₂] 115 Li[B(MalH⁻²)₂] Zn[B(CitH⁻²)₂]₂ Rb[B(SalH⁻²)₂] [Al(GlyH⁻²)]NO₃ Na[Al(GlyH⁻²)₂] Na₃[Al(GlyH⁻²)₃] [Al(LacH⁻²)]NO₃ Na[Al(LacH⁻²)₂] Na₃[Al(LacH⁻²)₃] [Al(MalH⁻²)(MalH⁻¹)] Na[Al₂(MalH⁻²)₂(MalH⁻³)] Na₃[Al₃(MalH⁻³)₄] Na[Al₂(MalH⁻⁴)(MalH⁻³)] Na₂[Al₂(MalH⁻⁴)₂] Na[Al(CitH⁻²)] [Al(CitH⁻³)] [Al₂(CitH⁻²)₃] K₄[Al₂(CitH⁻³)₂(CitH⁻⁴)] K₄[Al₃(CitH⁻³)₃(OH)] K[Al[CitH⁻⁴)] Na₅[Al(CitH⁻⁴)₂] Na₄[Al(CitH⁻³)(CitH⁻⁴)] Na₇[Al₃(CitH⁻⁴)₃(OH)₄] K₃[Al(CitH⁻³)₂] Na[Al(TarH⁻⁴)] Na[Al(TarH⁻²)₂] Na₄[Al(TarH⁻³)(TarH⁻⁴)] Na₇[Al(TarH⁻⁴)(TarH⁻³)₂] Na₈[Al(TarH⁻⁴)₂(TarH⁻³) Na₉[Al(TarH⁻⁴)₃] [Al(MucH⁻³)] K[Al(MucH⁻⁴)] 116 Na₂[Ge^(IV)(MalH⁻³)₂] Na₂[Ge^(IV)(CitH⁻³)₂] [Ge^(IV)(CitH⁻³)Cl(Bipy)] 117 [Bi(LacH⁻¹)₃] [Bi(MalH⁻³)] (NH₄)₃[Bi(MalH⁻³)₂] (NH₄)₈[Bi₂(CitH⁻⁴)₂(CitH⁻³)₂(H₂O)₄] K₅[Bi₂(CitH⁻⁴)₂(CitH⁻³)] K[Bi(CitH⁻⁴)₂] KNH₄[Bi₂(CitH⁻⁴)₂] K₆[Bi₆O₄(CitH⁻⁴)₄] K₁₂[Bi₁₂O₈(CitH⁻⁴)₈] [Bi(TarH⁻¹)(TarH⁻²)] NH₄[Bi(TarH⁻²)₂] [Bi₂(SalH⁻¹)₆(Bipy)₂] [Bi₂(SalH⁻¹)₂(SalH⁻²)₂(Phen)₂] 118 Notes. GlyH_(−x) is glycolate anion; LacH_(−x) is lactate anion; MalH_(−x) is malate anion; CitH_(−x) is citrate anion; TarH_(−x) is tartarate anion; MucH_(−x) is mucate anion; SalH_(−x) is salicylate anion; Phen is 1,10-phenanthroline; Bipy is 2,2′-bipyridine

The admixtures of the present invention can be prepared by a variety of methods, including but not limited to:

(i) The reaction of a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal, and/or metal oxide, hydroxide, carbonate and/or basic carbonate with one or more hydroxycarboxylic acid-derived ligands, as exemplified by but not limited to:

2Al+2Cit→2[Al(CitH⁻³)]+3H₂↑  (a)

Al₂O₃+4Mal→2[Al(MalH⁻²)(MalH⁻¹)]+3H₂O  (b)

2Al(OH)₃+3Cit→[Al₂(CitH⁻²)₃]+6H₂O  (c)

Fe^(II)CO₃+Cit→[Fe^(II)(CitH⁻²)]+CO₂↑+H₂O  (d)

(BiO)₂CO₃+2Mal→2[Bi(MalH⁻³)]+CO₂↑+3H₂O  (e)

(ii) The reaction of a group IA and/or IIA metal oxide, hydroxide, carbonate, basic carbonate and/or hydrogencarbonate, with a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal oxide, and one or more hydroxycarboxylic acid-derived ligands, as exemplified by but not limited to:

MgO+MoO₃+2Lac→Mg[MoO₂(LacH⁻²)₂]+2H₂O  (a)

KOH+Nb₂O₅+2Mal→K[Nb₂O₂(OH)(MalH⁻³)₂]+3H₂O  (b)

Ca(OH)₂+B₂O₃+4Mal→Ca[B(MalH⁻²)₂]₂+5H₂O  (c)

4NaOH+2Ca(OH)₂+Al₂O₃+4Tar→2CaNa₂[Al(TarH⁻³)(TarH⁻⁴)]+11H₂O  (d)

Li₂CO₃+2Nb₂O₅+6Mal→2Li[Nb₂O(MalH⁻³)₃]+CO₂↑+9H₂O  (e)

NaHCO₃+Al₂O₃+3Mal→Na[Al₂(MalH⁻²)₂(MalH⁻³)]+CO₂↑+4H₂O  (f)

(iii) The reaction of a group IA and/or IIA metal oxide, hydroxide, carbonate, basic carbonate and/or hydrogencarbonate, with a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal hydroxide, and one or more hydroxycarboxylic acid-derived ligands, as exemplified by but not limited to:

BaO+2Fe^(III)(OH)₃+Mal→Ba[Fe^(III) ₂(MalH⁻⁴)₂]+7H₂O  (a)

Mg(OH)₂+2B(OH)₃+4Cit→Zn[B(CitH⁻²)₂]₂+8H₂O  (b)

4NaOH+2Zr(OH)₄+6Lac→Na₄[Zr₂(LacH⁻²)₆]+10H₂O  (c)

5K₂CO₃+4Bi(OH)₃+6Cit→2K₅[Bi₂(CitH⁻⁴)₂(CitH⁻³)]+5CO₂↑+17H₂O  (d)

2NaHCO₃+Zn(OH)₂+2Mal→Na₂[Zn(MalH⁻²)₂]+2CO₂↑+4H₂O  (e)

(iv) The reaction of a group IA and/or IIA metal oxide, hydroxide, carbonate, basic carbonate and/or hydrogencarbonate, with a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal carbonate and/or basic carbonate, and one or more hydroxycarboxylic acid-derived ligands, as exemplified by but not limited to:

10NaOH+Zn₅(OH)₆(CO₃)₂+10Mal→5Na₂[Zn(MalH⁻²)₂]+2CO₂↑+18H₂O  (a)

3K₂CO₃+3(BiO)₂CO₃+4Cit→K₆[Bi₆O₄(CitH⁻⁴)₄]+6CO₂↑+8H₂O  (b)

3KHCO₃+FeCO₃+2Cit→K₃[Fe^(III)(CitH⁻³)₂]+4CO₂↑+4H₂O  (c)

(v) The reaction of a metal oxometallate of a group IA and/or IIA metal with a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal, and one or more hydroxycarboxylic acid-derived ligands, with or without the presence of a group IA and/or IIA metal hydroxide, carbonate, basic carbonate and/or hydrogencarbonate, and with or without the presence of a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal oxide, hydroxide, carbonate and/or basic carbonate, as exemplified by but not limited to:

Na₂Al₂O₄+4Gly→2Na[Al(GlyH⁻²)₂]+4H₂O  (a)

Na₂Al₂O₄+4NaOH+6Gly→2Na₃[Al(GlyH⁻²)₃]+8H₂O  (b)

Li₂TiO₃+LiOH+3Cit→Li₃[Ti(CitH⁻³)(CitH⁻²)₂]+4H₂O  (c)

2KNbO₃+Nb₂O₅+4Mal→2K[Nb^(V) ₂O₂(OH)(MalH⁻³)₂]+5H₂O  (d)

(vi) The reaction of a salt of a group IA and/or IIA metal with one or more hydroxycarboxylic acid-derived ligands, with a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal, and/or metal oxide, hydroxide, carbonate and/or basic carbonate, with or without the presence of one or more hydroxycarboxylic acid-derived ligands, as exemplified by but not limited to:

4Na₂(TarH⁻²)+2Al→2Na₄[Al(TarH⁻³)(TarH⁻⁴)]+3H₂↑  (a)

2NH₄(LacH⁻¹)+TiO₂+Lac→(NH₄)₂[Ti(LacH⁻²)₃]+2H₂O  (b)

4K₃(CitH⁻³)+6Bi₂O₃+4Cit→K₁₂[Bi₁₂O₈(CitH⁻⁴)₈]+10H₂O  (c)

K₃(CitH⁻³)+3Al(OH)₃+2Cit→3K[Al(CitH⁻⁴)]+9H₂O  (d)

(vii) The reaction of a group IA and/or IIA metal oxide, hydroxide, carbonate, basic carbonate and/or hydrogencarbonate, with the salt of a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal with a group IIIA, IVA, VA, VIA and/or VIIA nonmetal, and one or more hydroxycarboxylic acid-derived ligands, with or without the presence of a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal oxide, hydroxide, carbonate and/or basic carbonate, as exemplified by but not limited to:

14NaOH+Al₂(SO₄)₃+4Cit→2Na₄[Al(CitH⁻³)(CitH⁻⁴)]+3Na₂SO₄+14H₂O  (a)

3Ca(OH)₂+Al₂(SO₄)₃+4Mal→2[Al(MalH⁻²)(MalH⁻¹)]+3CaSO₄↓+6H₂O  (b)

2NaOH+CaCO₃+ZnSO₄+2Mal→Na₂[Zn(MalH⁻²)₂]+CaSO4↓+CO₂↑+4H₂O  (c)

(viii) The reaction of a group IA and/or IIA metal oxide, hydroxide, carbonate, basic carbonate and/or hydrogencarbonate, and/or a salt of a group IA and/or IIA metal with one or more hydroxycarboxylic acid-derived ligands, with an ore/mineral and/or mining byproduct and/or industrial byproduct containing a group IIA, IIIA, IVA, VA, IB, IIB, IIIB, IVB, VB, VIIB, VIIB and/or VIIIB metal, with or without one or more hydroxycarboxylic acid-derived ligands, as exemplified by but not limited to:

6Na(MalH⁻¹)+3Al₂SiO₅(Kyanite)+2Mal→2Na₃[Al₃(MalH⁻³)₄]+3SiO₂↓+9H₂O  (a)

4Na₂(CitH⁻²)+Al₂Si₂O₅(OH)₄(Kaolin)→2Na₄[Al(CitH⁻³)(CitH⁻⁴)]+2SiO₂↓+5H₂O  (b)

2K(CitH⁻¹)+2K₂(CitH⁻²)+3Bi₂S₃(Bismuthinite)+7O₂→K₆[Bi₆O₄(CitH⁻⁴)₄]+9S↓+5H₂O  (c)

Reactions may be conducted using crude, partially-purified or substantially pure hydroxycarboxylic acid-derived ligand feedstocks. Crude and partially-purified feedstocks for hydroxycarboxylic acid-derived ligands are exemplified by, but not limited to:

-   -   (i) Crude, filtered, concentrated, crystallized and/or extracted         fermentation broths containing hydroxycarboxylic acids such as         glycolic, lactic, malic, citric, citramalic and/or tartaric         acid. The fermentation production of hydroxycarboxylic acids is         described in the publications, Berovic, et al., Citric Acid         Production, 2007 Annu. Rev. Biotechnol. 13: 303-343; Hofvendahl,         et al., Factors affecting the fermentative lactic acid         production from renewable resources, 2007 Enzyme Microb.         Technol. 26: 87-107; John, et al., Fermentative production of         lactic acid from biomass: An overview on process developments         and future perspectives, 2007: Appl. Microbiol. Biotechnol. 74:         524-534; and Aristidou, et al., Metabolic engineering         applications to renewable resource utilization, 2000 Curr. Opin.         Biotechnol. 11: 187-199);     -   (ii) Crude, filtered, concentrated, crystallized and/or         extracted fruit juices and fermented fruit juices containing         hydroxycarboxylic acids such as glycolic, lactic, malic, citric,         citramalic and/or tartaric acid;     -   (iii) Crude, filtered, concentrated, crystallized and/or         extracted reaction mixtures resulting from the catalytic and/or         non-catalytic aerobic and/or non-aerobic oxidation of         monosaccharides, oligosaccharides, polysaccharides, fats, oils,         resins, extractives, biomass components, and/or biomass. These         oxidation reactions are described by Collinson, et al., The         catalytic oxidation of biomass to new materials focusing on         starch, cellulose and lignin, 2010 Coord. Chem. Rev. 254:         1854-1870; and Aouf, et al., Low Catalyst loadings for the         production of carboxylic acids from polysaccharides and hydrogen         peroxide, 2010 Chem. Sus. Chem. 3: 1200-1203);     -   (iv) Crude, filtered, concentrated, crystallized and/or         extracted reaction mixtures resulting from the catalytic and/or         non-catalytic interconversion of hydroxycarboxylic acids and         their derivatives such as esters, thioesters, amides,         N-substituted amides, imides, N-acylhydrazines and hydroxamic         acids, as exemplified by, but not limited to the partial         esterification and/or partial amidation of hydroxypolycarboxylic         acids with aliphatic alcohols and/or aliphatic amines         respectively; and the partial hydrolysis and/or partial         aminolysis of polyalkyl hydroxypolycarboxylates to form the         corresponding partial esters or ester amides.

Reactions may be conducted in solution or in suspension, in a variety of solvents, including but not limited to water, a mixture of water and an organic solvent exemplified by but not limited to methanol, ethanol, propan-1-ol, propan-2-ol (isopropanol), ethane-1,2-diol (ethylene glycol), propane-1,2,3-triol (glycerol), 2-ethoxyethanol (diethylene glycol), and 2-(2′-ethoxyethoxy)ethanol (triethylene glycol), or a water-free organic solvent exemplified by but not limited to methanol, ethanol, propan-1-ol, propan-2-ol (isopropanol), ethane-1,2-diol (ethylene glycol), propane-1,2,3-triol (glycerol), 2-ethoxyethanol (diethylene glycol), and 2-(2′-ethoxyethoxy)ethanol (triethylene glycol). When a mixture of water and organic solvent is used, the water content may range from 5% to 95% v/v, preferably 15% to 85% v/v, and more preferably 25% to 75% v/v.

When a solvent is used, the substrates and/or product(s) may be soluble or insoluble to varying degrees, and the reaction system may vary from homogeneous to heterogeneous. Furthermore, the nature of the reaction mixture may change during the course of the reaction, as exemplified by but not limited to the dissolution of initially insoluble or partially soluble reactants, and/or the transient precipitation/crystallization and subsequent dissolution of reaction intermediates(s) and/or the precipitation/crystallization of product(s).

When a solvent is used, the net concentration of the reactants is 5-80% w/w, and preferably 10-60% w/w, and more preferably 20-40% w/w.

Reactions may be conducted in the absence of solvent, or in the presence of a small amount (<20% w/w) of a solvent/adjuvant. Reactions may be performed by blending, grinding or milling a mixture of the reactants, with or without the addition of the solvent/adjuvant. The solvent/adjuvant is exemplified by but not limited to water, methanol, ethanol, propan-1-ol, propan-2-ol (isopropanol), ethane-1,2-diol (ethylene glycol), propane-1,2,3-triol (glycerol), 2-ethoxyethanol (diethylene glycol), and 2-(2′-ethoxyethoxy)ethanol (triethylene glycol).

Reactions may be conducted such that water and/or organic solvents are partially or fully removed by evaporation/distillation during the course of the reaction, in order to obtain a soluble concentrate of the product, a slurry of the product, a paste of the product, or a substantially or completely dry solid or semi-solid product.

Reactions may be conducted such that evolved gases, as exemplified by carbon dioxide and hydrogen, are partially or fully removed by sparging with a gas such as air, nitrogen or helium, or by the application of a vacuum of 0.01-0.98 bar.

Reactions may be conducted with sparging with a gas such as air or oxygen, when oxidizing conditions are desired—for example when the oxidation of a sulfide-containing reactant to elemental sulfur is desired. Alternatively, sparging with nitrogen or helium may be used when suppression of oxidation is desired—for example when complexes of iron(II) are being prepared and prevention of oxidation to iron(III) is needed.

Reactions may be conducted at ambient temperature, or at temperatures of 243-473 K, and preferably 273-423 K, and more preferably 293-373 K.

Reactions may be conducted at ambient pressure, or at pressures of 0.1-20 bar, and preferably 0.5-10 bar, and more preferably 1-5 bar.

Reactions may be conducted in non-pressurized or pressurized batch, semi-continuous or continuous glass or metal reactors, exemplified by but not limited to stirred tank reactors, packed bed reactors, fluidized bed reactors, bead mills, jet mills, homogenizers, colloid mills, ball mills, rotor-stator mixers, pug mills, and screw extruders.

The admixtures of the present invention may be prepared to contain one or more complexes as described above by Formula 1. The admixtures may be used as prepared, or may be further processed, as exemplified by but not limited to:

-   -   (i) Clarification/filtration of suspensions to furnish the         admixtures as solutions with product concentrations of 10-80%         w/w, and preferably 15-70% w/w, and more preferably 20-60% w/w.         Clarification/filtration may be accomplished by various methods,         including but not limited to plate filtration, fabric         filtration, tubular filtration, leaf filtration, filter         pressing, centrifugal filtration and centrifugation.     -   (ii) Concentration of solutions or suspensions to furnish the         admixtures as soluble or suspension concentrates, or slurries,         with product concentrations of 20-90% w/w, and preferably 30-80%         w/w, and more preferably 40-70% w/w. The removal of solvent may         be accomplished by various methods, including but not limited to         rotary evaporation, rising film evaporation, circulation         evaporation, falling film evaporation, fluidized bed         evaporation, plate evaporation, spiral tube evaporation, and         reverse osmosis. Furthermore, concentration may be combined with         solvent exchange.     -   (iii) Crystallization of solutions or suspensions to furnish the         admixtures as crystalline or semi-crystalline products. These         crystalline products may be relatively pure and contain         predominantly one complex, or may be semi-pure and contain a         mixture of distinct complexes. Furthermore, the crystalline         products may be anhydrous or may be hydrated/solvated.         Crystallization may be accomplished by accomplished various         methods, including but not limited to cooling and/or evaporative         methods, and using such equipment as stirred tank crystallizers         and fluidized bed crystallizers. Crystallization may be         accomplished by heating solutions or suspensions up to 293-373         K, and preferably to 303-363 K, and more preferably to 313-353         K, and concentrating the solution or suspension such that the         product concentration is 20-90% w/w, and preferably 30-80% w/w,         and more preferably 40-70% w/w. This may be followed by cooling         to 263-313 K, and preferably to 273-303 K, and more preferably         to 278-228 K. This may be further combined with seeding with         appropriate seed crystals, comprised of the desired complex, or         of an isomorphous crystalline compound. This may be further         combined with the addition of an anti-solvent, including but not         limited to methanol, ethanol, propan-1-ol, propan-2-ol         (isopropanol), ethane-1,2-diol (ethylene glycol),         propane-1,2,3-triol (glycerol), 2-ethoxyethanol (diethylene         glycol), and 2-(2′-ethoxyethoxy)ethanol (triethylene glycol).         The crystalline suspension may be used as is, with or without         solvent exchange. Alternatively, the crystalline product may be         separated by sedimentation/decantation, centrifugation and/or         filtration. The separated crystalline product may be partially         or fully dried to furnish an anhydrous or hydrated/solvated         solid crystalline or semi-crystalline product. Drying may be         accomplished by various methods, including but not limited to         plate drying, drum drying, rotary louvre drying, rotary steam         tube drying, and fluidized bed drying.     -   (iv) Concentration of solutions or suspensions, followed by         granulation and/or extrusion and/or partial or complete drying,         to furnish the admixtures as powders, flakes, granules or         pellets. The products may be amorphous, semi-crystalline or         crystalline, and may be anhydrous or hydrated/solvated. Drying         may be accomplished by various methods, including but not         limited to plate drying, drum drying, rotary louvre drying,         rotary steam tube drying, fluidized bed drying and spray drying.         Drying may be integrated with flaking, granulation, extrusion         and/or powdering.     -   (v) Adsorption of solutions, suspensions or slurries onto solid         carriers, followed by granulation and/or extrusion and/or         partial or complete drying, to furnish the admixtures as         solid-supported powders, flakes, granules or pellets, with         product concentrations of 10-90% w/w, and preferably 20-80% w/w,         and more preferably 30-70% w/w. The carrier is exemplified by,         but not limited to: (a) a biomass product such as wood flour,         wood sawdust, peat, coconut coir and coconut shell powder; (b) a         rock or mineral product such as kaolin, calcined kaolin, china         clay, perlite, expanded perlite, exfoliated vermiculite,         bauxite, calcined bauxite, red mud, brucite, clay,         montmorillonite clay, smectite clay, illite clay, chlorite clay,         bentonite clay, halloysite clay, imogolite clay, diatomaceous         earth, volcanic ash, tuff, chalk, limestone and gypsum; (c) a         combustion product such as rice hull ash, sugarcane bagasse ash         and fly ash. The product concentration in the solution,         suspension or slurry is 10-90% w/w, and preferably 15-80% w/w,         and more preferably 20-70% w/w. Adsorption may be accomplished         by various methods, including but not limited to drum coating         and fluidized bed coating. Drying may be accomplished by various         methods, including but not limited to plate drying, drum drying,         rotary louvre drying, and fluidized bed drying.

The admixtures of the present invention, prepared as described above, may be employed as admixtures for hydraulic cements in a number of ways, as exemplified by, but not limited to:

-   -   (i) Addition of admixtures, as solutions, suspensions, slurries         or solids, during any stage of the preparation of the cement         paste, mortar or concrete, and as typified by the addition of         admixtures to the mixing water;     -   (ii) Blending of admixtures as solids with dry cements or cement         components (OPC and/or SCMs) and/or aggregate, to form premixes,         that may be stored as desired, and made into a cement paste,         mortar or concrete when needed.

The admixtures of the present invention, prepared as described above, may be employed at dosages of 0.1-20% w/w (active solids with respect to the cement), and preferably 0.15-10% w/w, and more preferably 0.2-5% w/w.

The admixtures of the present invention, prepared as described above, may be combined together to form blended admixtures.

The admixtures of the present invention, prepared as described above, may be combined with conventional chemical admixtures as exemplified by, but not limited to water-reducers, superplasticizers, viscosity control agents, set accelerators, set retarders, rebar corrosion inhibiting agents, waterproofing agents, and air entraining agents.

The above examples are indicative of preformed complexes of metals with hydroxycarboxylic acid derivatives that are prepared as solutions, suspensions, slurries or solids, and are then subsequently used as admixtures for cement compositions. Alternatively, the same complexes may be formed in-situ in cement compositions by combining in the dry state, the individual precursors used to form the complexes, or combinations of the precursors, with the cement, mortar, grout or concrete components.

For example, in the case of the complex [Al(CitH⁻³)], aluminum(III) hydroxide (Al(OH)₃) and anhydrous citric acid (Cit) may be used as precursors. The required molar ratio (1:1 mol ratio of Al(OH)₃ and Cit) of these may be blended with fly ash C to produce a dry fly ash C—Al(OH)₃-Cit blend, which may be stored as required until used. When this blend is mixed with water, the precursors react to form the indicated complex in-situ, and this then exerts its effect(s) as a chemical admixture on the desired fly ash C cement.

Similarly, in the case of the complex Na₃[Al(GlyH⁻²)₃], sodium carbonate (Na₂CO₃) and aluminum(III) glycolate (Al(Gly)₃) may be used as precursors. The required molar ratio (3:2 mol ratio of Na₂CO₃ and Al(Gly)₃) of these may be blended with OPC and fly ash F respectively, and the obtained OPC-Na₂CO₃ and fly ash F—Al(Gly)₃ blends stored separately as a two-component cement, or combined to form a OPC-fly ash-Na₂CO₃—Al(Gly)₃ blended cement. As before, the addition of water, to a mixture of the separate OPC-Na₂CO₃ and fly ash F—Al(Gly)₃ products, or to the OPC-fly ash F—Na₂CO₃—Al(Gly)₃ mixture, results in the formation of the desired complex in-situ, and this exerts its action on the desired OPC-fly ash F blended cement.

EXAMPLES A. General 1. Materials

The chemicals used in the following Examples were obtained from Sigma-Aldrich Corporation, St. Louis, Mo., USA, American Elements, Los Angeles, Calif., USA, and Reade Advanced Materials, Reno, Nev., USA. The following chemicals were used: sodium hydroxide (NaOH, 99%, pellets); potassium hydroxide (KOH, 99%, pellets); lithium hydroxide (LiOH, 99%, powder); aluminum(III) hydroxide (Al(OH)₃, 99%, 18% water, powder); magnesium hydroxide (Mg(OH)₂, 99%, powder); calcium hydroxide (Ca(OH)₂, 97%, powder); iron(III) hydroxide (Fe(OH)₃, 98%, powder); aluminum(III) oxide (Al₂O₃, 99%, powder); bismuth(III) oxide (Bi₂O₃, 99%, powder); indium(III) oxide (In₂O₃, 99%, powder); gallium(III) oxide (Ga₂O₃, 99%, powder); zinc(II) oxide (ZnO, 99%, powder); zirconium(IV) hydroxide (Zr(OH)₄, 99%, powder); lanthanum(III) oxide (La₂O₃, 99%, powder); yttrium(III) oxide (Y₂O₃, 99%, powder); molybdenum(VI) oxide (MoO₃, 99%, powder); tungsten(VI) oxide (WO₃, 99%, powder); sodium carbonate (Na₂CO₃, 99%, powder); magnesium carbonate (MgCO₃, 99%, powder); calcium carbonate (CaCO₃, 99%, powder); aluminum(III) chloride hexahydrate (AlCl₃.6W, 98%, powder); dialuminum(III) chloride pentahydroxide (Al₂Cl(OH)₅, 95%, 50% w/w aqueous); aluminum(III) sulfate hexadecahydrate (Al₂(SO₄)₃.16W, 95%, powder); sodium aluminate(III) (Na₁₅Al₁₁O₂₄, 98%, powder); acetic acid (C₂H₄O₂, 99%, liquid); glycolic acid (C₂H₄O₃, 99%, 70% w/w aqueous liquid); DL-lactic acid (C₃H₆O₃, 99%, 90% w/w aqueous liquid); DL-malic acid (C₄H₆O₅, 99%, powder); citric acid (C₆H₈O₇, 99%, powder); tartaric acid (C₄H₆O₆, 99%, powder); DL-2-hydroxybutyric acid (C₄H₈O₃, 97%, liquid); DL-3-hydroxybutyric acid (C₄H₈O₃, 98%, liquid); DL-citramalic acid (C₅H₈O₅, 99%, powder); mucic acid (C₆H₁₀O₈, 99%, powder); caffeic acid (C₉H₈O₄, 98%, powder); chlorogenic acid (C₁₆H₁₈O₉, 95%, powder); 2,3-dihydroxybenzoic acid (C₇H₆O₄, 99%, powder); boric acid (H₃BO₃, 99%, powder); phosphoric acid (H₃PO₄, 99%, 85% w/w aqueous liquid).

SikaSet NC and SikaSet HE accelerating, water-reducing and superplasticizing admixtures, were obtained from Sika Corporation, Lyndhurst, N.J., USA. Pozzutec 20+ accelerating and water-reducing admixture was obtained from BASF Corporation, Florham Park, N.J., USA.

Type II OPC was obtained from Lehigh Southwest Cement Company, San Ramon, Calif., USA. Fly ash C and fly ash F were obtained from Boral Material Technologies, San Antonio, Tex., USA. Concrete sand was obtained from Graniterock, San Jose, Calif., USA. Limestone powder was obtained from Greymont Inc., Salt Lake City, Utah, USA. Basic oxygen furnace and electric arc furnace slags were obtained from Ecocem, Dublin, Ireland. Seawater brucite fines were obtained from the Moss Landing Business Park, Moss Landing, Calif., USA.

2. Methods

Laboratory-scale (typically 4 or 8 g) admixture preparations were carried out using Radleys carousel reaction stations, fitted with 40 mL glass reaction vials, and reflux heads.

The performances of the admixtures with hydraulic cement compositions were assessed by forming and testing 3:1:1 (w/w) OPC-fly ash F-sand and 3:2 (w/w) fly ash C-sand mortars. Mortars were prepared in 0.5 or 1.0 kg batches. Cement components (OPC and fly ash F, or fly ash C alone) and sand were blended together at 139 rpm for 2 minutes, using a Gilson planetary mixer. Agitation was increased to 285 rpm, and a mixture of water and admixture added, and mixing continued for 2 minutes. Mixing was stopped, the sides of the mixing bowl scraped down, and mixing continued for 2 minutes.

Set time measurements were performed on fresh mortars using an ACME needle penetrometer. Mortar specimens were placed in 2×4 inch polypropylene cylinders, and measurements were performed at 292-294 K, 30-40% relative humidity.

Hardness measurements were performed on 2 inch mortar cubes with a Leica microhardness tester fitted with a Vickers pyramidal diamond head, loaded at 10, 50 and 100 N. Measurements were performed at 292-294 K, and 30-40% relative humidity. Mortars were cast in polypropylene cube molds, and cured at 292-294 K, 40-60% relative humidity, for 1 day.

Compressive strength tests were performed on 2 inch mortar cubes using an Instron instrument. Measurements were performed at 292-294 K, and 30-40% relative humidity. Mortars were cast in polypropylene cube molds, and cured at 292-294 K, 40-60% relative humidity, for 1 day, then at 292-294 K, 30-40% relative humidity, thereafter.

Linear shrinkage measurements were made on single or duplicate 4×12″ mortar bars, cast using 316 SS molds, cured at 292-294 K, 40-60% relative humidity, for 1, demolded and cured at 292-294 K, 40-60% relative humidity, for 1 day, then demolded and cured at 292-294 K, 40-60% relative humidity, thereafter.

Water permeability determinations were made using a Taywood instrument. Mortars were cast as 1×12″ bars, using 316 SS moulds, cured at 50% H, 295 K, 0-1d, then demolded, cured at 292-294 K, and 40-60% RH, for 28 days, then sawn and cored with diamond tools to furnish 1″ thick disks. Specimens were de-aerated under 20 mbar vacuum for 20 hours, then water-saturated under 2 bar water pressure 2 hours, and measurements performed at water pressures of 5 and 10 bar, at 292-294 K.

Freeze-thaw resistance was evaluated as per ASTM C-666, wet method, using an Olson instrument. Mortars were cast as 3×12″ bars, using 316 SS molds, cured at 292-294 K, 40-60% relative humidity, for 1 day, then demolded and cured at 292-294 K, 40-60% relative humidity, thereafter.

B. Preparations

The following examples illustrate the preparation of the aforementioned admixtures for use with hydraulic cement compositions.

In the following examples, the nominal formulas for the admixtures are provided, which are indicative only of the molar ratios of the reactants used in the preparations. As such, the formulas do not indicate the actual complexes present, but rather the overall chemical compositions. Furthermore, the admixtures are expected to contain mixtures of such complexes as described above, and as exemplified in Table 8.

For comparative purposes, cement compositions prepared with the admixtures of the present invention were compared with control compositions prepared with water alone, and with the commercial accelerating admixtures, SikaSet NC, SikaSet HE and Pozzutec 20+.

Admixtures C1-C11 were prepared as 40% w/w aqueous solutions or suspensions, using the α-hydroxycarboxylic acid, glycolic acid (Gly) as the ligand. Admixture C1 is sodium glycolate (Na₁(Gly)₁), admixture C2 is an aluminum glycolate complex (Al₁(Gly)₃), and admixtures 3-11 are sodium glycolatoaluminate(III) complexes (Na_(x)Al_(y)(Gly)_(z), where x is between 1 and 5, y is between 1 and 2, and z is between 1 and 6). The formulation and preparation of the admixtures is detailed in Table 9, with representative examples (admixtures C1, C2 and C3-C11) provided below as Examples 1-3. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 10 and 11 respectively. Mortars prepared with sodium glycolatoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water, sodium glycolate, or the commercial SikaSet or Pozzutec admixtures.

The results show that glycolatoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 1 Admixture C1. Sodium Glycolate: Na₁(Gly)₁

Sodium hydroxide (2.78 g) was dissolved with stirring (340 rpm) in water (9.6 g) maintained at 293 K, glycolic acid (7.57 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Example 2 Admixture C2. Aluminum(III) Glycolate: Al₁(Gly)₃

Aluminum(III) hydroxide (2.51 g) was suspended with stirring (340 rpm) in water (8.9 g) maintained at 343 K, glycolic acid (8.60 g) added over 1 minute, and stirring continued at 343 K for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Example 3 Admixture C3. Sodium Glycolatoaluminate(III): Na₁Al₁(Gly)₁

Sodium hydroxide (1.19 g) was dissolved with stirring (340 rpm) in water (9.9 g) maintained at 293 K, glycolic acid (3.23 g) added over 2 minutes, and stifling continued for 15 minutes. Aluminum(III) hydroxide (5.65 g) was then added, the temperature raised to 343 K, and stifling continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C4-C11 were similarly prepared using the method of Example 3.

TABLE 9 Preparation and Properties of Admixtures C1-C11 Admixtures Reactants (Mass in g) Reaction Product # Mol Composition NaOH Al(OH)₃ Gly Water pH Appearance C1 Na₁(Gly)₁ 2.78 — 7.57 9.6 11.8 Clear Solution C2 Al₁(Gly)₃ — 2.51 8.60 8.9 3.2 White Suspension C3 Na₁Al₁(Gly)₁ 1.19 5.65 3.23 9.9 8.8 White Suspension C4 Na₂Al₂(Gly)₃ 1.39 3.31 5.68 9.6 8.1 White Suspension C5 Na₃Al₂(Gly)₃ 1.92 3.05 5.23 9.8 10.7 White Suspension C6 Na₁Al₁(Gly)₂ 1.20 2.84 6.50 9.5 8.5 White Suspension C7 Na₃Al₂(Gly)₄ 1.67 2.65 6.05 9.6 11.1 White Suspension C8 Na₂Al₁(Gly)₃ 1.67 1.99 6.82 9.5 8.0 White Suspension C9 Na₃Al₁(Gly)₄ 1.93 1.53 6.99 9.5 7.8 White Suspension C10 Na₄Al₁(Gly)₄ 2.38 1.42 6.48 9.7 8.1 White Suspension C11 Na₅Al₁(Gly)₆ 2.20 1.05 7.18 9.6 8.2 White Suspension Notes. Reaction conditions are detailed in Examples 1-3; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Gly is glycolic acid; W is water.

TABLE 10 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C1-C11 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 dayP20 Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C1 0.41 6.0 2.46 205 63 10.2 29.3 C2 0.41 6.0 2.46 165 78 13.6 30.5 C3 0.41 6.0 2.46 95 128 19.1 44.6 C4 0.41 6.0 2.46 90 121 18.8 43.2 C5 0.41 6.0 2.46 70 123 19.6 44.7 C6 0.41 6.0 2.46 70 138 20.3 45.9 C7 0.41 6.0 2.46 65 151 21.5 43.8 C8 0.41 6.0 2.46 75 130 18.1 40.9 C9 0.41 6.0 2.46 58 137 19.2 38.5 C10 0.41 6.0 2.46 43 119 17.8 36.4 C11 0.41 6.0 2.46 36 123 17.3 37.0 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 11 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C1-C11 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C1 0.22 6.0 1.32 13 123 18.4 40.9 C2 0.22 6.0 1.32 46 107 15.0 35.2 C3 0.22 6.0 1.32 25 178 25.3 52.5 C4 0.22 6.0 1.32 23 188 26.7 54.7 C5 0.22 6.0 1.32 22 184 26.1 53.2 C6 0.22 6.0 1.32 28 179 25.3 53.3 C7 0.22 6.0 1.32 28 193 27.7 57.0 C8 0.22 6.0 1.32 32 201 28.6 59.2 C9 0.22 6.0 1.32 28 190 26.1 56.9 C10 0.22 6.0 1.32 34 181 24.8 53.5 C11 0.22 6.0 1.32 27 186 26.1 55.1 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C12-C20 were prepared as 40% w/w aqueous solutions or suspensions, using the α-hydroxycarboxylic acid acid, lactic acid (Lac) as the ligand. Admixture C12 is sodium lactate (Na₁(Lac)₁), admixture C13 is an aluminum lactate complex (Al₁(Lac)₃), and admixtures C14-C20 are sodium lactatoaluminate(III) complexes (Na_(x)Al_(y)(Lac)_(z), where x is between 1 and 5, y is between 1 and 2, and z is between 1 and 6). The formulation and preparation of the admixtures is detailed in Table 12, with representative examples (admixtures C12, C13 and C14-C20) provided below as Examples 4-6. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 13 and 14 respectively. Mortars prepared with sodium lactatoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water, sodium lactate, or the commercial SikaSet or Pozzutec admixtures.

The results show that lactatoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 4 Admixture C12. Sodium Lactate: Na₁(Lac)₁

Sodium hydroxide (2.48 g) was dissolved with stirring (340 rpm) in water (11.3 g) maintained at 293 K, lactic acid (6.22 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Example 5 Admixture C13. Aluminum(III) Lactate: Al₁(Lac)₃

Aluminum(III) hydroxide (2.21 g) was suspended with stirring (340 rpm) in water (10.8 g) maintained at 343 K, lactic acid (6.97 g) added over 1 minute, and stirring continued at 343 K for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Example 6 Admixtures C14. Sodium Lactatoaluminate(III): Na₁Al₁(Lac)₁

Sodium hydroxide (1.55 g) was dissolved with stirring (340 rpm) in water (10.9 g) maintained at 293 K, lactic acid (3.89 g) added over 2 minutes, and stifling continued for 15 minutes. Aluminum(III) hydroxide (3.69 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C15-C20 were similarly prepared using the method of Example 6.

TABLE 12 Preparation and Properties of Admixtures C12-C20 Admixture Reactants (Mass in g) Reaction Product # Mol Composition NaOH Al(OH)₃ Lac Water pH Appearance C12 Na₁(Lac)₁ 2.48 — 6.22 11.3 12.4 Clear Solution C13 Al₁(Lac)₃ — 2.21 6.97 10.8 3.5 White Suspension C14 Na₁Al₁(Lac)₁ 1.55 3.69 3.89 10.9 9.0 White Suspension C15 Na₁Al₁(Lac)₂ 1.08 2.58 5.43 10.9 8.6 Cloudy Solution C16 Na₂Al₁(Lac)₃ 1.51 1.79 5.67 11.0 8.9 Cloudy Solution C17 Na₂Al₂(Lac)₃ 1.28 3.04 4.79 10.9 7.8 Cloudy Solution C18 Na₃Al₂(Lac)₃ 1.78 2.81 4.44 11.0 10.4 Cloudy Solution C19 Na₃Al₂(Lac)₄ 1.52 2.42 5.08 11.0 9.2 White Suspension C20 Na₅Al₂(Lac)₆ 1.80 1.71 5.41 11.1 9.1 White Suspension Notes. Reaction conditions are detailed in Examples 1-3; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Lac is lactic acid; W is water.

TABLE 13 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C12-C20 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C12 0.41 6.0 2.46 185 65 11.8 28.6 C13 0.41 6.0 2.46 135 69 10.2 28.8 C14 0.41 6.0 2.46 80 132 19.3 47.4 C15 0.41 6.0 2.46 75 136 21.4 53.1 C16 0.41 6.0 2.46 65 137 23.7 55.8 C17 0.41 6.0 2.46 85 155 21.3 56.5 C18 0.41 6.0 2.46 57 162 26.5 53.9 C19 0.41 6.0 2.46 52 154 21.4 49.8 C20 0.41 6.0 2.46 47 138 18.1 47.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 14 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C12-C20 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C12 0.22 6.0 1.32 15 128 18.3 42.2 C13 0.22 6.0 1.32 53 107 14.6 29.4 C14 0.22 6.0 1.32 24 183 25.2 55.1 C15 0.22 6.0 1.32 26 196 26.7 58.1 C16 0.22 6.0 1.32 30 206 29.3 58.7 C17 0.22 6.0 1.32 22 205 29.8 57.2 C18 0.22 6.0 1.32 21 191 29.8 61.1 C19 0.22 6.0 1.32 24 181 25.4 57.0 C20 0.22 6.0 1.32 27 188 28.3 56.3 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C21-C27 were prepared as 40% w/w aqueous solutions or suspensions, using the α-hydroxydicarboxylic acid acid, malic acid (Mal) as the ligand. Admixture C21 is sodium malate (Na₂(Mal)₁), admixture C22 is an aluminum malate complex (Al₂(Mal)₃), and admixtures C23-C27 are sodium malatoaluminate(III) complexes (Na_(x)Al_(y)(Mal)_(z), where x is between 1 and 4, y is between 1 and 2, and z is between 1 and 3). The formulation and preparation of the admixtures is detailed in Table 15, with representative examples (admixtures C21, C22 and C23) provided below as Examples 7-9. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 16 and 17 respectively. Mortars prepared with sodium malatoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water, sodium malate, or the commercial SikaSet or Pozzutec admixtures.

The results show that malatoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 4 Admixture C21. Sodium Malate: Na₂(Mal)₁

Sodium hydroxide (3.01 g) was dissolved with stirring (340 rpm) in water (11.9 g) maintained at 293 K, lactic acid (5.06 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Example 8 Admixture C22. Aluminum(III) Malate: Al₂(Mal)₃

Aluminum(III) hydroxide (2.75 g) was suspended with stirring (340 rpm) in water (11.4 g) maintained at 343 K, malic acid (5.82 g) added over 1 minute, and stirring continued at 343 K for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Example 9 Admixture C23. Sodium Malatoaluminate(III): Na₁Al₁(Mal)₁

Sodium hydroxide (1.28 g) was dissolved with stirring (340 rpm) in water (11.4 g) maintained at 293 K, malic acid (4.30 g) added over 2 minutes, and stifling continued for 15 minutes. Aluminum(III) hydroxide (3.05 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C24-C27 were similarly prepared using the method of Example 9.

TABLE 15 Preparation and Properties of Admixtures C21-C27 Admixture Reactants (Mass in g) Reaction Product # Mol Composition NaOH Al(OH)₃ Mal Water pH Appearance C21 Na₂(Mal)₁ 3.02 — 5.06 11.9 12.8 Clear Solution C22 Al₂(Mal)₃ — 2.75 5.82 11.4 3.4 White Suspension C23 Na₁Al₁(Mal)₁ 1.28 3.05 4.30 11.4 7.2 Clear Solution C24 Na₁Al₁(Mal)₁ 2.21 2.63 3.71 11.4 10.9 Cloudy Solution C25 Na₂Al₂(Mal)₁ 1.75 4.15 2.93 11.2 8.4 White Suspension C26 Na₃Al₂(Mal)₂ 1.78 2.82 3.98 11.4 8.6 White Suspension C27 Na₄Al₂(Mal)₃ 1.80 2.14 4.53 11.5 9.1 White Suspension Notes. Reaction conditions are detailed in Examples 1-3; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; MalH is malic acid; W is water.

TABLE 16 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C21-C27 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C21 0.41 6.0 2.46 160 68 11.7 33.0 C22 0.41 6.0 2.46 150 64 9.6 26.1 C23 0.41 6.0 2.46 95 151 19.8 53.4 C24 0.41 6.0 2.46 80 143 16.2 51.4 C25 0.41 6.0 2.46 80 136 15.8 47.6 C26 0.41 6.0 2.46 65 138 17.7 50.8 C27 0.41 6.0 2.46 51 140 17.2 43.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 17 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C21-C27 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C21 0.22 6.0 1.32 16 135 19.4 43.2 C22 0.22 6.0 1.32 105 149 19.6 42.6 C23 0.22 6.0 1.32 28 198 29.2 61.7 C24 0.22 6.0 1.32 16 175 24.1 53.8 C25 0.22 6.0 1.32 34 164 24.0 50.4 C26 0.22 6.0 1.32 28 181 26.8 56.9 C27 0.22 6.0 1.32 42 139 19.0 40.4 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C28-C37 were prepared as 40% w/w aqueous solutions or suspensions, using the α-hydroxytricarboxylic acid, citric acid (Cit) as the ligand. Admixture C28 is sodium citrate (Na₃(Cit)₁), admixtures C29 and C30 are aluminum citrate complexes (Al₁(Cit)₁ and Al₄(Cit)₁), and admixtures C31-C37 are sodium citratoaluminate(III) complexes (Na_(x)Al_(y)(Cit)₁, where x is between 1 and 3, and y is between 1 and 4). The formulation and preparation of the admixtures is detailed in Table 18, with representative examples (admixtures C28, C29 and C31) provided below as Examples 10-12. The testing of the admixtures for Portland cement-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 19 and 20 respectively. Mortars prepared with sodium citratoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water, sodium citrate, or the commercial SikaSet or Pozzutec admixtures.

The results show that citratoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 10 Admixture C28. Sodium Citrate: Na₃(Cit)₁

Sodium hydroxide (3.11 g) was dissolved with stirring (340 rpm) in water (11.9 g) maintained at 293 K, citric acid (4.97 g) added over 1 minute, and stifling continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Example 11 Admixture C29. Aluminum(III) Citrate: Al₁(Cit)₁

Aluminum(III) hydroxide (2.85 g) was suspended with stirring (340 rpm) in water (11.4 g) maintained at 343 K, citric acid (5.75 g) added over 1 minute, and stifling continued at 343 K for 70 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixture C30 was similarly prepared using the method of Example 11.

Example 12 Admixture C31. Sodium Citratoaluminate(III): Na₁Al₁(Cit)₁

Sodium hydroxide (1.04 g) was dissolved with stirring (340 rpm) in water (11.5 g) maintained at 293 K, citric acid (5.01 g) added over 2 minutes, and stirring continued for 15 minutes. Aluminum(III) hydroxide (2.48 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C32-C37 were similarly prepared using the method of Example 12.

TABLE 18 Preparation and Properties of Admixtures C28-C37 Admixture Reactants (Mass in g) Reaction Product # Mol Composition NaOH Al(OH)₃ Cit Water pH Appearance C28 Na₃(Cit)₁ 3.11 — 4.97 11.9 9.5 Clear Solution C29 Al₁(Cit)₁ — 2.85 5.75 11.4 2.2 Clear Solution C30 Al₄(Cit)₁ — 6.10 3.08 10.8 6.0 White Suspension C31 Na₁Al₁(Cit)₁ 1.04 2.48 5.01 11.5 2.5 Clear Solution C32 Na₂Al₁(Cit)₁ 1.85 2.20 4.43 11.5 8.6 Clear Solution C33 Na₃Al₁(Cit)₁ 2.49 1.97 3.98 11.6 10.2 Cloudy Gel C34 Na₂Al₂(Cit)₁ 1.51 3.59 3.63 11.3 8.7 White Suspension C35 Na₃Al₂(Cit)₁ 2.07 3.28 3.32 11.3 10.0 Cloudy Gel C36 Na₁Al₄(Cit)₁ 0.59 5.65 2.85 10.9 6.8 White Suspension C37 Na₂Al₄(Cit)₁ 1.11 5.26 2.66 11.0 8.8 White Suspension Notes: Reaction conditions are detailed in Examples 10-12; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Cit is citric acid; W is water.

TABLE 19 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C28-C37 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C28 0.41 6.0 2.46 185 61 10.5 27.6 C29 0.41 6.0 2.46 175 63 11.3 31.5 C30 0.41 6.0 2.46 160 58 9.9 23.2 C31 0.41 6.0 2.46 145 129 18.1 43.9 C32 0.41 6.0 2.46 140 155 21.6 52.4 C33 0.41 6.0 2.46 125 146 20.6 49.3 C34 0.41 6.0 2.46 130 144 18.1 40.5 C35 0.41 6.0 2.46 105 137 18.4 44.7 C36 0.41 6.0 2.46 125 133 16.2 35.1 C37 0.41 6.0 2.46 115 124 17.4 37.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 20 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C28-C37 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C28 0.22 6.0 1.32 19 121 15.4 34.9 C29 0.22 6.0 1.32 110 117 14.9 31.6 C30 0.22 6.0 1.32 54 124 17.1 37.9 C31 0.22 6.0 1.32 38 130 17.8 41.6 C32 0.22 6.0 1.32 44 156 21.5 56.1 C33 0.22 6.0 1.32 55 201 28.7 58.9 C34 0.22 6.0 1.32 28 198 26.8 57.9 C35 0.22 6.0 1.32 25 165 24.7 53.9 C36 0.22 6.0 1.32 58 141 18.4 42.9 C37 0.22 6.0 1.32 64 124 19.6 40.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C38-052 were prepared as 40% w/w aqueous solutions or suspensions, using a variety of other hydroxycarboxylic acids, namely the α-hydroxycarboxylic acid, 2-hydroxybutyric acid (2HBt), the β-hydroxycarboxylic acid, 3-hydroxybutyric acid (3HBt), the α-hydroxydicarboxylic acid, citramalic acid (Cml), the α,α′-dihydroxydicarboxylic acid, tartaric acid (Tar), and the α,α′,β,β′-tetrahydroxydicarboxylic acid, mucic acid (Muc).

Admixture C38 is sodium 2-hydroxybutyrate (Na₁(2HBt)₁), and admixtures C39 and C40 are sodium 2-hydroxybutyratoaluminate(III) complexes (Na₁Al₁(2HBt)_(x), where x is 1 or 2). Admixture C41 is sodium 3-hydroxybutyrate (Na₁(3HBt)₁), and admixtures C42 and C43 are sodium 3-hydroxybutyratoaluminate(III) complexes (Na₁Al₁(2HBt)_(x), where x is 1 or 2). Admixture C44 is sodium citramalate (Na₂(Cml)₁), and admixtures C45 and C46 are sodium citramalatoaluminate(III) complexes (Na_(x)Al₁(Cml)_(x), where x is 1 or 2). Admixture C47 is sodium tartarate (Na₂(Tar)₁), and admixtures C48 and C49 are sodium tartaratoaluminate(III) complexes (Na_(x)Al_(y)(Tar)_(y), where x is 1 or 3, and y is 1 or 2). Admixture C50 is sodium mucate (Na₂(Muc)₁), and admixtures C51 and C52 are sodium mucatoaluminate(III) complexes (Na_(x)Al_(y)(Muc)_(y), where x is 1 or 3, and y is 1 or 2). The formulation and preparation of the admixtures is detailed in Table 21, with representative examples (admixtures C38 and C39) provided below as Examples 13 and 14. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 22 and 23 respectively.

Mortars prepared with 2-hydroxybutyratoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water, sodium 2-hydroxybutyrate, or the SikaSet or Pozzutec admixtures. A similar trend was seen with the 3-hydroxybutyrate admixtures. Also, mortars prepared with the 2-hydroxybutyratoaluminate(III) admixtures had significantly higher hardness and compressive strengths than those prepared with the corresponding 3-hydroxybutyratoaluminate(III) admixtures, perhaps due to the increased distance of the hydroxyl group from the carboxyl function.

Mortars prepared with the citramalatoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water, sodium citramalate, or the commercial SikaSet or Pozzutec admixtures. Mortars prepared with the sodium tartaratoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water or sodium tartarate, and performed similarly to those prepared with the SikaSet and Pozzutec admixtures. A similar trend was seen with the mucate admixtures. Mortars prepared with tartaratoaluminate(III) or mucatoaluminate(III) admixtures showed lower hardness and compressive strengths than those prepared with the other hydroxycarboxylate admixtures, perhaps due to the presence of multiple hydroxyl groups.

The results show that hydroxycarboxylatoaluminate(III) complexes derived from a variety of aliphatic α- and β-hydroxycarboxylic acids are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 13 Admixture C38. Sodium 2-Hydroxybutyrate: Na₁(2HBt)₁

Sodium hydroxide (2.24 g) was dissolved with stirring (340 rpm) in water (11.8 g) maintained at 293 K, 2-hydroxybutyric acid (5.96 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C41, C44, C47 and C50 were similarly prepared using the method of Example 13, and employing 3-hydroxybutyric acid, citramalic acid, tartaric acid or mucic acid instead of 2-hydroxybutyric acid.

Example 14 Admixture C39. Sodium 2-Hydroxybutyratoaluminate(III): Na₁Al₁(2HBut)₁

Sodium hydroxide (1.46 g) was dissolved with stirring (340 rpm) in water (11.2 g) maintained at 293 K, 2-hydroxybutyric acid (3.87 g) added over 2 minutes, and stirring continued for 15 minutes. Aluminum(III) hydroxide (3.46 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A cloudy solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C40, and C42, C43, C45, C46, C48, C49, C51 and C52 were similarly prepared using the method of Example 14, the latter admixtures employing 3-hydroxybutyric acid, citramalic acid, tartaric acid or mucic acid instead of 2-hydroxybutyric acid.

TABLE 21 Preparation and Properties of Admixtures C38-C52 Admixture Reactants (Mass in g) Reaction Product # Mol Composition NaOH Al(OH)₃ Water pH Appearance 2HBt C38 Na₁(2HBt)₁ 2.24 — 5.96 11.8 12.5 Clear Solution C39 Na₁Al₁(2HBt)₁ 1.46 3.46 3.87 11.2 9.2 Cloudy Solution C40 Na₁Al₁(2HBt)₂ 0.99 2.36 5.26 11.4 8.8 Cloudy Solution 3HBt C41 Na₁(3HBt)₁ 2.24 — 5.90 11.9 12.3 Clear Solution C42 Na₁Al₁(3HBt)₁ 1.46 3.46 3.83 11.3 9.0 Cloudy Solution C43 Na₁Al₁(3HBt)₂ 0.99 2.36 5.21 11.4 8.3 Cloudy Solution Cml C44 Na₂(Cml)₁ 2.83 — 5.25 11.9 12.6 Clear Solution C45 Na₁Al₁(Cml)₁ 1.21 2.89 4.50 11.4 7.6 Cloudy Solution C46 Na₂Al₁(Cml)₂ 1.42 1.69 5.27 11.6 11.2 Cloudy Solution Tar C47 Na₂(Tar)₁ 2.81 — 5.27 11.9 12.7 Clear Solution C48 Na₁Al₁(Tar)₁ 1.21 2.87 4.52 11.4 7.8 Cloudy Solution C49 Na₃Al₂(Tar)₂ 1.68 2.67 4.21 11.4 7.2 Cloudy Solution Muc C50 Na₂(Muc)₁ 2.23 — 5.85 11.9 13.3 White Suspension C51 Na₁Al₁(Muc)₁ 0.99 2.34 5.17 11.5 5.4 White Suspension C52 Na₃Al₂(Muc)₂ 1.39 2.21 4.88 11.5 8.1 White Suspension Notes: Reaction conditions are detailed in Examples 13 and 14; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; 2HBt is 2-hydroxybutyric acid; 3HBt is 3-hydroxybutyric acid; Cml is citramalic acid; Tar is tartaric acid; Muc is mucic acid; W is water.

TABLE 22 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C38-C52 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C38 0.41 6.0 2.46 155 59 9.7 22.8 C39 0.41 6.0 2.46 70 124 18.5 41.2 C40 0.41 6.0 2.46 55 129 20.3 43.7 C41 0.41 6.0 2.46 180 53 9.4 20.9 C42 0.41 6.0 2.46 85 121 17.3 37.5 C43 0.41 6.0 2.46 70 117 17.8 35.8 C44 0.41 6.0 2.46 145 65 10.8 23.5 C45 0.41 6.0 2.46 80 147 18.0 39.9 C46 0.41 6.0 2.46 57 141 17.3 37.3 C47 0.41 6.0 2.46 260 37 7.1 13.2 C48 0.41 6.0 2.46 230 92 15.3 27.8 C49 0.41 6.0 2.46 215 88 14.5 29.6 C50 0.41 6.0 2.46 210 34 6.3 11.4 C51 0.41 6.0 2.46 190 82 13.4 29.1 C52 0.41 6.0 2.46 145 88 14.1 32.7 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 23 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C38-C52 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C38 0.22 6.0 1.32 21 117 18.8 38.4 C39 0.22 6.0 1.32 27 175 26.2 53.1 C40 0.22 6.0 1.32 24 182 28.0 55.6 C41 0.22 6.0 1.32 29 109 17.2 33.2 C42 0.22 6.0 1.32 31 163 24.7 50.9 C43 0.22 6.0 1.32 26 165 24.1 47.4 C44 0.22 6.0 1.32 13 133 18.6 37.1 C45 0.22 6.0 1.32 24 152 23.7 50.2 C46 0.22 6.0 1.32 22 156 24.5 53.7 C47 0.22 6.0 1.32 21 76 10.3 23.8 C48 0.22 6.0 1.32 17 102 16.0 30.4 C49 0.22 6.0 1.32 15 110 16.8 32.7 C50 0.22 6.0 1.32 57 70 9.7 21.9 C51 0.22 6.0 1.32 80 97 14.5 29.4 C52 0.22 6.0 1.32 70 123 16.5 31.6 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C53-C60 were prepared as 20% w/w aqueous solutions or suspensions, using a variety of cycloaliphatic and aromatic hydroxycarboxylic acids, namely the hydroxylated benzoic acid, 2,3-dihydroxybenzoic acid (Dhb), the hydroxylated cinnamic acid, caffeic acid (Caf), and the quinic acid-caffeic acid conjugate, chlorogenic acid (Chl).

Admixture C53 is sodium 2,3-dihydroxybenzoate (Na₁(Dhb)₁), and admixture C54 is the sodium 2,3-dihydroxybenzoatoaluminate(III) complex (Na₂Al₁(Dhb)₂). Admixture C55 is sodium caffeate (Na₁(Caf)₁), and admixtures C56 and C57 are sodium caffeatoaluminate(III) complexes (Na_(x)Al₁(Caf)_(y), where x is 3 or 5, and y is 2 or 3). Admixture C58 is sodium chlorogenate (Na₁(Chl)₁), and admixtures C59 and C60 are sodium chlorogenatoaluminate(III) complexes (Na_(x)Al₁(Chl)_(y), where x is 3 or 5, and y is 2 or 3). The formulation and preparation of the admixtures is detailed in Table 24, with representative examples (admixtures C53 and C54) provided below as Examples 16 and 17. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 25 and 26 respectively.

Mortars prepared with 2,3-dihydroxybenzoatoaluminate(III) admixtures achieved substantially greater hardness and compressive strength than those prepared with water, sodium 2,3-dihydroxybenzoate, or the commercial SikaSet or Pozzutec admixtures. A similar trend was seen with the caffeatoaluminate(III) and chlorogenatoaluminate(III) admixtures.

These results show that a hydroxycarboxylatoaluminate(III) complexes formed from a variety of aromatic hydroxycarboxylic acids are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 15 Admixture C53. Sodium 2,3-Dihydroxybenzoate: Na₁(Dhb)₁

Sodium hydroxide (0.83 g) was dissolved with stirring (340 rpm) in water (16.0 g) maintained at 293 K, 2,3-dihydroxybenzoic acid (3.21 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A brown solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C55 and C58 were similarly prepared using the method of Example 15, and employing caffeic acid or chlorogenic acid instead of 2,3-dihydroxybenzoic acid.

Example 16 Admixture C54. Sodium 2,3-Dihydroxybenzoatoaluminate(III): Na₂Al₁(Dhb)₂

Sodium hydroxide (0.69 g) was dissolved with stirring (340 rpm) in water (15.8 g) maintained at 293 K, 2,3-dihydroxybenzoic acid (2.67 g) added over 2 minutes, and stifling continued for 15 minutes. Aluminum hydroxide(III) (0.82 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A brown solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C56, C57, C59 and C60 were similarly prepared using the method of Example 16, and employing caffeic acid or chlorogenic acid instead of 2,3-dihydroxybenzoic acid.

TABLE 24 Preparation and Properties of Admixtures C53-C60 Admixture Reactants (Mass in g) Reaction Products # Mol Composition NaOH Al(OH)₃ Water pH Appearance Dhb C53 Na₁(Dhb)₁ 0.83 — 3.21 16.0 7.9 Brown Solution C54 Na₂Al₁(Dhb)₂ 0.69 0.82 2.67 15.8 8.6 Brown Solution Caf C55 Na₁(Caf)₁ 0.73 — 3.34 15.9 12.2 Brown Solution C56 Na₃Al₁(Caf)₂ 0.87 0.69 2.63 15.8 7.2 Brown Suspension C57 Na₅Al₁(Caf)₃ 0.99 0.47 2.70 15.8 9.3 Brown Suspension Chl C58 Na₁(Chl)₁ 0.41 — 3.78 15.8 11.9 Yellow Solution C59 Na₃Al₁(Chl)₂ 0.53 0.42 3.29 15.8 7.3 Yellow Suspension C60 Na₅Al₁(Chl)₃ 0.60 0.29 3.34 15.8 9.0 Yellow Suspension Notes: Reaction conditions are detailed in Examples 15 and 16; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Dhb is 2,3-dihydroxybenzoic acid; Caf is caffeic acid; Chl is chlorogenic acid; W is water.

TABLE 25 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C53-C60 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C53 0.41 6.0 2.46 155 62 9.6 22.5 C54 0.41 6.0 2.46 90 123 17.9 36.2 C55 0.41 6.0 2.46 210 62 9.8 22.7 C56 0.41 6.0 2.46 150 152 18.4 38.5 C57 0.41 6.0 2.46 125 157 18.7 39.4 C58 0.41 6.0 2.46 190 57 9.6 22.1 C59 0.41 6.0 2.46 165 144 17.8 34.9 C60 0.41 6.0 2.46 140 153 18.8 39.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 26 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C53-C60 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C53 0.22 6.0 1.32 22 127 18.3 39.4 C54 0.22 6.0 1.32 18 155 22.9 46.0 C55 0.22 6.0 1.32 46 118 18.0 35.6 C56 0.22 6.0 1.32 33 151 23.9 46.1 C57 0.22 6.0 1.32 31 153 24.3 48.7 C58 0.22 6.0 1.32 65 109 16.3 35.6 C59 0.22 6.0 1.32 47 147 21.7 44.5 C60 0.22 6.0 1.32 32 138 20.8 42.0 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C61-C65 were prepared as 40% w/w aqueous solutions, based upon the sodium malatoaluminate(III) complex, Na₁Al₁(Mal)₁ (Admixture C23), but were prepared using aluminum compounds other than aluminum(III) hydroxide as precursors. Thus, aluminum(III) oxide, sodium aluminate(III), aluminum(III) chloride hexahydrate, dialuminum(III) chloride pentahydroxide, and aluminum(III) sulfate hexadecahydrate were used to prepare admixtures C61-C65 respectively. The formulation and preparation of the admixtures is detailed in Table 27, with representative examples (admixtures C61-C63) provided below as Examples 17-19. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 28 and 29 respectively.

Mortars prepared with admixtures C61 and C62 behaved similarly to those prepared with admixture 23, while those prepared with admixtures C63-C65 were somewhat inferior in terms of hardness and compressive strength development. The latter result may be due to the presence of sodium chloride and sodium sulfate salts in admixtures C63-C65.

The results show that hydroxycarboxylatoaluminate(III) complexes prepared from a variety of aluminum-containing precursors are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 17 Admixture C61. Sodium Malatoaluminate(III): Na₁Al₁(Mal)₁

Sodium hydroxide (1.44 g) was dissolved with stirring (340 rpm) in water (6.9 g) maintained at 293 K. The temperature was then raised to 363 K, aluminum(III) oxide (1.83 g) added, stifling continued at 363 K for 70 h, and the temperature decreased to 343 K. Malic acid (4.81 g) dissolved in water (5.0 g) was then added over 5 minutes, and stifling continued at 343 K for 70 h. A cloudy solution was obtained, and this was diluted to 6% w/w solids for testing.

Example 18 Admixture C62. Sodium Malatoaluminate(III): Na₁Al₁(Mal)₁

Sodium aluminate(III) (3.38 g) was dissolved with stifling (340 rpm) in water (6.9 g) maintained at 293 K, the temperature raised to 343 K, and stirring continued for 15 minutes. Malic acid (4.73 g) dissolved in water (5.0 g) was then added over 5 minutes, and stirring continued at 343 K for 70 hours. A cloudy solution was obtained, and this was diluted to 6% w/w solids for testing.

Example 19 Admixture C63. Sodium Malatoaluminate(III): Na₁Al₁(Mal)₁

Sodium hydroxide (3.03 g) was dissolved with stirring (340 rpm) in water (5.8 g) maintained at 293 K, malic acid (2.54 g) added over 2 minutes, and stirring continued at 293 K for 15 minutes, Aluminum(III) chloride hexahydrate (4.63 g) dissolved in water (4.0 g) hydroxide (0.82 g) was then added, the temperature raised to 343 K, and stifling continued for 70 hours. A cloudy solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C64 and C65 were similarly prepared using the method of Example 19, and employing dialuminum(III) chloride pentahydroxide or aluminum(III) sulfate hexadecahydrate instead of aluminum(III) chloride hexahydrate.

TABLE 27 Preparation and Properties of Admixtures C61-C65 Admixture Reactants (Mass in g) Reaction Product # Mol Composition NaOH Mal Water pH Appearance Al₂O₃ 61 Na₁Al₁(Mal)₁ 1.44 1.83 4.81 11.9 7.4 Cloudy Solution Na₁₅Al₁₁O₂₄ C62 Na₂₇Al₂₂(Mal)₂₀ — 3.38 4.73 11.9 8.5 Cloudy Solution AlCl₃•6W C63 Na₁Al₁(Mal)₁ 3.03 4.63 2.54 9.8 7.4 Cloudy Solution Al₂Cl(OH)₅ C64 Na₁Al₁(Mal)₁ 2.15 4.88 3.60 9.4 7.8 Cloudy Solution Al₂(SO₄)₃•16W C65 Na₁Al₁(Mal)₁ 2.78 5.74 2.33 9.2 7.5 Cloudy Solution Notes: Reaction conditions are detailed in Examples 17-19; NaOH is sodium hydroxide; Al₂O₃ is aluminum(III) oxide; Na₁₅Al₁₁O₂₄ is sodium aluminate(III); AlCl₃•6W is aluminum(III) chloride hexahydrate; Al₂Cl(OH)₅ is dialuminum(III) chloride pentahydroxide; Al₂(SO₄)₃•16W is aluminum(III) sulfate hexadecahydrate; Mal is malic acid; W is water.

TABLE 28 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C61-C65 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C61 0.41 6.0 2.46 140 158 22.9 50.9 C62 0.41 6.0 2.46 130 145 21.4 49.2 C63 0.41 6.0 2.46 85 137 18.8 43.6 C64 0.41 6.0 2.46 100 147 22.0 46.3 C65 0.41 6.0 2.46 75 144 20.7 45.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 29 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C61-C65 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C61 6.0 1.32 32 183 27.2 61.4 6.0 C62 6.0 1.32 27 170 25.7 58.2 6.0 C63 6.0 1.32 24 165 22.8 51.5 6.0 C64 6.0 1.32 28 173 24.1 53.6 6.0 C65 6.0 1.32 21 156 22.0 52.2 6.0 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C66-C78 were prepared as 40% w/w aqueous solutions or suspensions, using lithium instead of sodium, and the α-hydroxycarboxylic acids, glycolic acid, lactic acid, malic acid and citric acid as ligands. Admixture C66 is lithium glycolate (Li₁(Gly)₁), and admixtures C67 and C68 are lithium glycolatoaluminate(III) complexes (Li_(x)Al_(x)(Gly)_(y), where x is 1 or 2, and y is 2 or 3). Admixture C69 is lithium lactate (Li₁(Lac)₁), and admixtures C70 and C71 are lithium lactatoaluminate(III) complexes (Li₁Al₁(Lac)_(x), where x is 1 or 2). Admixture C72 is lithium malate (Li₂(Mal)₁), and admixtures C73-C75 are lithium malatoaluminate(III) complexes (Li_(x)Al_(y)(Mal)_(i), where x is 1-3, and y is 1 or 2). Admixture C76 is lithium citrate (Li₃(Cit)₁), and admixtures C77 and C78 are lithium citratoaluminate(III) complexes (Li_(x)Al₁(Cit)_(y), where x is 2 or 5, and y is 1 or 2). The formulation and preparation of the admixtures is detailed in Table 30, with representative examples (admixtures C66 and C67) provided below as Examples 20 and 21. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 31 and 32 respectively.

Admixtures C66-C78 behaved in a broadly similar manner to the corresponding sodium-containing admixtures (detailed in Tables 9-20), although they showed slower hardness and compressive strength development. Mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water, lithium α-hydroxycarboxylate, or the commercial SikaSet or Pozzutec admixtures.

These results show that lithium α-hydroxycarboxylatoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 20 Admixture C66. Lithium Glycolate: Li₁(Gly)₁

Lithium hydroxide (1.94 g) was dissolved with stirring (340 rpm) in water (9.3 g) maintained at 293 K, glycolic acid (8.78 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C69, C72 and C76 were similarly prepared using the method of Example 20, and employing lactic acid, malic acid or citric acid instead of glycolic acid.

Example 21 Admixture C67. Lithium Glycolatoaluminate(III): Li₁Al₁(Gly)₁

Lithium hydroxide (1.09 g) was dissolved with stifling (340 rpm) in water (9.7 g) maintained at 293 K, glycolic acid (4.93 g) added over 2 minutes, and stifling continued for 15 minutes. Aluminum(III) hydroxide (4.32 g) was then added, the temperature raised to 343 K, and stifling continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C68, and C70, C71, C73-C75, C77 and C78 were similarly prepared using the method of Example 21, the latter admixtures employing lactic acid, malic acid or citric acid instead of glycolic acid.

TABLE 30 Preparation and Properties of Admixtures C66-C78 Admixture Reactants (Mass in g) Reaction Product # Mol Composition LiOH Al(OH)₃ Water pH Appearance Gly C66 Li₁(Gly)₁ 1.94 — 8.78 9.3 11.4 Clear Solution C67 Li₁Al₁(Gly)₁ 1.09 4.32 4.93 9.7 8.2 White Suspension C68 Li₂Al₂(Gly)₃ 0.90 3.56 6.10 9.5 8.0 White Suspension Lac C69 Li₁(Lac)₁ 1.70 — 7.09 11.2 12.1 Clear Solution C70 Li₁Al₁(Lac)₁ 1.01 4.00 4.21 10.8 9.1 White Suspension C71 Li₁Al₁(Lac)₂ 0.69 2.72 5.73 10.9 8.4 Cloudy Solution Mal C72 Li₂(Mal)₁ 2.13 — 5.95 11.9 12.4 Clear Solution C73 Li₁Al₁(Mal)₁ 0.82 3.26 4.59 11.3 7.4 White Suspension C74 Li₂Al₁(Mal)₁ 1.49 2.96 4.17 11.4 10.6 White Suspension C75 Li₃Al₂(Mal)₁ 1.61 4.25 2.99 11.2 7.4 White Suspension Cit C76 Li₃(Cit)₁ 2.20 — 5.88 11.9 6.1 Clear Solution C77 Li₂Al₁(Cit)₁ 1.22 2.42 4.88 11.5 7.2 Cloudy Gel C78 Li₅Al₁(Cit)₂ 1.67 1.32 5.33 11.7 7.8 Cloudy Gel Notes: Reaction conditions are detailed in Examples 20 and 21; LiOH is lithium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Gly is glycolic acid; Lac is lactic acid; Mal is malic acid; Cit is citric acid; W is water.

TABLE 31 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C66-C78 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C66 0.41 6.0 2.46 220 51 8.8 20.7 C67 0.41 6.0 2.46 125 85 13.7 34.8 C68 0.41 6.0 2.46 140 81 12.8 31.5 C69 0.41 6.0 2.46 235 56 9.3 18.5 C70 0.41 6.0 2.46 110 112 16.4 36.9 C71 0.41 6.0 2.46 85 123 18.1 40.3 C72 0.41 6.0 2.46 230 53 9.9 20.3 C73 0.41 6.0 2.46 90 116 17.2 39.1 C74 0.41 6.0 2.46 95 124 19.5 43.8 C75 0.41 6.0 2.46 110 108 18.0 38.3 C76 0.41 6.0 0.80 190 49 8.1 18.4 C77 0.41 6.0 0.80 95 119 19.8 37.8 C78 0.41 6.0 0.80 115 107 17.2 34.4 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 32 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C66-C78 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C66 0.22 6.0 1.32 25 128 16.8 33.8 C67 0.22 6.0 1.32 25 157 23.2 57.3 C68 0.22 6.0 1.32 23 173 23.5 55.3 C69 0.22 6.0 1.32 15 130 18.3 42.3 C70 0.22 6.0 1.32 24 176 25.2 55.1 C71 0.22 6.0 1.32 26 192 26.7 58.1 C72 0.22 6.0 1.32 14 120 17.5 36.6 C73 0.22 6.0 1.32 22 188 25.9 53.9 C74 0.22 6.0 1.32 18 172 24.2 47.7 C75 0.22 6.0 1.32 18 149 22.9 43.5 C76 0.22 6.0 0.80 15 124 17.6 38.9 C77 0.22 6.0 0.80 31 153 22.0 49.2 C78 0.22 6.0 0.80 28 173 22.8 53.4 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C79-C91 were prepared as 40% w/w aqueous solutions or suspensions, using potassium instead of sodium, and the α-hydroxycarboxylic acids, glycolic acid, lactic acid, malic acid and citric acid as ligands. Admixture C79 is potassium glycolate (K₁(Gly)₁), and admixtures C80 and C81 are potassium glycolatoaluminate(III) complexes (K_(x)Al_(x)(Gly)_(y), where x is 1 or 2, and y is 2 or 3). Admixture C82 is potassium lactate (K₁(Lac)₁), and admixtures C83 and C84 are potassium lactatoaluminate(III) complexes (K₁Al₁(Lac)_(x), where x is 1 or 2). Admixture C85 is potassium malate (K₂(Mal)₁), and admixtures C86-C88 are potassium malatoaluminate(III) complexes (K_(x)Al_(y)(Mal)_(i), where x is 1-3, and y is 1 or 2). Admixture C89 is potassium citrate (K₃(Cit)₁), and admixtures C90 and C91 are potassium citratoaluminate(III) complexes (K_(x)Al₁(Cit)_(y), where x is 2 or 5, and y is 1 or 2). The formulation and preparation of the admixtures is detailed in Table 33, with representative examples (admixtures C79 and C80) provided below as Examples 22 and 23. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 34 and 35 respectively.

Admixtures C79-C91 behaved in a broadly similar manner to the corresponding sodium- and lithium-containing admixtures (detailed in Tables 9-20, and Tables 30-32 respectively), although they showed slower hardness and compressive strength development. Mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water, potassium α-hydroxycarboxylate, or the commercial SikaSet or Pozzutec admixtures.

These results show that potassium α-hydroxycarboxylatoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 22 Admixture C79. Potassium Glycolate: K₁(Gly)₁

Potassium hydroxide (3.43 g) was dissolved with stirring (340 rpm) in water (9.9 g) maintained at 293 K, glycolic acid (6.65 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C82, C85 and C89 were similarly prepared using the method of Example 22, and employing lactic acid, malic acid or citric acid instead of glycolic acid.

Example 23 Admixture C80. Potassium Glycolatoaluminate(III): K₁Al₁(Gly)₁

Potassium hydroxide (2.15 g) was dissolved with stirring (340 rpm) in water (10.0 g) maintained at 293 K, glycolic acid (4.18 g) added over 2 minutes, and stifling continued for 15 minutes. Aluminum(III) hydroxide (3.66 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C81, and C83, C84, C86-C88, C90 and C91 were similarly prepared using the method of Example 23, the latter admixtures employing lactic acid, malic acid or citric acid instead of glycolic acid.

TABLE 33 Preparation and Properties of Admixtures C79-C91 Admixture Reactants (Mass in g) Reaction Product # Mol Composition KOH Al(OH)₃ Water pH Appearance Gly C79 K₁(Gly)₁ 3.43 — 6.65 9.9 11.9 Clear Solution C80 K₁Al₁(Gly)₁ 2.15 3.66 4.18 10.0 8.6 White Suspension C81 K₂Al₂(Gly)₃ 1.82 3.10 5.31 9.8 8.4 White Suspension Lac C82 K₁(Lac)₁ 3.10 — 5.54 11.4 12.7 Clear Solution C83 K₁Al₁(Lac)₁ 2.02 3.43 3.61 10.9 9.4 White Suspension C84 K₁Al₁(Lac)₂ 1.44 2.45 5.15 11.0 8.9 Cloudy Solution Mal C85 K₂(Mal)₁ 3.68 — 4.40 11.9 12.7 Clear Solution C86 K₁Al₁(Mal)₁ 1.69 2.87 4.04 11.4 7.6 White Suspension C87 K₂Al₁(Mal)₁ 2.79 2.37 3.34 11.5 11.2 Clear Solution C88 K₃Al₂(Mal)₁ 2.96 3.36 2.37 11.3 8.9 White Suspension Cit C89 K₃(Cit)₁ 3.77 — 4.31 11.9 9.9 Clear Solution C90 K₂Al₁(Cit)₁ 2.37 2.01 4.06 11.6 8.8 Clear Solution C91 K₅Al₁(Cit)₂ 3.05 1.04 4.18 11.7 9.7 Clear Solution Notes: Reaction conditions are detailed in Examples 22 and 23; KOH is potassium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Gly is glycolic acid; Lac is lactic acid; Mal is malic acid; Cit is citric acid; W is water.

TABLE 34 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C79-C91 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C79 0.41 6.0 2.46 180 59 8.4 18.1 C80 0.41 6.0 2.46 95 112 16.3 35.4 C81 0.41 6.0 2.46 90 108 16.9 38.7 C82 0.41 6.0 2.46 205 60 9.0 21.4 C83 0.41 6.0 2.46 85 108 15.7 35.1 C84 0.41 6.0 2.46 80 117 17.2 40.6 C85 0.41 6.0 2.46 190 58 8.8 20.1 C86 0.41 6.0 2.46 75 131 18.1 42.5 C87 0.41 6.0 2.46 75 122 17.3 41.0 C88 0.41 6.0 2.46 65 118 17.0 35.3 C89 0.41 6.0 0.80 210 55 8.1 17.3 C90 0.41 6.0 0.80 125 115 17.7 37.3 C91 0.41 6.0 0.80 110 108 16.3 35.8 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 35 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C79-C91 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C79 0.22 6.0 1.32 18 125 16.4 34.2 C80 0.22 6.0 1.32 32 176 25.8 58.4 C81 0.22 6.0 1.32 27 159 22.5 53.4 C82 0.22 6.0 1.32 22 135 18.7 40.8 C83 0.22 6.0 1.32 27 170 25.1 54.0 C84 0.22 6.0 1.32 25 185 26.5 57.2 C85 0.22 6.0 1.32 21 128 18.9 41.7 C86 0.22 6.0 1.32 34 185 27.3 54.7 C87 0.22 6.0 1.32 26 161 23.6 51.1 C88 0.22 6.0 1.32 36 160 22.9 50.6 C89 0.22 6.0 0.80 24 121 16.0 33.4 C90 0.22 6.0 0.80 43 154 21.4 47.0 C91 0.22 6.0 0.80 51 165 23.7 50.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C92-C99 were prepared as 20% w/w aqueous solutions or suspensions, using magnesium or calcium instead of sodium, and the α-hydroxycarboxylic acid, citric acid as the ligand. Admixture C92 is magnesium citrate (Mg₃(Cit)₂), and admixtures C93-C95 are magnesium citratoaluminate(III) complexes (Mg_(x)Al_(y)(Cit)_(y), where x is 1, 2 or 3, and y is 1 or 2). Admixture C96 is calcium citrate (Ca₃(Cit)₂), and admixtures C97-C99 are calcium citratoaluminate(III) complexes (Ca_(x)Al_(y)(Cit)_(y), where x is 1, 2 or 3, and y is 1 or 2). The formulation and preparation of the admixtures is detailed in Table 36, with representative examples (admixtures C92 and C93) provided below as Examples 24 and 25. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 37 and 38 respectively.

Admixtures C92-C99 behaved in a somewhat similar manner to the corresponding sodium-, lithium- and potassium-containing admixtures (detailed in Tables 9-20, and Tables 30-35 respectively), although they showed increased set times and slower hardness and compressive strength development. However, mortars prepared with the admixtures C93-C95, and C97-C99, achieved substantially greater hardness and compressive strength than those prepared with water, calcium or magnesium citrates, or the commercial SikaSet or Pozzutec admixtures.

These results show that magnesium and calcium α-hydroxycarboxylatoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 24 Admixture C92. Magnesium Citrate: Mg₃(Cit)₂

Potassium hydroxide (3.43 g) was dissolved with stirring (340 rpm) in water (9.9 g) maintained at 293 K, glycolic acid (6.65 g) added over 1 minute, and stirring continued at 293 K for 22 hours. A clear solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixture C95 was similarly prepared using the method of Example 24, and employing calcium hydroxide instead of magnesium hydroxide.

Example 25 Admixture C93. Magnesium Citratoaluminate(III): Mg₁Al₂(Cit)₂

Potassium hydroxide (2.15 g) was dissolved with stirring (340 rpm) in water (10.0 g) maintained at 293 K, glycolic acid (4.18 g) added over 2 minutes, and stifling continued for 15 minutes. Aluminum(III) hydroxide (3.66 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C94, C95, and C97-C99 were similarly prepared using the method of Example 25, the latter admixtures employing calcium hydroxide instead of magnesium hydroxide.

TABLE 36 Preparation and Properties of Admixtures C92-C99 Admixture Reactants (Mass in grams) Reaction Products # Mol Composition Al(OH)₃ Cit Water pH Appearance Mg(OH)₂ C92 Mg₃(Cit)₂ 1.26 — 2.78 16.0 6.1 White Suspension C93 Mg₁Al₂(Cit)₂ 0.39 1.28 2.59 15.7 3.6 Clear Solution C94 Mg₁Al₁(Cit)₁ 1.22 0.99 2.01 15.8 6.9 Clear Solution C95 Mg₃Al₂(Cit)₂ 0.99 1.07 2.17 15.8 8.1 Clear Solution Ca(OH)₂ C96 Ca₃(Cit)₂ 1.51 — 2.56 15.9 9.6 White Suspension C97 Ca₁Al₂(Cit)₂ 0.50 1.25 2.53 15.7 4.2 White Suspension C98 Ca₂Al₁(Cit)₁ 1.46 0.92 1.86 15.8 6.3 White Suspension C99 Ca₃Al₂(Cit)₂ 1.20 1.01 2.04 15.8 7.3 White Suspension Notes: Reaction conditions are detailed in Examples 24 and 25; KOH is potassium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Mg(OH)₂ is magnesium hydroxide; Ca(OH)₂ is calcium hydroxide; Cit is citric acid; W is water.

TABLE 37 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C92-C99 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C92 0.41 6.0 2.46 290 51 9.3 22.7 C93 0.41 6.0 2.46 245 78 11.4 26.1 C94 0.41 6.0 2.46 215 92 13.0 28.5 C95 0.41 6.0 2.46 170 101 15.2 32.3 C96 0.41 6.0 2.46 260 53 9.1 24.9 C97 0.41 6.0 2.46 220 96 13.8 29.7 C98 0.41 6.0 2.46 195 112 17.5 36.8 C99 0.41 6.0 2.46 170 103 16.7 38.9 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 38 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C92-C99 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C92 0.22 6.0 1.32 165 42 7.8 18.2 C93 0.22 6.0 1.32 110 88 12.3 26.7 C94 0.22 6.0 1.32 80 109 14.6 31.4 C95 0.22 6.0 1.32 70 131 17.8 36.2 C96 0.22 6.0 1.32 150 47 8.0 17.3 C97 0.22 6.0 1.32 120 135 17.4 37.0 C98 0.22 6.0 1.32 75 171 23.5 47.4 C99 0.22 6.0 1.32 65 146 19.2 42.9 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C100-C106 were prepared as 40% w/w aqueous solutions, using acetic acid together with an α-hydroxycarboxylic acid, selected from malic acid or citric acid, or a combination of α-hydroxycarboxylic acids, selected from malic acid, citric acid and tartaric acid, as ligands. Admixture C100 is a sodium acetatomalatoaluminate(III) complex (Na₂Al₁(Ac)₁(Mal)₁), and admixture C101 is a sodium acetatocitratoaluminate(III) complex (Na₃Al₁(Ac)₁(Cit)₁). Admixture C102 is a sodium malatotartaratoaluminate(III) complex (Na₄Al₂(Tar)₁(Mal)₁), and admixture C103 is a sodium citratotartaratoaluminate(III) complex (Na₅Al₂(Tar)₁(Cit)₁). Admixtures C104-C106 are sodium citratomalatoaluminate(III) complexes (Na_(x)Al₂(Cit)₁(Mal)_(y), where x is 3, 4 or 5, and y is 1 or 2). The formulation and preparation of the admixtures is detailed in Table 39, with a representative example (admixture C100) provided below as Example 26. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 40 and 41 respectively.

Admixtures C100-C106 behaved in a similar manner to the malatoaluminate(III) and citratoaluminate(III) admixtures (detailed in Tables 15-20), with the inclusion of a second α-hydroxycarboxylic acid ligand or a carboxylic acid ligand resulting in a useful variation in the set time, and hardness and compressive strength development. In all cases, mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water, or the commercial SikaSet or Pozzutec admixtures.

These results show that sodium α-hydroxycarboxylatoaluminate(III) complexes with a mixture of carboxylic acid and α-hydroxycarboxylic acid ligands, or a mixture of α-hydroxycarboxylic acid ligands, are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 26 Admixture C100. Sodium Acetatomalatoaluminate(III): Na₂Al₁(Ac)₁(Mal)₁

Sodium hydroxide (1.84 g) was dissolved with stirring (340 rpm) in water (11.5 g) maintained at 293 K, acetic acid (1.38 g) and malic acid (3.08 g) added over 1 minute, and stirring continued for 15 minutes. Aluminum(III) hydroxide (2.18 g) was then added, the temperature raised to 343 K, and stifling continued for 70 hours. A cloudy solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C101-C106 were similarly prepared using the method of Example 26, and using the appropriate acid ligands.

TABLE 39 Preparation and Properties of Admixtures C100-C106 Admixture Reactants (Mass in grams) Reaction Product # Mol Composition NaOH Al(OH)₃ Water pH Appearance Mal Ac C100 Na₂Al₁(Ac)₁(Mal)₁ 1.84 2.18 3.08 1.38 11.5 7.2 Cloudy Solution Cit Ac C101 Na₃Al₁(Ac)₁(Cit)₁ 2.15 1.71 3.29 1.09 11.8 7.8 Cloudy Solution Mal Tar C102 Na₄Al₂(Tar)₁(Mal)₁ 2.15 2.56 1.69 2.02 11.6 8.1 Cloudy Solution Cit Tar C103 Na₅Al₂(Tar)₁(Cit)₁ 2.31 2.20 2.10 1.74 11.6 8.6 Cloudy Solution Cit Mal C104 Na₃Al₂(Cit)₁(Mal)₁ 1.61 2.55 2.41 1.80 11.6 7.3 Cloudy Solution C105 Na₄Al₂(CitA)₁(MalA)₂ 1.67 1.98 1.90 2.79 11.7 7.6 Cloudy Solution C106 Na₅Al₂(Cit)₁(Mal)₂ 1.98 1.88 1.81 2.65 11.7 8.3 Cloudy Solution Notes: Reaction conditions are detailed in Example 26; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Ac is acetic acid; Cit is citric acid; Mal is malic acid; Tar is tartaric acid; W is water.

TABLE 40 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C100-C106 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C100 0.41 6.0 2.46 120 132 18.3 44.7 C101 0.41 6.0 2.46 135 120 17.6 42.9 C102 0.41 6.0 2.46 85 126 18.2 43.6 C103 0.41 6.0 2.46 70 117 17.8 40.2 C104 0.41 6.0 2.46 105 135 19.4 45.6 C105 0.41 6.0 2.46 90 142 21.0 48.7 C106 0.41 6.0 2.46 85 131 18.0 43.0 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 41 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C100-C106 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C100 0.22 6.0 1.32 31 171 25.2 52.8 C101 0.22 6.0 1.32 36 166 24.0 50.6 C102 0.22 6.0 1.32 27 163 23.3 48.7 C103 0.22 6.0 1.32 22 152 21.9 45.3 C104 0.22 6.0 1.32 28 186 27.9 57.6 C105 0.22 6.0 1.32 27 190 28.3 59.1 C106 0.22 6.0 1.32 24 174 26.1 55.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C107-C123 were prepared as 40% w/w aqueous solutions, using the α-hydroxycarboxylic acids, malic acid or citric acid as the primary ligand, and borate (BO₃ ³⁻), which forms complexes with α-hydroxyacids and participates in mineralization reactions, as a secondary ligand. Admixture C107-C110 are sodium boratomalatoaluminate(III) complexes (Na_(x)Al_(y)(BO₃)₄(Mal)_(z), where x is 3 or 4, y is 2, 4 or 6, and z is 2 or 3), and admixture C110-C123 are sodium boratocitratoaluminate(III) complexes (Na_(w)Al_(x)(BO₃)_(y)(Cit)_(z), where w is 2, 3, 4, 5 or 7, x is 1, 2, 3, 4 or 6, y is 2 or 6, and z is 1 or 2). The formulation and preparation of the admixtures is detailed in Table 42, with a representative example (admixture C107) provided below as Example 27. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 43 and 44 respectively.

Admixtures C107-C123 behaved in a similar manner to the malatoaluminate(III) and citratoaluminate(III) admixtures (detailed in Tables 15-20), with the inclusion of borate as a secondary ligand resulting in useful variations in the set time, and hardness and compressive strength development. In all cases, mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water, or the commercial SikaSet or Pozzutec admixtures.

These results show that sodium boratomalatoaluminate(III) and sodium boratocitratoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 27 Admixture C107. Sodium Boratomalatoaluminate(III): Na₃Al₂(BO₃)₄(Mal)₂

Malic acid (2.74 g) was dissolved with stirring (340 rpm) in water (6.6 g) maintained at 293 K, boric acid (2.52 g) added over 1 minute, the temperature raised to 343 K, and stifling continued for 20 hours. The temperature was lowered to 293 K, a solution of sodium hydroxide (1.23 g) in water (5.0 g) added, and stirring continued for 15 minutes. Aluminum(III) hydroxide (1.94 g) was then added, the temperature raised to 343 K, and stirring continued for 50 hours. A cloudy solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C108-C110, and C111-C123 were similarly prepared using the method of Example 27, the latter admixtures employing citric acid instead of malic acid.

TABLE 42 Preparation and Properties of Admixtures C107-C123 Admixture Reactants (Mass in grams) Reaction Product # Mol Composition NaOH Al(OH)₃ H₃BO₃ Water pH Appearance Mal C107 Na₃Al₂(BO₃)₄(Mal)₂ 1.23 1.94 2.74 2.52 11.6 7.0 Cloudy Solution C108 Na₃Al₄(BO₃)₄(Mal)₂ 1.02 3.25 2.11 2.11 11.5 7.3 Cloudy Gel C109 Na₄Al₂(BO₃)₄(Mal)₃ 1.34 1.59 3.22 2.07 11.8 6.1 Clear Solution C110 Na₄Al₆(BO₃)₄(Mal)₃ 1.01 3.61 2.33 1.56 11.5 6.7 White Suspension Cit C111 Na₂Al₁(BO₃)₂(Cit)₁ 1.36 1.62 3.13 2.11 11.8 7.1 Clear Solution C112 Na₃Al₁(BO₃)₂(Cit)₁ 1.89 1.50 2.90 1.94 11.8 8.6 Cloudy Solution C113 Na₄Al₁(BO₃)₂(Cit)₁ 2.34 1.39 2.69 1.80 11.8 10.4 Cloudy Solution C114 Na₃Al₂(BO₃)₂(Cit)₁ 1.64 2.60 2.46 1.69 11.6 8.9 Cloudy Solution C115 Na₄Al₂(BO₃)₂(Cit)₁ 2.05 2.43 2.31 1.58 11.6 10.0 White Gel C116 Na₃Al₂(BO₃)₂(Cit)₂ 1.24 1.96 3.76 1.27 11.8 6.5 Clear Solution C117 Na₅Al₂(BO₃)₂(Cit)₂ 1.87 1.78 3.42 1.16 11.8 8.3 Clear Solution C118 Na₃Al₃(BO₃)₂(Cit)₁ 1.45 3.44 2.13 1.49 11.5 8.9 Cloudy Solution C119 Na₄Al₃(BO₃)₂(Cit)₁ 1.82 3.25 2.02 1.41 11.5 9.8 Cloudy Gel C120 Na₅Al₄(BO₃)₂(Cit)₂ 1.58 3.01 2.82 0.98 11.6 8.8 Clear Solution C121 Na₇Al₄(BO₃)₂(Cit)₂ 2.06 2.80 2.63 0.91 11.6 9.7 Cloudy Gel C122 Na₇Al₆(BO₃)₆(Cit)₂ 1.51 3.07 1.91 1.99 11.5 9.1 Cloudy Solution C123 Na₄Al₆(BO₃)₆(Cit)₁ 1.09 3.87 1.19 2.52 11.3 9.8 Cloudy Solution Notes: Reaction conditions are detailed in Example 27; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Cit is citric acid; Mal is malic acid; H₃BO₃ is boric acid; W is water.

TABLE 43 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C107-C123 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C107 0.41 6.0 2.46 325 71 10.7 23.0 C108 0.41 6.0 2.46 310 75 11.1 25.6 C109 0.41 6.0 2.46 280 63 9.3 20.2 C110 0.41 6.0 2.46 315 66 9.9 22.1 C111 0.41 6.0 2.46 270 73 10.8 24.1 C112 0.41 6.0 2.46 255 65 9.8 22.0 C113 0.41 6.0 2.46 240 73 12.4 27.1 C114 0.41 6.0 2.46 280 69 9.5 23.9 C115 0.41 6.0 2.46 260 71 11.8 24.5 C116 0.41 6.0 2.46 290 74 11.3 26.4 C117 0.41 6.0 2.46 275 78 11.2 26.7 C118 0.41 6.0 2.46 260 78 13.3 28.3 C119 0.41 6.0 2.46 230 62 10.6 22.7 C120 0.41 6.0 2.46 225 61 10.2 23.2 C121 0.41 6.0 2.46 210 53 8.8 20.1 C122 0.41 6.0 2.46 215 55 9.8 17.6 C123 0.41 6.0 2.46 230 58 10.6 24.5 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 44 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C107-C123 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C107 0.22 6.0 1.32 33 135 19.5 52.5 C108 0.22 6.0 1.32 42 119 18.0 54.7 C109 0.22 6.0 1.32 21 149 20.1 56.6 C110 0.22 6.0 1.32 42 189 27.2 63.6 C111 0.22 6.0 1.32 50 173 23.6 56.6 C112 0.22 6.0 1.32 23 147 19.5 53.9 C113 0.22 6.0 1.32 38 184 24.5 52.3 C114 0.22 6.0 1.32 20 152 21.6 54.8 C115 0.22 6.0 1.32 28 176 25.6 52.7 C116 0.22 6.0 1.32 30 135 20.2 46.5 C117 0.22 6.0 1.32 28 144 19.0 42.4 C118 0.22 6.0 1.32 54 155 23.6 50.3 C119 0.22 6.0 1.32 50 170 23.3 51.5 C120 0.22 6.0 1.32 30 152 22.0 50.1 C121 0.22 6.0 1.32 26 153 22.5 53.2 C122 0.22 6.0 1.32 28 180 25.1 60.4 C123 0.22 6.0 1.32 21 158 24.7 50.5 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C124-C132 were prepared as 40% w/w aqueous suspensions, using the α-hydroxycarboxylic acid, citric acid as the primary ligand, and phosphate (PO₄ ³⁻) and carbonate (CO₃ ²⁻), which participate in mineralization reactions, as secondary ligands. Admixtures C124-C126 are sodium phosphatocitratoaluminate(III) complexes (Na_(x)Al₂(PO₄)₁(Cit)₁, where x is 3, 4 or 5). Admixtures C127 and C128 are sodium carbonatocitratoaluminate(III) complexes (Na_(x)Al₂(CO₃)_(y)(Cit)₁, where x is 2 or 4, and y is 1 or 2). Admixture C129 is a calcium carbonatocitratoaluminate(III) complex (Ca₁Al₂(CO₃)₁(Cit)₁), and admixture C130 is a calcium sodium carbonatocitratoaluminate(III) complex (Na₂Ca₁Al₂(CO₃)₂(Cit)₁). Admixture C131 is a magnesium carbonatocitratoaluminate(III) complex (Mg₁Al₂(CO₃)₁(Cit)₁), and admixtures C132 is a magnesium sodium carbonatocitratoaluminate(III) complex (Na₂Mg₁Al₂(CO₃)₂(Cit)₁). The formulation and preparation of the admixtures is detailed in Table 45, with representative examples (admixtures C124, C127, C129 and C130) provided below as Examples 28-31. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 46 and 47 respectively.

Admixtures C124-C131 behaved in a similar manner to the citratoaluminate(III) admixtures (detailed in Tables 18-20), with the inclusion of phosphate or carbonate as secondary ligands resulting in useful variations in the set time, and hardness and compressive strength development. In all cases, mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water, or the commercial SikaSet or Pozzutec admixtures.

These results show that sodium, calcium, magnesium and mixed calcium-sodium and magnesium-sodium phosphatocitratoaluminate(III) and carbonatocitratoaluminate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 28 Admixture C124. Sodium Phosphatocitratoaluminate(III): Na₃Al₂(PO₄)₁(Cit)₁

Sodium hydroxide (1.71 g) was dissolved with stirring (340 rpm) in water (6.4 g) maintained at 293 K, phosphoric acid (1.65 g) added over 2 minutes, the temperature raised to 343 K, and stirring continued for 5 hours. A solution of citric acid (2.49 g) in water (5.0 g) was then added, and stifling continued for 15 minutes. Aluminum(III) hydroxide (2.72 g) was then added, and stirring continued for 50 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C125-C126 were similarly prepared using the method of Example 28.

Example 29 Admixture C127. Sodium Carbonatocitratoaluminate(III): Na₂Al₂(CO₃)₁(Cit)₁

Citric acid (3.42 g) was dissolved with stirring (340 rpm) in water (6.3 g) maintained at 293 K, aluminum hydroxide (3.39 g) added over 1 minute, the temperature raised to 343 K, and stirring continued for 40 hours. A solution of sodium carbonate (1.89 g) in water (5.0 g) was then added, and stifling continued for 42 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixture C128 was similarly prepared using the method of Example 29.

Example 30 Admixture C129. Calcium Carbonatocitratoaluminate(III): Ca₁Al₂(CO₃)₁(Cit)₁

Citric acid (3.46 g) was dissolved with stirring (340 rpm) in water (11.3 g) maintained at 293 K, aluminum hydroxide (3.43 g) added over 1 minute, the temperature raised to 343 K, and stirring continued for 40 hours. Calcium carbonate (1.80 g) was then added, and stifling continued for 42 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixture C131 was similarly prepared using the method of Example 30, but using magnesium carbonate instead of calcium carbonate.

Example 31 Admixture C130. Calcium Sodium Carbonatocitratoaluminate(III): Na₂Ca₁Al₂(CO₃)₂(Cit)₁

Citric acid (2.80 g) was dissolved with stirring (340 rpm) in water (6.6 g) maintained at 293 K, aluminum hydroxide (2.59 g) added over 1 minute, the temperature raised to 343 K, and stirring continued for 40 hours. Calcium carbonate (1.46 g) was then added, followed by a solution of sodium carbonate (1.55 g) in water (5.0 g), and stifling continued for 42 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixture C132 was similarly prepared using the method of Example 30, but using magnesium carbonate instead of calcium carbonate.

TABLE 45 Preparation and Properties of Admixtures C124-C132 Admixture Reactants (Mass in g) Reaction Product # Mol Composition Al(OH)₃ Cit Water pH Appearance NaOH H₃PO₄ C124 Na₃Al₂(PO₄)₁(Cit)₁ 1.71 2.72 2.49 1.65 11.4 6.6 White Suspension C125 Na₄Al₂(PO₄)₁(Cit)₁ 2.13 2.54 2.34 1.54 11.5 8.7 White Suspension C126 Na₅Al₂(PO₄)₁(Cit)₁ 2.50 2.38 2.20 1.44 11.5 10.5 White Suspension Na₂CO₃ C127 Na₂Al₂(CO₃)₁(Cit)₁ 1.89 3.39 3.42 — 11.3 10.3 White Suspension C128 Na₄Al₂(CO₃)₂(Cit)₁ 3.06 2.74 2.77 — 11.4 10.7 White Suspension Na₂CO₃ CaCO₃ C129 Ca₁Al₂(CO₃)₁(Cit)₁ — 3.43 3.46 1.80 11.3 6.3 White Suspension C130 Na₂Ca₁Al₂(CO₃)₂(Cit)₁ 1.55 2.59 2.80 1.46 11.6 10.4 White Suspension Na₂CO₃ MgCO₃ C131 MgAl₂(CO₃)₁(Cit)₁ — 3.56 3.59 1.58 11.3 7.6 White Suspension C132 Na₂Mg₁Al₂(CO₃)₂(Cit)₁ 1.59 2.66 2.88 1.27 11.6 10.8 White Suspension Notes: Reaction conditions are detailed in Examples 28-31; NaOH is sodium hydroxide; Na₂CO₃ is sodium carbonate; Al(OH)₃ is aluminum(III) hydroxide; CaCO₃ is calcium carbonate; MgCO₃ is magnesium carbonate; Cit is citric acid; H₃PO₄ is phosphoric acid; W is water.

TABLE 46 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C124-C132 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C124 0.41 6.0 2.46 130 62 9.3 19.8 C125 0.41 6.0 2.46 115 77 12.5 27.9 C126 0.41 6.0 2.46 110 70 12.4 30.1 C127 0.41 6.0 2.46 150 137 19.1 42.7 C128 0.41 6.0 2.46 140 149 21.3 45.8 C129 0.41 6.0 2.46 120 142 20.1 43.5 C130 0.41 6.0 2.46 135 153 22.8 47.4 C131 0.41 6.0 2.46 115 138 20.2 44.6 C132 0.41 6.0 2.46 90 162 25.5 51.6 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 47 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C124-C132 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C124 0.22 6.0 1.32 28 134 20.4 47.0 C125 0.22 6.0 1.32 23 163 23.3 51.0 C126 0.22 6.0 1.32 18 171 22.5 51.8 C127 0.22 6.0 1.32 28 160 22.8 47.5 C128 0.22 6.0 1.32 35 171 24.6 50.3 C129 0.22 6.0 1.32 43 153 21.7 45.9 C130 0.22 6.0 1.32 39 162 23.0 49.0 C131 0.22 6.0 1.32 33 159 22.1 46.2 C132 0.22 6.0 1.32 37 178 24.9 53.0 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C133-C151 were prepared as 40% w/w aqueous suspensions, using the α-hydroxycarboxylic acids, malic acid and citric acid as ligand, and bismuth(III) instead of aluminum(III) as the coordinating metal center. Admixtures C149-C151 also contained borate as a secondary ligand. Admixtures C133-C134 are bismuth(III) malate complexes (Bi₂(Mal)_(x), where x is 1 or 3), and admixtures C135-C138 are sodium malatobismuthate(III) complexes (Na_(x)Bi₁(Mal)_(y), where x is 1-3, and y is 1 or 2). Admixtures C139-C140 are bismuth(III) citrate complexes (Bi_(x)(Cit)₁, where x is 1 or 3), and admixtures C141-C148 are sodium citratobismuthate(III) complexes (Na_(x)Bi₁(Cit)_(y), where x is 1-6, and y is 1 or 2). Admixtures C149-C151 are sodium boratocitratobismuthate(III) complexes (Na_(w)Bi_(x)(BO₃)_(y)Cit)_(z), where w is 3-6, and x and y are 1 or 2, and z is 2 or 3). The formulation and preparation of the admixtures is detailed in Table 48, with representative examples (admixtures C133, C135, C149) provided below as Examples 32-34. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 49 and 50 respectively.

Admixtures C133-C151 behaved in a similar manner to the malatoaluminate(III) and citratoaluminate(III) admixtures (detailed in Tables 15-20), except that the substitution of bismuth(III) for aluminum(III) resulted in substantial set retardation, especially with the fly ash C-sand mortars. In certain cases (admixtures C142, C145 and C148), no setting was observed for fly ash C-sand mortars within the observation period (7 days). In almost all cases, mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water, or the commercial SikaSet or Pozzutec admixtures.

These results show that sodium malatobismuthate(III), citratobismuthate(III) and boratocitratobismuthate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 32 Admixture C133. Bismuth(III) Citrate: Bi₁(Mal)₁

Malic acid (1.81 g) was dissolved with stirring (340 rpm) in water (11.9 g) maintained at 293 K, bismuth(III) oxide (6.28 g) added over 2 minutes, the temperature raised to 343 K, and stirring continued for 70 hours. A yellow suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C134, and C139-C140 were similarly prepared using the method of Example 32, the latter admixtures employing citric acid instead of malic acid.

Example 33 Admixture C135. Sodium malatobismuthate(III): Na₁Bi₁(Mal)₁

Sodium hydroxide (0.79 g) was dissolved with stirring (340 rpm) in water (11.9 g) maintained at 293 K, malic acid (2.66 g) added over 1 minute, and stirring continued for 15 minutes. Bismuth(III) oxide (4.62 g) was then added, the temperature raised to 343 K, and stirring continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C136-C138, and C141-C148 were similarly prepared using the method of Example 33, the latter admixtures employing citric acid instead of malic acid.

Example 34 Admixture C149. Sodium Boratocitratobismuthate(III): Na₃Bi₁(BO₃)₂(Cit)₂

Citric acid (3.57 g) was dissolved with stirring (340 rpm) in water (6.0 g) maintained at 293 K, boric acid (1.16 g) added over 1 minute, the temperature raised to 343 K, and stifling continued for 20 hours. A solution of sodium hydroxide (1.13 g) in water (6.0 g) was then added, followed by bismuth(III) oxide (2.19 g) and stirring continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C150 and C151 were similarly prepared using the method of Example 34.

TABLE 48 Preparation and Properties of Admixtures C133-C151 Admixture Reactants (Mass in g) Reaction Product # Mol Composition NaOH Bi₂O₃ Water pH Appearance Mal — C133 Bi₂(Mal)₁ — 6.28 1.81 11.9 — 6.3 Yellow Suspension C134 Bi₂(Mal)₃ — 4.34 3.74 11.9 — 3.1 White Suspension C135 Na₁Bi₁(Mal)₁ 0.79 4.62 2.66 11.9 — 8.1 White Suspension C136 Na₂Bi₁(Mal)₁ 1.45 4.21 2.42 11.9 — 10.9 White Suspension C137 Na₂Bi₁(Mal)₂ 1.11 3.24 3.73 11.9 — 7.2 White Suspension C138 Na₃Bi₁(Mal)₂ 1.56 3.03 3.49 11.9 — 9.6 White Suspension Cit C139 Bi₃(Cit)₁ — 6.34 1.74 11.9 — 5.1 Yellow Suspension C140 Bi₁(Cit)₁ — 4.43 3.65 11.9 — 4.4 White Suspension C141 Na₁Bi₁(Cit)₁ 0.69 4.05 3.34 11.9 — 6.6 White Suspension C142 Na₂Bi₁(Cit)₁ 1.28 3.73 3.07 11.9 — 7.9 White Suspension C143 Na₃Bi₁(Cit)₁ 1.78 3.45 2.85 11.9 — 12.3 Yellow Suspension C144 Na₃Bi₁(Cit)₂ 1.32 2.55 4.21 11.9 — 5.5 White Suspension C145 Na₄Bi₁(Cit)₂ 0.49 2.86 4.72 11.9 — 5.9 White Suspension C146 Na₅Bi₁(Cit)₂ 0.49 2.86 4.72 11.9 — 7.9 White Suspension C147 Na₆Bi₁(Cit)₂ 0.49 2.86 4.72 11.9 — 12.7 Yellow Suspension C148 Na₃Bi₃(Cit)₂ 0.81 4.69 2.58 11.9 — 7.5 White Suspension H₃BO₃ C149 Na₃Bi₁(BO₃)₂(Cit)₂ 1.13 2.19 3.57 12.0 1.16 4.8 White Suspension C150 Na₄Bi₂(BO₃)₂(Cit)₂ 1.14 3.32 2.71 11.9 0.88 7.2 White Suspension C151 Na₆Bi₂(BO₃)₁(Cit)₃ 1.44 2.80 3.43 12.0 0.37 7.4 White Suspension Notes: Reaction conditions are detailed in Examples 32-34; NaOH is sodium hydroxide; Bi₂O₃ is bismuth(III) oxide; Mal is malic acid; Cit is citric acid; H₃BO₃ is boric acid; W is water.

TABLE 49 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C133-C151 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C133 0.41 6.0 2.46 380 43 6.4 13.6 C134 0.41 6.0 2.46 440 47 7.9 19.1 C135 0.41 6.0 2.46 420 71 11.2 23.6 C136 0.41 6.0 2.46 415 71 12.9 28.9 C137 0.41 6.0 2.46  8 h 73 12.5 29.5 C138 0.41 6.0 2.46 430 85 13.0 30.7 C139 0.41 6.0 2.46 315 40 5.9 12.6 C140 0.41 6.0 2.46  8 h 44 6.3 14.4 C141 0.41 6.0 2.46 335 93 14.3 32.6 C142 0.41 6.0 2.46 12 h 88 12.4 28.9 C143 0.41 6.0 2.46 415 92 13.2 32.5 C144 0.41 6.0 2.46 12 h 91 13.8 32.7 C145 0.41 6.0 2.46 15 h 94 14.9 32.1 C146 0.41 6.0 2.46  8 h 107 15.8 36.8 C147 0.41 6.0 2.46 375 111 16.7 37.1 C148 0.41 6.0 2.46 18 h 93 13.5 29.4 C149 0.41 6.0 2.46 13 h 112 16.9 39.0 C150 0.41 6.0 2.46  9 h 108 18.1 40.3 C151 0.41 6.0 2.46  8 h 96 15.2 37.1 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 50 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C133-C151 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C133 0.22 6.0 1.32 105 108 16.7 29.9 C134 0.22 6.0 1.32 130 96 14.5 26.9 C135 0.22 6.0 1.32 115 102 16.2 33.5 C136 0.22 6.0 1.32 90 112 17.3 38.9 C137 0.22 6.0 1.32 120 98 15.0 32.5 C138 0.22 6.0 1.32 110 103 16.4 36.8 C139 0.22 6.0 1.32 47 105 15.6 28.8 C140 0.22 6.0 1.32 135 99 14.4 27.8 C141 0.22 6.0 1.32 90 186 24.5 47.9 C142 0.22 6.0 1.32 No Set <2 ND ND C143 0.22 6.0 1.32 80 161 24.7 50.1 C144 0.22 6.0 1.32 60 h 178 26.4 53.9 C145 0.22 6.0 1.32 No Set <2 ND ND C146 0.22 6.0 1.32 70 h 195 25.5 51.9 C147 0.22 6.0 1.32 80 181 25.6 52.6 C148 0.22 6.0 1.32 No Set <2 ND ND C149 0.22 6.0 1.32 44 h 176 25.4 53.1 C150 0.22 6.0 1.32 20 h 170 24.7 53.2 C151 0.22 6.0 1.32 29 h 171 24.4 50.1 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C152-C160 were prepared as 40% w/w aqueous suspensions, using the α-hydroxycarboxylic acids, malic acid and citric acid as ligand, and both aluminum(III) and bismuth(III) as coordinating metal centers. Admixtures C152-C154 are sodium malatoaluminate(III)bismuthate(III) complexes (Na_(x)Al₄Bi₁(Mal)_(y), where x is 5, 10 or 15, and y is 5 or 10). Admixtures C155-C160 are sodium citratoaluminate(III)bismuthate(III) complexes (Na_(x)Al₄Bi₁(Cit)_(y), where x is 8, 10, 15, 20 or 30, and y is 5 or 10). The formulation and preparation of the admixtures is detailed in Table 51, with a representative example (admixture C152) provided below as Example 35. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 52 and 53 respectively.

Admixtures C152-C160 behaved in an intermediate manner to the malatoaluminate(III) and citratoaluminate(III) admixtures (detailed in Tables 8-20) and the malatobismuthate(III) and citratobismuthate(III) admixtures (detailed in Tables 48-50), with the inclusion of bismuth(III) resulting in significant set retardation, especially with the fly ash C-sand mortars. In all cases, mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water or the commercial SikaSet or Pozzutec admixtures.

These results show that sodium malatoaluminate(III)bismuthate(III) and citratoaluminate(III)bismuthate(III) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 35 Admixture C152. Sodium Malatoaluminate(III)bismuthate(III): Na₅Al₄Bi₁(Mal)₅

Sodium hydroxide (1.14 g) was dissolved with stirring (340 rpm) in water (11.5 g) maintained at 293 K, malic acid (3.83 g) added over 1 minute, and stirring continued for 15 minutes. Aluminum(III) hydroxide (2.17 g), was then added over 1 min, followed by bismuth(III) oxide (1.33 g), the temperature raised to 343 K, and stirring continued for 70 hours. A white suspension was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C153 and C154, and C155-C160 were similarly prepared using the method of Example 35, the latter admixtures employing citric acid instead of malic acid.

TABLE 51 Preparation and Properties of Admixtures C152-C160 Admixture Reactants (Mass in g) Reaction Product # Mol Composition NaOH Al(OH)₃ Bi₂O₃ Water pH Appearance Mal C152 Na₅Al₄Bi₁(Mal)₅ 1.14 2.17 1.33 3.83 11.5 7.3 White Suspension C153 Na₁₀Al₄Bi₁(Mal)₁₀ 1.41 1.34 0.82 4.74 11.7 4.8 White Suspension C154 Na₁₅Al₄Bi₁(Mal)₁₀ 1.95 1.24 0.76 4.36 11.7 7.9 White Suspension Cit C155 Na₅Al₄Bi₁(Cit)₅ 0.95 1.80 1.10 4.55 11.6 2.9 White Suspension C156 Na₈Al₄Bi₁(Cit)₅ 1.42 1.68 1.03 4.25 11.6 6.9 White Suspension C157 Na₁₀Al₄Bi₁(Cit)₅ 1.70 1.61 0.99 4.07 11.6 8.6 White Suspension C158 Na₁₅Al₄Bi₁(Cit)₅ 2.30 1.46 0.89 3.69 11.7 11.3 White Suspension C159 Na₂₀Al₄Bi₁(Cit)₁₀ 1.98 0.94 0.58 4.75 11.7 6.1 White Suspension C160 Na₃₀Al₄Bi₁(Cit)₁₀ 2.65 0.84 0.51 4.23 11.8 11.3 Yellow Suspension Notes: Reaction conditions are detailed in Example 35; NaOH is sodium hydroxide; Al(OH)₃ is aluminum(III) hydroxide; Bi₂O₃ is bismuth(III) oxide; Mal is malic acid; Cit is citric acid; W is water.

TABLE 52 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C152-C160 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C152 0.41 6.0 2.46 350 122 16.7 35.9 C153 0.41 6.0 2.46 370 136 17.4 40.7 C154 0.41 6.0 2.46 325 126 17.2 44.6 C155 0.41 6.0 2.46 305 103 17.2 39.0 C156 0.41 6.0 2.46 310 118 19.1 40.2 C157 0.41 6.0 2.46 285 123 20.6 43.6 C158 0.41 6.0 2.46 270 117 20.3 46.5 C159 0.41 6.0 2.46 360 125 22.5 43.7 C160 0.41 6.0 2.46 330 112 22.9 44.5 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 53 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C152-C160 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C152 0.22 6.0 1.32 65 171 24.7 54.2 C153 0.22 6.0 1.32 70 195 28.5 56.3 C154 0.22 6.0 1.32 85 189 28.9 55.7 C155 0.22 6.0 1.32 53 194 26.6 50.9 C156 0.22 6.0 1.32 62 189 26.9 53.3 C157 0.22 6.0 1.32 75 197 28.9 56.7 C158 0.22 6.0 1.32 75 166 24.9 53.8 C159 0.22 6.0 1.32 115 216 29.4 57.1 C160 0.22 6.0 1.32 90 185 25.9 53.4 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

Admixtures C161-C184 were prepared as 20 or 40% w/w aqueous solutions or suspensions, using the α-hydroxycarboxylic acids, malic acid and citric acid as ligands, and a variety of metals, namely magnesium(II), calcium(II), indium(III), gallium(III), iron(III), zinc(II), zirconium(IV), lanthanum(III), yttrium(III), molybdenum(VI) and tungsten(VI), as coordinating metal centers instead of aluminum(III). Admixture C161 is sodium magnesium citrate complex (Na₂Mg₁(Cit)₁). Admixture C162 is sodium calcium citrate complex (Na₂Ca₁(Cit)₁). Admixtures C163 and C164 are sodium malatoindate(III) complexes (Na₁In₁(Mal)₁ and Na₃In₁(Mal)₂). Admixtures C165 and C166 are sodium malatogallate(III) complexes (Na₁Ga₁(Mal)₁ and Na₃Ga₁(Mal)₂). Admixtures C167 and C168 are sodium malatoferrate(III) complexes (Na₁Fe(III)₁(Mal)₁ and Na₂Fe(III)₁(Mal)₁). Admixtures C169 and C170 are sodium malatozincate(II) complexes (Na₁Zn₁(Mal)₁ and Na₃Zn₁(Mal)₂). Admixtures C171 and C172 are sodium malatozirconate(IV) complexes (Na₂Zr₁(Mal)₁ and Na₃Zr₁(Mal)₂). Admixtures C173 and C174 are sodium malatolanthanate(III) complexes (Na₁La₁(Mal)₁ and Na₃La₁(Mal)₂). Admixtures C175 and C176 are sodium malatoyttrate(III) complexes (Na₁Y₁(Mal)₁ and Na₃Y₁(Mal)₂). Admixtures C177-C180 are sodium citratomolybdate(VI) complexes (Na_(x)Mo_(y)(Mal)_(z), where x is 3, 4, 5 or 7, y is 1 or 2, and z is 1 or 2). Admixtures C181-C184 are sodium citratotungstate(VI) complexes (Na_(x)W₁(Mal)_(z), where x is 3, 4, 6 or 7, and y is 1 or 2). The formulation and preparation of the admixtures is detailed in Table 54, with a representative example (admixture C161) provided below as Example 36. The testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 55 and 56 respectively.

Admixtures C161-C184 behaved in a similar manner to the malatoaluminate(III) and citratoaluminate(III) admixtures (detailed in Tables 15-20), with the substitution of aluminum(III) by magnesium(II), calcium(II), indium(III), gallium(III), iron(III), zinc(II), zirconium(IV), lanthanum(III), yttrium(III), molybdenum(VI) and tungsten(VI), resulting in reduced hardness and compressive strength development. In all cases, mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water or the commercial SikaSet or Pozzutec admixtures.

These results show that sodium magnesium citrate, sodium calcium citrate, sodium malatoindate(III), sodium malatogallate(III), malatoferrate(III), sodium malatozincate(II), malatozirconate(IV), sodium malatolanthanate(III), malatoyttrate(III), sodium citratomolybdate(VI) and sodium citratotungstate(VI) complexes are useful as admixtures for hydraulic cement compositions, and that they improve setting, hardness and compressive strength.

Example 36 Admixture C161. Sodium Magnesium Citrate Complex: Na₂Mg₁(Cit)₁

Sodium hydroxide (0.98 g) was dissolved with stirring (340 rpm) in water (16.0 g) maintained at 293 K, citric acid (2.35 g) added over 1 minute, and stifling continued for 15 minutes. Magnesium hydroxide (0.71 g), was then added over 1 min, the temperature raised to 343 K, and stirring continued for 70 hours. A cloudy solution was obtained, and this was diluted to 6% w/w solids for testing.

Admixtures C160-C184 were similarly prepared using the method of Example 36, with calcium(hydroxide, indium(III) oxide, gallium(III) oxide, iron(III) hydroxide, zinc(II) oxide, zirconium(IV) hydroxide, lanthanum(III) oxide, yttrium(III) oxide, molybdenum(VI) oxide and tungsten(VI) oxide used in place of magnesium hydroxide, and citric acid used in place of malic acid, where indicated.

TABLE 54 Preparation and Properties of Admixtures C161-C184 Admixture Reactants (Mass in grams) Reaction Products # Mol Composition NaOH Water pH Appearance Mg(OH)₂ Cit C161 Na₂Mg₁(Cit)₁ 0.98 0.71 2.35 16.0 9.8 Cloudy Solution Ca(OH)₂ Cit C162 Na₂Ca₁(Cit)₁ 0.93 0.88 2.24 15.9 10.2 White Suspension In₂O₃ Mal C163 Na₁In₁(Mal)₁ 1.03 3.58 3.46 11.9 7.2 Cloudy Solution C164 Na₃In₁(Mal)₂ 1.84 2.13 4.11 11.9 8.8 Cloudy Solution Ga₂O₃ Mal C165 Na₁Ga₁(Mal)₁ 1.21 2.83 4.05 11.9 7.8 Cloudy Solution C166 Na₃Ga₁(Mal)₂ 2.01 1.57 4.50 11.9 9.2 Cloudy Solution Fe(OH)₃ Mal C167 Na₁Fe(III)₁(Mal)₁ 1.15 3.11 3.86 11.9 9.8 Brown Solution C168 Na₂Fe(III)₁(Mal)₁ 2.01 2.72 3.38 11.9 8.1 Brown Suspension ZnO Mal C169 Na₁Zn₁(Mal)₁ 1.27 2.57 4.24 11.9 7.0 White Suspension C170 Na₃Zn₁(Mal)₂ 2.06 1.40 4.62 11.9 8.1 White Suspension Zr(OH)₄ Mal C171 Na₂Zr₁(Mal)₁ 1.73 3.45 2.90 11.9 11.5 White Suspension C172 Na₃Zr₁(Mal)₂ 1.77 2.35 3.96 11.9 4.8 White Suspension La₂O₃ Mal C173 Na₁La₁(Mal)₁ 0.96 3.91 3.22 11.9 7.3 White Suspension C174 Na₃La₁(Mal)₂ 1.76 2.39 3.93 11.9 8.8 White Suspension Y₂O₃ Mal C175 Na₁Y₁(Mal)₁ 1.13 3.18 3.78 11.9 7.5 White Suspension C176 Na₃Y₁(Mal)₂ 1.94 1.82 4.33 11.9 9.1 White Suspension MoO₃ Cit C177 Na₄Mo₂(Cit)₁ 2.02 3.63 2.43 11.9 5.7 Clear Solution C178 Na₅Mo₂(Cit)₁ 2.38 3.42 2.28 11.9 6.6 Clear Solution C179 Na₃Mo₁(Cit)₁ 2.13 2.55 3.40 11.9 5.9 Clear Solution C180 Na₇Mo₂(Cit)₂ 2.38 2.44 3.26 11.9 6.9 Clear Solution WO₃ Cit C181 Na₃W₁(Cit)₁ 1.78 3.44 2.85 11.9 6.4 Clear Solution C182 Na₄W₁(Cit)₁ 2.21 3.21 2.66 11.9 12.8 Clear Solution C183 Na₆W₁(Cit)₂ 2.27 2.19 3.63 11.9 6.7 Clear Solution C184 Na₇W₁(Cit)₂ 2.53 2.09 3.47 11.9 7.5 Clear Solution Notes: Reaction conditions are detailed in Example 36; Mg(OH)₂ is magnesium hydroxide; Ca(OH)₂ is calcium hydroxide; In₂O₃ is indium(III) oxide; Ga₂O₃ is gallium(III) oxide; Fe(OH)₃ is iron(III) hydroxide; ZnO is zinc(II) oxide; Zr(OH)₄ is zirconium(IV) hydroxide; La₂O₃ is lanthanum(III) oxide; Y₂O₃ is yttrium(III) oxide; MoO₃ is molybdenum(VI) oxide; WO₃ is tungsten(VI) oxide; Mal is malic acid; Cit is citric acid; W is water.

TABLE 55 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C161-C184 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C161 0.41 6.0 2.46 160 84 12.7 27.9 C162 0.41 6.0 2.46 135 90 13.5 27.8 C163 0.41 6.0 2.46 115 131 20.9 43.0 C164 0.41 6.0 2.46 105 126 18.8 39.7 C165 0.41 6.0 2.46 120 123 18.1 36.4 C166 0.41 6.0 2.46 95 125 19.2 38.0 C167 0.41 6.0 2.46 110 147 21.7 50.8 C168 0.41 6.0 2.46 80 156 22.9 53.6 C169 0.41 6.0 2.46 210 116 15.1 29.3 C170 0.41 6.0 2.46 190 121 17.0 34.5 C171 0.41 6.0 2.46 180 92 15.5 31.6 C172 0.41 6.0 2.46 150 107 15.8 33.8 C173 0.41 6.0 2.46 125 116 17.2 39.4 C174 0.41 6.0 2.46 90 122 19.1 42.5 C175 0.41 6.0 2.46 110 128 19.3 43.7 C176 0.41 6.0 2.46 85 126 19.7 44.2 C177 0.41 6.0 2.46 310 121 20.8 40.6 C178 0.41 6.0 2.46 280 126 22.5 43.5 C179 0.41 6.0 2.46 255 112 17.3 36.7 C180 0.41 6.0 2.46 230 125 19.7 38.3 C181 0.41 6.0 2.46 295 108 17.3 32.9 C182 0.41 6.0 2.46 290 121 21.8 42.6 C183 0.41 6.0 2.46 250 124 22.4 46.9 C184 0.41 6.0 2.46 230 123 21.5 43.5 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 56 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C161-C184 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C161 0.22 6.0 1.32 52 92 13.4 29.0 C162 0.22 6.0 1.32 40 88 12.8 27.6 C163 0.22 6.0 1.32 32 141 23.6 51.2 C164 0.22 6.0 1.32 27 136 20.8 48.5 C165 0.22 6.0 1.32 37 133 21.5 50.3 C166 0.22 6.0 1.32 33 125 18.3 46.7 C167 0.22 6.0 1.32 35 171 26.0 54.1 C168 0.22 6.0 1.32 29 180 27.3 55.6 C169 0.22 6.0 1.32 28 104 16.7 35.2 C170 0.22 6.0 1.32 22 111 17.4 37.5 C171 0.22 6.0 1.32 33 112 17.4 36.5 C172 0.22 6.0 1.32 29 123 18.5 40.1 C173 0.22 6.0 1.32 38 141 21.3 47.5 C174 0.22 6.0 1.32 29 134 19.6 45.3 C175 0.22 6.0 1.32 26 153 22.8 49.6 C176 0.22 6.0 1.32 22 145 20.3 47.8 C177 0.22 6.0 1.32 56 109 16.5 39.2 C178 0.22 6.0 1.32 51 118 18.3 41.8 C179 0.22 6.0 1.32 49 135 20.9 42.0 C180 0.22 6.0 1.32 38 126 17.5 37.6 C181 0.22 6.0 1.32 65 134 19.3 38.2 C182 0.22 6.0 1.32 85 162 24.6 49.4 C183 0.22 6.0 1.32 65 141 20.8 44.6 C184 0.22 6.0 1.32 60 129 19.3 42.0 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

In Examples 37-40, the scale-up of representative admixtures (C185-C188) is described, using aluminum(III) hydroxide as precursor (Examples 37 and 38, admixtures C185 and C186), and sodium aluminate(III) as precursor (Examples 39 and 40, admixtures C187 and C188). Admixture C185 is a sodium lactatoaluminate(III) complex (Na₃Al₂(Lac)₄) prepared as a 50% w/w aqueous solution, and admixture C186 is a sodium citratoaluminate(III) complex (Na₂Al₁(Cit)₁) prepared as a 50% w/w aqueous solution. Admixture C187 is a sodium citratoaluminate(III) complex (Na₃₃Al₂₄(Cit)₁₆) isolated as a solid, and admixture C188 is a sodium lactatoaluminate(III) complex (Na₃₇Al₂₅(Lac)₅₀) adsorbed onto diatomaceous earth. The formulation and preparation of the admixtures is detailed in Examples 37-40, and the testing of the admixtures for OPC-fly ash F-sand and fly ash C-sand mortars is detailed in Tables 57 and 58 respectively.

Admixtures C185-C188 behaved in a very similar manner to the lactatoaluminate(III) and citratoaluminate(III) admixtures (detailed in Tables 12-14 and 18-20). In all cases, mortars prepared with the admixtures achieved substantially greater hardness and compressive strength than those prepared with water, or the SikaSet or Pozzutec admixtures.

These results show that the syntheses of sodium α-hydroxycarboxylatoaluminate(III) complexes can be readily scaled up for industrial use, and the admixtures obtained as aqueous solutions, solids and adsorbates, for use as admixtures in the present invention.

Example 37 Admixture C185. Sodium Lactatoaluminate(III): Na₃Al₂(Lac)₄

A 30 L Buchi minipilot jacketed glass reactor (fitted with an overhead stirrer, double coil reflux condenser, solid and liquid addition ports, drain valve, a circulating heater, and a circulating cooler) was charged with water (10.638 kg), and stirring (280-300 rpm) initiated. Sodium hydroxide (2.324 kg) was then added over a period of 1 hour, while maintaining the temperature below 343 K, and stirring continued for 1 h, to give a clear solution. The temperature was adjusted to 293 K and lactic acid (7.754 kg) added over a period of 1 hour, while maintaining the temperature below 343 K, and stifling continued for 1 hour. Aluminum(III) hydroxide (3.648 kg) was then added over a period of 15 minutes, the temperature raised to 353 K and stirring continued for a further 70 h, to give a cloudy solution (24.31 kg) with a pH of 8.9. A 100 mL sample of the solution was diluted to 6% w/w solids for testing.

Example 38 Admixture C186. Sodium Citratoaluminate(III): Na₂Al₁(Cit)₁

A 30 L Buchi minipilot jacketed glass reactor was set up as in Example 37, charged with water (7.806 kg), and stirring (290-310 rpm) initiated. Sodium hydroxide (1.916 kg) was then added over a period of 1 hour, while maintaining the temperature below 343 K, and stirring continued for 1 h, to give a clear solution. The temperature was adjusted to 293 K and citric acid (4.600 kg) added over a period of 1 hour, while maintaining the temperature below 343 K, and stirring continued for 1 hour. Aluminum(III) hydroxide (2.278 kg) was then added over a period of 15 minutes, the temperature raised to 353 K and stirring continued for a further 70 h, to give a cloudy solution (16.52 kg) with a pH of 8.8. A 100 mL sample of the solution was diluted to 6% w/w solids for testing.

Example 39 Admixture C187. Sodium Citratoaluminate(III): Na₃₃Al₂₄(Cit)₁₆

A 30 L Buchi minipilot jacketed glass reactor was set up as in Example 37, charged with water (3.319 kg), and stirring (310 rpm) initiated. Sodium aluminate(III) (2.281 kg) was then added over a period of 1 hour, while maintaining the temperature below 343 K, and stirring continued for 2 h, to give a cloudy solution. The temperature was adjusted to 293 K, and a solution of citric acid (3.029 kg) in water (4.439 kg) added over a period of 4 hours, while maintaining the temperature below 323 K, and stirring continued for 2 hours. The temperature was then raised to 353 K and stirring continued for a further 70 h, to give a white suspension. The pH of the solution was then adjusted to 9.5 with 50% w/w sodium hydroxide (0.380 kg), heating stopped, and the mixture stirred for a further 20 h, to give a white suspension (13.27 kg). The suspension was then dried using a Simon drum dryer and flaker, with a drum temperature of 343 K, and suspension feed rate of 3.17 kg per hour, to give the dry product as white flakes (6.31 kg). The product was dissolved in water at 6% w/w solids for testing.

Example 40 Admixture C188. Sodium Lactatoaluminate(III)-Celite: Na₃₇Al₂₅(Lac)₅₀ on Celite

A 15 L Buchi minipilot jacketed glass reactor was set up as in Example 37, charged with water (1.925 kg), and stirring (310 rpm) initiated. Sodium aluminate(III) (1.312 kg) was then added over a period of 1 hour, while maintaining the temperature below 343 K, and stirring continued for 2 h, to give a cloudy solution. The temperature was adjusted to 293 K, and a mixture of lactic acid (2.743 kg) and water (1.478 kg) added over a period of 3 hours, while maintaining the temperature below 323 K, and stirring continued for 2 hours. The temperature was then raised to 353 K and stirring continued for a further 70 h, to give a cloudy solution. The pH of the solution was then adjusted to 9.5 with 50% w/w sodium hydroxide (0.217 kg), heating stopped, and the mixture stirred for a further 20 h, to give a cloudy solution (6.97 kg). The solution was then adsorbed onto diatomaceous earth (3.526 kg) using a Munson MX drum mixer, with a spray rate of 22.6 kg per hour, and a batching time of 20 minutes, then dried using a Simon drum dryer, with a drum temperature of 333 K, to give the diatomaceous earth-supported product as white granules (7.23 kg). This was then milled to below 200 mesh using a Munson SK attrition mill (granules fed at 9.4 kg per h, and batch completed in 1.3 h) to give the product as a white powder. The product was dispersed in water at 6% w/w (active) solids for testing.

TABLE 57 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars made with Admixtures C185-C188 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.46 — — 190 48 7.8 18.9 SNC 0.42 — 0.5 160 52 8.1 22.9 SHE 0.41 — 0.5 125 81 13.6 28.7 P20 0.42 — 0.5 110 93 14.0 32.4 C185 0.41 6.0 2.46 70 147 22.9 55.6 C186 0.41 6.0 2.46 120 143 20.3 50.8 C187 0.41 6.0 2.46 90 154 23.5 55.1 C188 0.41 6.0 2.46 57 138 20.6 49.2 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

TABLE 58 2:3 (w/w) Fly Ash C-Sand Mortars made with Admixtures C185-C188 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) # (w/w) In Stock vs Cement (min) 1 day 1 day 28 day Water 0.27 — — 26 31 4.1 14.3 SNC 0.25 — 0.5 37 44 5.2 16.8 SHE 0.23 — 0.5 42 63 8.9 23.5 P20 0.24 — 0.5 33 71 9.5 26.0 C185 0.22 6.0 1.32 22 193 27.4 60.2 C186 0.22 6.0 1.32 41 151 22.8 54.9 C187 0.22 6.0 1.32 32 188 28.3 57.4 C188 0.22 6.0 1.32 24 158 21.5 52.4 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness; SNC is SikaSet NC; SHE is SikaSet HE; P20 is Pozzutec 20+.

In Examples 43-51 (Table 59), the sodium citratoaluminate(III) complex (Na₃₃Al₂₄(Cit)₁₆, admixture C187) was tested as admixture with mortars made with a variety of other hydraulic cements, namely pure OPC (Example 43), fly ash F-fly ash C (Examples 44 and 45), basic oxygen furnace steel slag (Example 46), basic oxygen furnace steel slag-electric arc furnace steel slag (Example 47), OPC-electric arc furnace steel slag (Example 48), OPC-limestone powder (Examples 49 and 50) and OPC-seawater brucite fines (Examples 51 and 52). Mortars made with admixture C187 typically displayed faster sets and greater hardness and compressive strength as compared to mortars prepared with water alone.

These results show that the admixtures of the present invention, as exemplified by the sodium citratoaluminate(III) complex C187, can be used with pure OPC, blended OPCs and non-OPCs, to gain improvements in setting, hardness and compressive strength.

TABLE 59 Hydraulic Cement-Sand Mortars made with Admixture C186 W/C [Admixture] (% w/w) Set Time Hardness (MPa) Compressive Strength (MPa) Admixture (w/w) In Stock vs Cement (min) 1 day 1 day 28 day EXAMPLE 43. 2:3 (w/w) OPC-Sand Mortar Water 0.47 — — 190 103 14.3 45.7 C187 0.41 6.0 2.46 110 147 22.8 55.3 EXAMPLE 44. 1:1:3 (w/w) Fly Ash F-Fly Ash C-Sand Mortar Water 0.31 — — 140 26 3.5 12.7 C187 0.26 6.0 1.56 47 133 17.6 53.7 EXAMPLE 45. 3:1:6 (w/w) Fly Ash F-Fly Ash C-Sand Mortar Water 0.33 — — 215 22 3.1 10.4 C187 0.28 6.0 1.68 120 117 15.2 46.8 EXAMPLE 46. 2:3 (w/w) Basic Oxygen Furnace Slag-Sand Mortar Water 0.27 6.0 1.50 9 71 9.7 22.5 C186 0.25 14 107 14.1 34.8 EXAMPLE 47. 1:1:3 (w/w) Basic Oxygen Furnace Slag-Electric Arc Furnace Slag-Sand Mortar Water 0.35 — — 12 54 7.8 18.6 C187 0.32 6.0 1.92 15 96 13.2 28.4 EXAMPLE 48. 1:1:3 (w/w) OPC-Electric Arc Furnace Slag-Sand Mortar Water 0.28 — — 17 56 8.4 19.3 C187 0.27 6.0 1.62 23 88 11.6 30.6 EXAMPLE 49. 1:1:3 (w/w) OPC-Limestone Powder-Sand Mortar Water 0.43 — — 255 51 7.3 20.6 C187 0.42 6.0 2.52 220 92 13.1 32.9 EXAMPLE 50. 1:3:6 (w/w) OPC-Limestone Powder-Sand Mortar Water 0.44 — — 375 33 5.2 16.4 C187 0.42 6.0 2.52 255 76 10.8 28.7 EXAMPLE 51. 1:1:3 (w/w) OPC-Seawater Brucite Fines-Sand Mortar Water 0.43 — — 215 55 8.7 21.7 C187 0.40 6.0 2.40 80 121 17.4 43.5 EXAMPLE 52. 1:3:6 (w/w) OPC-Seawater Brucite Fines-Sand Mortar Water 0.42 — — 290 41 6.6 18.2 C187 0.38 6.0 2.28 95 92 13.1 35.6 Notes: W/C is the water-to-cement ratio; Hardness is the Vickers indentation hardness.

In Examples 53-55, other hardened properties and the durability of mortars made w/o the citratoaluminate(III) complex, admixture C187, and w/o an air entrainer (Daravair 1000) was tested by examining linear shrinkage, water permeability and freeze-thaw resistance. 1:1:3 (w/w) OPC-fly ash F-sand mortars are detailed in Example 53, 2:3 (w/w) fly ash C-sand mortars in Example 54, and 1:1:3 (w/w) fly ash C-fly ash F-sand mortars in example 55. In all cases, the inclusion of admixture C187 resulted in a substantial decrease in linear shrinkage and water permeability, and a considerable enhancement in freeze-thaw durability. The improvements in shrinkage, permeability and freeze-thaw resistance were observed both in the absence and presence of Daravair. Furthermore, in the case of freeze-thaw resistance the protective effects of admixture C187 and Daravair appeared to be synergistic.

These results show that the admixtures of the present invention, as exemplified by the sodium citratoaluminate(III) complex C187, improve other hardened properties of cement compositions, such as linear shrinkage and water permeability, as well as durability measures such as freeze-thaw resistance.

TABLE 60 Hardened Properties and Durability of Mortars made w/o Admixture C187 [Admixture] [Daravair] Linear Water (% w/w) (% w/w) Shrinkage Permeability Freeze-Thaw Admixture W/C (vs Cement) (vs Cement) (%, 28 days) (mDa, 28 days) Cycles P_(C) DF EXAMPLE 53. 1:1:3 (w/w) OPC-Fly Ash F-Sand Mortars Water 0.46 — — −0.0452 0.0682 32 13 1.4 C187 0.41 2.46 — −0.0216 0.0024 312 49 51 Water 0.47 — 0.015 −0.0341 0.0378 304 96 97 C187 0.42 2.52 0.015 −0.0198 0.0044 304 99 100 EXAMPLE 54. 2:3 (w/w) Fly Ash C-Sand Mortars Water 0.26 — — −0.1246 0.0426 32 12 1.3 C187 0.22 1.32 — −0.0120 0.0181 311 57 59 Water 0.27 — 0.015 −0.1392 0.0384 76 64 16 C187 0.23 1.38 0.015 −0.0147 0.0209 312 98 102 EXAMPLES 55. 1:1:3 (w/w) Fly Ash C-Fly Ash F-Sand Mortars Water 0.32 — — −0.1782 0.0661 32 8 0.9 C187 0.27 1.62 — −0.0287 0.0215 312 62 65 Water 0.33 — 0.015 −0.2031 0.0492 81 53 14 C187 0.27 1.62 0.015 −0.0310 0.0183 312 98 102 Notes: W/C is the water-to-cement ratio; Cycles is cycles of freeze-thaw completed; P_(C) is the Relative Dynamic Modulus; DF is the Durability Factor

In addition to the above disclosed examples, the admixtures of the present invention may be used as admixtures for other hydraulic cements, including but not restricted to:

(i) Special Portland cements, such as high-alite, low-alite, and high-belite Portland cements; (ii) Portland-type cements, such as alinite, fluoroalinite, sulfoalite, fluoroalite, alite-calcium fluoroaluminate, belite, sulfobelite, calcium sulfoferrite, calcium sulfoaluminate, calcium chloroaluminate, calcium fluoroaluminate, calcium ferroaluminate, calcium sulfoferroaluminate, belite-calcium sulfoaluminate, belite-calcium sulfoferrite, belite-calcium aluminoferrite, belite-calcium fluoroaluminate, and belite-calcium sulfoferroaluminate cements; (iii) Non-calcium aluminate/silicate cements, such as magnesium silicate, magnesium aluminosilicate, barium silicate, strontium silicate, barium aluminate, and strontium aluminate; (iv) Acid-base cements, such as magnesium phosphate, ammonium magnesium phosphate (struvite), magnesium potassium phosphate, aluminum phosphate, zinc phosphate, iron(II) phosphate, iron(III) phosphate, basic calcium phosphate (hydroxyapatite), magnesium oxychloride (Sorel), zinc oxychloride, magnesium carbonate, magnesium hydroxycarbonate, and glass-ionomer cements; and (v) Polymer-modified cements and macro-defect-free (MDF) cements.

While the foregoing written description of the invention enables one of ordinary skill to make and use what is considered presently to be the best mode thereof, those of ordinary skill will understand and appreciate the existence of variations, modifications, combinations, and equivalents of the specific embodiments, methods, and examples herein. The invention should therefore not be limited by the above described embodiments, methods, and examples, but by all embodiments, variations, and methods within the scope and spirit of the claimed invention and its equivalents. 

What is claimed is: 1: A method for improving the properties of a hydraulic cement composition comprising adding a chemical admixture to said hydraulic cement composition, wherein the chemical admixture comprises complexes of metals with hydroxycarboxylic acid derived ligands, complexes of semi-metals with hydroxycarboxylic acid derived ligands, and any combination thereof, represented by the formula: A¹ _(a) . . . A^(n) _(x)B¹ _(a′) . . . B^(n) _(x′)[M¹ _(a″) . . . M^(n) _(x″)C¹ _(a′″) . . . C^(n) _(x′″)L¹ _(a″″) . . . L^(n) _(x″″)] such that: A¹ through A^(n) are a plurality of cations, wherein n is a number equal to or greater than 1; B¹ through B^(n) are a plurality of anions, wherein n is a number equal to or greater than 1; M¹ through M^(n) are a plurality of chelated metal or semi-metal cations, wherein n is a number equal to or greater than 1; C¹ through C^(n) are a plurality of coordinating ligands, wherein n is a number equal to or greater than 1; L¹ through L^(n) are a plurality of chelating hydroxycarboxylic acid derived ligands, wherein n is a number equal to or greater than 1; a and x are cation stoichiometries and represent numbers equal to or greater than 0; a′ and x′ are anion stoichiometries and represent numbers equal to or greater than 0; a″ and x″ are chelated metal stoichiometries and represent numbers equal to or greater than 1; a′″ and x′″ are coordinating ligand stoichiometries and represent numbers equal to or greater than 0; and a″″ and x″″ are chelating hydroxcarboxylic acid-derived ligand stoichiometries and represent numbers equal to or greater than
 1. 2: The method of claim 1 wherein said chemical admixture includes at least one member of the group consisting of glycolatoaluminum(III), sodium glycolatoaluminate(III), lactatoaluminum(III), sodium lactatoaluminate(III), malatoalumin(III), sodium malatoaluminate(III), citratoaluminum(III), sodium citratoaluminate(III), sodium 2-hydroxybutyratoaluminate(III), sodium 3-hydroxybutyratoaluminate(III), sodium citramalatoaluminate(III), sodium tartaratoaluminate(III), sodium mucatoaluminate(III), sodium 2,3-dihydroxybenzoatoaluminate(III), sodium caffeatoaluminate(III), sodium chlorogenatoaluminate(III), sodium malatoaluminate(III), sodium chloridomalatoaluminate(III), sodium malatosulfatoaluminate(III), lithium glycolatoaluminate(III), lithium lactatoaluminate(III), lithium malatoaluminate(III), lithium citratoaluminate(III), potassium glycolatoaluminate(III), potassium lactatoaluminate(III), potassium malatoaluminate(III), potassium citratoaluminate(III), magnesium citratoaluminate(III), calcium citratoaluminate(III), sodium acetatomalatoaluminate(III), sodium acetatocitratoaluminate(III), sodium malatotartaratoaluminate(III), sodium citratotartaratoaluminate(III), sodium citratomalatoaluminate(III), sodium boromalatoaluminate(III), sodium borocitratoaluminate(III), sodium citratophosphatoaluminate(III), sodium carbonatocitratoaluminate(III), calcium carbonatocitratoaluminate(III), sodium calcium carbonatocitratoaluminate(III), magnesium carbonatocitratoaluminate(III), malatobismuth(III), sodium malatobismuthate(III), citratobismuth(III), sodium citratobismuthate(III), sodium borocitratobismuthate(III), sodium malatoaluminate(III)bismuthate(III), sodium citratoaluminate(III)bismuthate(III), sodium citratomagnesate(II), sodiumcitratocalcate(II), sodium malatoindate(III), sodium malatogallate(III), sodium malatoferrate(III), sodium malatozincate(II), sodium malatozirconate(IV), sodium malatolanthanate(III), sodiummalatoyttrate(III), sodium citratomolybdate(VI), and sodium citratotungstate(VI). 3: The method of claim 1 wherein said hydraulic cement composition comprises Portland cement, Portland cement and Type F fly ash, Portland cement and electric arc furnace slag, Portland cement and limestone powder, Portland cement and brucite, Type C fly ash, Type C fly ash and Type F fly ash, Basic Oxygen Furnace Slag, and Basic Oxygen Furnace Slag and Electric Arc Furnace Slag, or any combination thereof. 4: The method of claim 1 wherein said properties of the hydraulic cement composition comprise set time, hardness, compressive strength, shrinkage, water permeability and freeze-thaw resistance. 5: The method of claim 1 wherein the plurality of cations A¹ through A^(n) includes at least one member of the group consisting of the hydronium ion, cations of Group IA elements, and cations of Group IIA elements. 6: The method of claim 1 wherein the plurality of cations A¹ through A^(n) includes at least one member of the group consisting of the hydronium ion, lithium(I), sodium(I), potassium(I), magnesium(II), and calcium(II). 7: The method of claim 1 wherein the plurality of anions B¹ through B^(n) includes at least one member of the group consisting of anions of Group IVA elements, anions of Group VA elements, anions of Group VIA elements, and anions of Group VIIA elements. 8: The method of claim 1 wherein the plurality of anions B¹ through B^(n) includes at least one member of the group consisting of trioxocarbonate(IV), tetraoxophosphate(V), tetraoxosulfate(VI), and chloride. 9: The method of claim 1 wherein the plurality of chelated metal or semi-metal cations M¹ through M^(n) includes at least one member of the group consisting of cations of Group IIA elements, cations of Group IIIA elements, cations of Group VA elements, cations of Group IIB elements, cations of Group IIIB elements, cations of Group IVB elements, cations of Group VIB elements, and cations of Group VIIIB elements. 10: The method of claim 1 wherein the plurality of chelated metal or semi-metal cations M¹ through M^(n) includes at least one member of the group consisting of magnesium(II), calcium(II), yttrium(III), lanthanum(III), cerium(III), titanium(IV), zirconium(IV), molybdenum(VI), tungsten(VI), iron(III), zinc(II), boron(III), aluminum(III), gallium(III), indium(III), bismuth(III), and zirconium(IV). 11: The method of claim 1 wherein the plurality of coordinating ligands C¹ through C^(n) includes at least one member of the group consisting of anions of Group IIIA elements, anions of Group IVA elements, and aliphatic carboxylic acids. 12: The admixture of claim 1 wherein the plurality of coordinating ligands C¹ through C^(n) includes at least one member of the group consisting of water, trioxoborate(III), and ethanoate. 13: The method of claim 1 wherein the plurality of chelating hydroxycarboxylic acid-derived ligands L¹ through L^(n) includes at least one member of the group consisting of anions of hydroxycarboxylic acids with a single hydroxyl group and a single carboxylic acid group, anions of hydroxycarboxylic acids with two or more hydroxyl groups and one carboxylic acid group, anions of hydroxycarboxylic acids with one hydroxyl group and two or more carboxylic acid groups, and anions of hydroxycarboxylic acids with two or more hydroxyl groups and two or more carboxylic acid groups. 14: The method of claim 1 wherein the plurality of chelating hydroxycarboxylic acid-derived ligands L¹ through L^(n) includes at least one member of the group consisting of hydroxyacetate, 2-hydroxypropanoate, 2-hydroxybutanoate, 3-hydroxybutanoate, 2-hydroxybutane-1,4-dioate, 2-hydroxy-2-methylbutane-1,4-dioate, 3-carboxy-3-hydroxypentane-1,5-dioate, 2,3-dihydroxybutane-1,4-dioate, 2,3,4,5-tetrahydroxyhexane-1,6-dioate, 2,3-dihydroxybenzoate, 3-(3′,4′-dihydroxyphenyl)prop-2-enoate), and chlorogenate. 15: The method of claim 1 wherein said admixture is prepared by reacting at least one member of a group consisting of an oxide, hydroxide, carbonate or basic carbonate of a Group IIA, Group IIIA, Group VA, Group IIB, Group IIIB, Group IVB, Group VIB, and a Group VIIIB element with at least one hydroxycarboxylic acid-derived ligand. 16: The method of claim 1 wherein said admixture is prepared by reacting at least one member of a group consisting of an oxide, hydroxide, carbonate or basic carbonate of a Group IIA, Group IIIA, Group VA, Group IIB, Group IIIB, Group IVB, Group VIB, and a Group VIIIB element with at least one hydroxycarboxylic acid-derived ligand, and at least one member of the group consisting of an oxide, hydroxide, carbonate, and hydrogen carbonate of a Group IA or a Group IIA metal. 17: The method of claim 1 wherein said admixture is prepared by reacting at least one member of a group consisting of an oxometallate compound of a Group IA element and a Group IIIA element, with at least one hydroxycarboxylic acid-derived ligand. 18: The method of claim 1 wherein said admixture is prepared by reacting at least one member of the group consisting of an oxide, hydroxide, carbonate, basic carbonate or hydrogencarbonate of a Group IA or a Group IIA element with a salt of at least one member of the group consisting of a Group IIA, Group IIIA, Group VA, Group IIB, Group IIIB, Group IVB, Group VIB and a Group VIIIB element with at least one member of the group consisting of a Group IIIA, Group IVA, Group VA, Group VIA and Group VIIA nonmetal with at least one hydroxycarboxylic acid-derived ligand. 